The flow stress behavior and microstructure development of Al-5Zn-2Mg （7005） aluminum alloy were studied by hot compression tests at deformation temperatures between 300-500 ＆#176;C and strain rates between 0.05-50...The flow stress behavior and microstructure development of Al-5Zn-2Mg （7005） aluminum alloy were studied by hot compression tests at deformation temperatures between 300-500 ＆#176;C and strain rates between 0.05-50 s-1. The deformed structures of the samples were observed by optical microscopy （OM）, transmission electron microscopy （TEM） and electron backscattering diffraction （EBSD） analysis. The calculated activation energy is 147 kJ/mol, which is very close to the activation energy for lattice self-diffusion in aluminum （142 kJ/mol）. Dynamic recovery is the dominant restoration mechanism during the deformation. At high strain rate of 50 s-1, temperature rise due to deformation heating leads to a significant flow softening. Microstructure observations indicated that the remaining softening after deformation heating correction at high strain rate and the softening observed at high temperature are associated with grain coarsening induced by grain boundary migration during dynamic recovery process.展开更多
With microscopic phase-field kinetic model, atomic-scale computer simulation program for the precipitation sequence and microstructure evolution of the ordered intermetallic compound γ＇ and θ in ternary Ni75AlxV25-...With microscopic phase-field kinetic model, atomic-scale computer simulation program for the precipitation sequence and microstructure evolution of the ordered intermetallic compound γ＇ and θ in ternary Ni75AlxV25-x alloy were studied. The simulation results show that Al concentration has important effects on the precipitation sequence. When Al concentration in Ni75AlxV25-x alloy is low, 0（Ni3V） ordered phase will be firstly precipitated, followed by γ＇（Ni3Al） ordered phase. With Al concentration increasing, θ and γ＇ ordered phases are simultaneously precipitated. With A1 concentration further increasing, γ＇ ordered phase is firstly precipitated, followed by θ ordered phase. There is a competition relationship between θ and γ＇ ordered phases during growth and coarsening process. No matter which first precipitates, θ ordered phase always occupies advantage in the competition process of coarsening, thus, the microstructure with preferred orientation is formed.展开更多
The hot deformation behavior of Al-Zn-Mg-0.25Sc-Zr alloy and its microstructural evolution were investigated by isothermal axisymmetric hot compression tests at temperatures from 340 to 500°C and strain rates ran...The hot deformation behavior of Al-Zn-Mg-0.25Sc-Zr alloy and its microstructural evolution were investigated by isothermal axisymmetric hot compression tests at temperatures from 340 to 500°C and strain rates ranging from 0.001 to 10 s -1 .The steady flow stress increased with increasing the strain rate or decreasing the deformation temperature,which can be described by a hyperbolic-sine constitutive equation with the deformation activation energy of 150.25 kJ/mol.The tendency of dynamic recrystallization enhanced at high deforming temperatures and low strain rates,which corresponded to low Z values.With decreasing Z value,the main softening mechanism of the alloy transformed from dynamic recovery to dynamic recrystallization, correspondingly,the subgrain size increased and the dislocation density decreased.展开更多
Spark plasma sintering method （SPS） was used to consolidate mixed W-5.6Ni-1.4Fe （mass fraction, %） powders from commercial fine elemental powders, and both the densification behavior and microstructure evolution i...Spark plasma sintering method （SPS） was used to consolidate mixed W-5.6Ni-1.4Fe （mass fraction, %） powders from commercial fine elemental powders, and both the densification behavior and microstructure evolution in sintering were investigated at different heating rates. The results show that the SPS densification process can be divided into three stages. At the initial unshrinking stage, fast heating generates instantaneous discharge and locally inhomogeneous temperature distribution in solid-state powder particles, enhancing later densification; during the intermediate solid state sintering stage, diffusion is more sufficient in the slow-heated SPS process; at the final transient liquid-phase sintering stage, tungsten grains become sphered and coarsen rapidly, but fast heating helps maintain rather small grain sizes.展开更多
基金Project(51075132)supported by the National Natural Science Foundation of ChinaProject(20090161110027)supported by the Doctoral Fund of Ministry of Education of ChinaProject(2011BAG03B02)supported by National Key Technology R&D Program during the 12th Five-Year Plan Period,China
文摘The flow stress behavior and microstructure development of Al-5Zn-2Mg （7005） aluminum alloy were studied by hot compression tests at deformation temperatures between 300-500 ＆#176;C and strain rates between 0.05-50 s-1. The deformed structures of the samples were observed by optical microscopy （OM）, transmission electron microscopy （TEM） and electron backscattering diffraction （EBSD） analysis. The calculated activation energy is 147 kJ/mol, which is very close to the activation energy for lattice self-diffusion in aluminum （142 kJ/mol）. Dynamic recovery is the dominant restoration mechanism during the deformation. At high strain rate of 50 s-1, temperature rise due to deformation heating leads to a significant flow softening. Microstructure observations indicated that the remaining softening after deformation heating correction at high strain rate and the softening observed at high temperature are associated with grain coarsening induced by grain boundary migration during dynamic recovery process.
