纳米TiO_2光催化剂制备工艺条件研究

以钛酸丁酯为主要原料，采用溶胶一凝胶法制备纳米TiO2粉体。以罗丹明B为降解对象，确定制备条件。结果表明：以乙醇为溶剂、醋酸为催化剂、pH值=2～3、陈化时间为1天。通过XRD检测，可知所制得纳米TiO2多为锐钛矿型。

纳米TiO_2薄膜的制备及其光催化性能研究

采用溶胶-凝胶(Sol-gel)法在玻璃衬底上制备了纳米TiO_2薄膜。采用X射线衍射仪(XRD)、紫外可见-光谱(UV/vis)和原子力显微镜(AFM)对纳米TiO_2进行表征。结果表明,经300～700℃退火得到的TiO_2粉体呈锐钛矿相,经800℃退火得到了锐钛矿相与金红石相的混合晶相,经900℃退火完全转化为金红石相。薄膜表面粒子分布均匀,表面平均粗糙度为1.54nm,该薄膜具有较高的光催化活性,可直接用于光催化降解有机物等领域,具有广阔的应用前景。

纳米TiO_2光催化材料的改性研究

本文以钛酸四丁酯为前驱体,溶胶-凝胶法制备纯Ti O2和Fe3+-Ti O2纳米粉末,并采用透射电子显微镜(TEM)、X光衍射(XRD)、热重差热分析仪(DTA-TG)、UV光谱检测的测试技术,对粉末的平均粒径、形貌、物相、热稳定性和光催化性能等进行了表征。分析结果表明,用溶胶-凝胶法制备的掺杂Fe的Ti O2纳米粉末颗粒细小均匀,形状完整,外观呈球形,平均粒径约为15nm。通过对样品在500-190nm区间的光谱扫描,发现Fe掺杂提高了Ti O2对紫外光的吸收强度,并且提高了其对可见光的响应强度,使其光谱影响范围发生了一定程度的红移,从而提高了材料的光催化性能。

Hydrophilic and photocatalytic activities of Nd-doped titanium dioxide thin films

The Nd-doped TiO2 thin films with higher hydrophilic and photocatalytic activities were prepared on glass slides by an acid-catalyzed sol？gel method. The effects of Nd doping on crystalline phase, surface composition and optical property were investigated by means of techniques such as X-ray diffraction （XRD）, scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, Fourier transform infrared spectroscopy （FT-IR）, optical contact angle tester and UV-Vis spectroscopy. The results show that Nd doping obviously influences the hydrophilic and photocatalytic activities of TiO2thin films. Nd doping could cause the TiO2 lattice distortion, inhibit phase transition from anatase to rutile, cause red shift of the absorption spectrum edge, produce hydroxyl radicals （·OH）, and accelerate surface hydroxylation, which result in a significant improvement in the hydrophilicity and photoreactivity of Nd-doped TiO2 thin films. When the content of Nd is 0.1% （mass fraction）, TiO2 thin films achieve the smallest grain size （about 15 nm）, and the hydrophilic and photocatalytic activities of TiO2 thin film reach the maximum, the contact angle is only 8.1°, and 92% of methylene blue is finally degraded. Moreover, the modification mechanism of Nd doping was also discussed.

Influence of lanthanum-doping on photocatalytic properties of BiFeO_3 for phenol degradation

A series of BiFeO3 and lanthanum‐doped BiFeO3 photocatalysts were synthesized by a facile sol‐gel method using citric acid as complexing agent, and used to remove phenol in industrial wastewater under simulated sunlight irradiation. The samples were characterized by X‐ray diffraction, energy dispersive spectroscopy, X‐ray photoelectron spectroscopy, UV‐Vis diffuse reflectance spectroscopy and photoluminescence spectroscopy. The introduction of La effectively suppressed the generation of an impurity phase. All the metals （La, Bi and Fe） are well distributed. Under simulated sunlight irradiation, the La‐doped BiFeO3 photocatalysts exhibited superior photocatalytic activity to pure BiFeO3. The 15%La‐doped BiFeO3 photocatalyst exhibited the best activity, with a degradation rate of 96%and COD removal rate of 81.53%after irradiation for 180 min, and it showed good recycling stability. The enhanced photocatalytic ability of 15% La‐doped BiFeO3 was attributed to the in‐crease of adsorbed surface hydroxyl groups, enhancement of visible light absorption and reduction of electron‐hole recombination. We confirmed that the primary active species was -OH by adding different scavengers during the photodegradation of phenol and proposed a reaction mechanism based on these experiments.

Effects of Ni doping contents on photocatalytic activity of B-BiVO_4 synthesized through sol-gel and impregnation two-step method

To enhance the photocatalytic activity of B-BiVO4,Ni-doped B?BiVO4photocatalyst(Ni-B-BiVO4)was synthesized through sol-gel and impregnation method.The photocatalysts were characterized by XPS,XRD,SEM,EDS,BET and UV-Vis DRS techniques.The results showed that single or double doping did not change the crystalline structure and morphology,but the particle size decreased with Ni doping.The band gap energy absorption edge of Ni-B-BiVO4shifted to a longer wavelength compared with undoped,B or Ni single doped BiVO4.More V4+and surface hydroxyl oxygen were observed in BiVO4after Ni-B co-doping.When the optimal mass fraction of Ni is0.30%,the degradation rate of MO in50min is95%for0.3Ni-B-BiVO4sample which also can effectively degrade methyl blue(MB),acid orange(AOII)II and rhodamine B(RhB).The enhanced photocatalytic activity is attributed to the synergistic effects of B and Ni doping.

