Mesoporous SiO_2 microspheres were synthesized using the sol-gel method and were characterized by TEM, FT-IR and BET techniques. The diameter of the microspheres is about 100—150 nm, and the average mesopore diameter...Mesoporous SiO_2 microspheres were synthesized using the sol-gel method and were characterized by TEM, FT-IR and BET techniques. The diameter of the microspheres is about 100—150 nm, and the average mesopore diameter is 2.55 nm, while the specific surface area is 1 088.9 m2/g. Mesoporous SiO_2 microspheres adsorb glutaraldehyde and immobilize laccase by means of the aldehyde group in glutaral which can react with the amidogen of laccase. The immobilization conditions were optimized at a glutaraldehyde concentration of 0.75%, a crosslinking time of 8 h, a laccase concentration of 0.04 L/L and an immobilization time of 10 h. When diesel leakage concentration was 80 mg/L, the highest corrosion inhibition efficiency of immobilized laccase reached 49.23%, which was slightly lower than the corrosion inhibition efficiency of free laccase(59%). The diesel degradation ratio could reach up to 45%. It has been proved that the immobilized laccase could degrade diesel to inhibit corrosion.展开更多
Laccase was immobilized on the ceramic-chitosan composite support by using glutaraldehyde as the cross-linking reagent. The immobilization conditions and characterization of the immobilized enzyme were investigated. T...Laccase was immobilized on the ceramic-chitosan composite support by using glutaraldehyde as the cross-linking reagent. The immobilization conditions and characterization of the immobilized enzyme were investigated. The immobilization of laccase was successfully realized when 3.0 mL of 1.25 mg/mL of laccase at a pH value of 4.0 reacted with 0.15 g of ceramic-chitosan composite support(CCCS) at 4 ℃ for 24 h. The immobilized enzyme exhibited a maximum activity at pH 3.0. The optimal temperatures for immobilized enzyme were 25 ℃ and 50 ℃. The K_m value of immobilized laccase for ABTS was 66.64 μmol/L at a pH value of 3.0 at 25 ℃. Compared with free laccase, the thermal, operating and storage stability of immobilized laccase was improved after the immobilization.展开更多
基金supported by the Foundation for Top Talents Program of China University of Petroleum
文摘Mesoporous SiO_2 microspheres were synthesized using the sol-gel method and were characterized by TEM, FT-IR and BET techniques. The diameter of the microspheres is about 100—150 nm, and the average mesopore diameter is 2.55 nm, while the specific surface area is 1 088.9 m2/g. Mesoporous SiO_2 microspheres adsorb glutaraldehyde and immobilize laccase by means of the aldehyde group in glutaral which can react with the amidogen of laccase. The immobilization conditions were optimized at a glutaraldehyde concentration of 0.75%, a crosslinking time of 8 h, a laccase concentration of 0.04 L/L and an immobilization time of 10 h. When diesel leakage concentration was 80 mg/L, the highest corrosion inhibition efficiency of immobilized laccase reached 49.23%, which was slightly lower than the corrosion inhibition efficiency of free laccase(59%). The diesel degradation ratio could reach up to 45%. It has been proved that the immobilized laccase could degrade diesel to inhibit corrosion.
文摘Laccase was immobilized on the ceramic-chitosan composite support by using glutaraldehyde as the cross-linking reagent. The immobilization conditions and characterization of the immobilized enzyme were investigated. The immobilization of laccase was successfully realized when 3.0 mL of 1.25 mg/mL of laccase at a pH value of 4.0 reacted with 0.15 g of ceramic-chitosan composite support(CCCS) at 4 ℃ for 24 h. The immobilized enzyme exhibited a maximum activity at pH 3.0. The optimal temperatures for immobilized enzyme were 25 ℃ and 50 ℃. The K_m value of immobilized laccase for ABTS was 66.64 μmol/L at a pH value of 3.0 at 25 ℃. Compared with free laccase, the thermal, operating and storage stability of immobilized laccase was improved after the immobilization.