基金Projects(51174168,51274167)supported by the National Natural Science Foundation of ChinaProject(2014JM7261)supported by the Natural Science Basic Research Plan in Shaanxi Province of ChinaProject(B08040)supported by "111" Project,China
文摘With microscopic phase-field kinetic model, atomic-scale computer simulation program for the precipitation sequence and microstructure evolution of the ordered intermetallic compound γ＇ and θ in ternary Ni75AlxV25-x alloy were studied. The simulation results show that Al concentration has important effects on the precipitation sequence. When Al concentration in Ni75AlxV25-x alloy is low, 0（Ni3V） ordered phase will be firstly precipitated, followed by γ＇（Ni3Al） ordered phase. With Al concentration increasing, θ and γ＇ ordered phases are simultaneously precipitated. With A1 concentration further increasing, γ＇ ordered phase is firstly precipitated, followed by θ ordered phase. There is a competition relationship between θ and γ＇ ordered phases during growth and coarsening process. No matter which first precipitates, θ ordered phase always occupies advantage in the competition process of coarsening, thus, the microstructure with preferred orientation is formed.
基金Project(2012CB619503)supported by the High-tech Research and Development Program of China
文摘The hot deformation behavior of Al-Zn-Mg-0.25Sc-Zr alloy and its microstructural evolution were investigated by isothermal axisymmetric hot compression tests at temperatures from 340 to 500°C and strain rates ranging from 0.001 to 10 s -1 .The steady flow stress increased with increasing the strain rate or decreasing the deformation temperature,which can be described by a hyperbolic-sine constitutive equation with the deformation activation energy of 150.25 kJ/mol.The tendency of dynamic recrystallization enhanced at high deforming temperatures and low strain rates,which corresponded to low Z values.With decreasing Z value,the main softening mechanism of the alloy transformed from dynamic recovery to dynamic recrystallization, correspondingly,the subgrain size increased and the dislocation density decreased.
基金Project (2010CB635104) supported by the National Basic Research Program of ChinaProject (2007AA03Z112) supported by the National High-Tech Research and Development Program of China+2 种基金Project (9140A18040709JW1601) supported by the Advanced Research Fund of DOD, ChinaProject (2009ZZ0019) supported by the Fundamental Research Funds for the Central Universities, ChinaProject (NCET-10-0364) supported by the Program for New Century Excellent Talents in University, China
文摘Spark plasma sintering method （SPS） was used to consolidate mixed W-5.6Ni-1.4Fe （mass fraction, %） powders from commercial fine elemental powders, and both the densification behavior and microstructure evolution in sintering were investigated at different heating rates. The results show that the SPS densification process can be divided into three stages. At the initial unshrinking stage, fast heating generates instantaneous discharge and locally inhomogeneous temperature distribution in solid-state powder particles, enhancing later densification; during the intermediate solid state sintering stage, diffusion is more sufficient in the slow-heated SPS process; at the final transient liquid-phase sintering stage, tungsten grains become sphered and coarsen rapidly, but fast heating helps maintain rather small grain sizes.