Structure,morphology and opto-magnetic properties of Bi_2MoO_6 nano-photocatalyst synthesized by sol-gel method

Bismuth molybdate （Bi2MoO6） nano-particles （NPs） were synthesized using bismuth nitrate, ammonium molybdate, citric acid and ethyl cellulose by a simple sol-gel method. The structure, morphology, opto-magnetic and photocatalytic properties of the obtained powder were characterized by X-ray diffraction （XRD）, Fourier transform infrared （FT-IR） spectra, high resolution scanning electron microscopy （HRSEM）, energy dispersive X-ray （EDX）, ultraviolet-visible diffuse reflectance spectra （DRS）, photoluminescence （PL） spectra and vibrating sample magnetometer （VSM） techniques. The XRD, FT-IR and EDX results indicate that the resultant powder is pure and single phase crystalline Bi2MoO6 with orthorhombic structure. The HRSEM image shows that the morphology of obtained powder consists with well defined nano-particles structure. The VSM results show superparamagnetic behavior of the obtained nano-particles. The photocatalytic activity of Bi2MoO6 nano-particles was performed. The addition of TiO2 catalyst enhances the photocatalytic activity of Bi2MoO6 nano-particles. The catalysts Bi2MoO6, TiO2 and mixed oxide catalyst Bi2MoO6-TiO2 nano-composites （NCs） were tested for the photocatalytic degradation （PCD） of 4-chlorophenol （4-CP）. It is found that the PCD efficiency of Bi2MoO6-TiO2 NCs is higher than that of pure Bi2MoO6 and TiO2 catalysts.

Preparation and photocatalytic activity of neodymium doping titania loaded to silicon dioxide

Neodymium doping titania was loaded to silicon dioxide to prepare Nd/TiO2-SiO2 by sol-gel method and Nd/TiO2-SiO2 was characterized by X-ray diffractometry （XRD）, scanning electron microscopy （SEM）, Fourier transform-infrared spectroscopy （FT-IR） and diffuse reflectance spectra （DRS）. Photocatalytic activities of Nd/TiO2-SiO2 with different neodymium contents were evaluated by degradation of methyl orange. The light absorption of Nd/TiO2-SiO2 increased with increasing doping neodymium in a visible light range of 388-619 nm, and Nd doping was in favor of decreasing the recombination of photo-generated electrons with holes. Nd and SiO2 improved the photocatalytic activity of TiO2. The optimal molar fraction of Nd to Ti was 0.1%, and the optimum calcination temperature was 600 ℃. The highest degradation rate of methyl orange was 82.9% after irradiation for 1 h.

ZnO/TiO2 Nanocomposite Synthesized by Sol Gel from Highly Soluble Single Source Molecular Precursor

Single source molecular precursors （SSPs） provide an opportunity to get control over the microstructure of nanomaterials at atomic level. A SSP was designed and developed for the synthesis of ZnO/TiO2 nanocomposite by sol gel method. In a typical synthe-sis process, a bimetallic molecular compound with chemical formula [Cl2TiZn（dmae）4] （dmae=dimethylaminoethanol） was synthesized and its chemical composition was deter-mined by elemental analysis. The obtained compound has shown excellent solubility in common organic solvents, a prerequisite for its use in sol gel method as SSP. The SSP ob-tained was controllably hydrolyzed by adding equimolar amount of water using ethanol as solvent to get ZnO/TiO2 nanocomposite gel. The resulting gel was precipitated at pH=9 and sintered at 200 ℃ （T200）, 400℃ （T400）, and 600℃ （T600）. The XRD analyses have shown that the as synthesized （non-sintered, T00） powder was amorphous. However, the crystallinity improved upon sintering, and the XRD analyses revealed that the resulting nanomaterials were composed of mixed oxides i.e., ZnO and TiO2. The ZnO was in wurtzite （hexagonal） while the TiO2 was in brookite （orthorhombic） phase. The increase in particlesize was further confirmed from BET analysis and SEM micrographs. The IR spectra ob-tained for the resulting powder have shown the peculiar vibrational bands for Zn-O and Ti-O. Furthermore, the IR spectra revealed that the non-sintered ZnO/TiO2 nanocomposite had significant number of OH group which was removed upon sintering. The photocatalytic activities of the ZnO/TiO2 nanocomposites were tested. All the samples have shown good photocatalytic activities. However, the T400 has shown higher activity than the T00, T200, and T600. The higher photocatalytic activity of T400 than T00, T200, and T600 may be due to improved crystallinity which ensures efficient grain boundary interfaces.

Low temperature doping of anatase nano TiO2

In this paper. Glucose, nitrate, and urea were respectively used as C, B, and N sources doped TiO2 at low temperature sol gel method, The obtained nano TiO2 was characterized by DRS, FIRT, TG-DTG. The photocatalytic properties and the optical response range of the natase nanocrystalline were analyzed and studied with the hybrid orbital theory. The results show that the band gap of the doped TiO2 was narrow, and the photocatalytic ability could be excited by the visible lighL and the doping of non metallic elements broadens the application range of TiO2, so that it could be excited under the visible light and obtained better use value.