Titanium alloys have been successfully applied for aerospace, ship and chemical industries because they possess many good characteristics such as high specific strength, superior corrosion resistance and excellent hig...Titanium alloys have been successfully applied for aerospace, ship and chemical industries because they possess many good characteristics such as high specific strength, superior corrosion resistance and excellent high temperature resistance. Though these alloys show reasonable weldability characteristics, the joint properties are greatly influenced by the welding processes. Weld thermal cycle of the processes will control the weld metal solidification and subsequent phase transformation and resultant microstructure. The welded joints of Ti-6Al-4V alloy were fabricated by gas tungsten arc welding （GTAW）, laser beam welding （LBW） and electron beam welding （EBW） processes. The joints fabricated by EBW process exhibit higher strength compared with the GTAW and LBW joints; but the joints by GTAW process exhibit higher impact toughness compared with the LBW and EBW joints. The resultant tensile and impact properties of the welded joints were correlated with the weld metal microstructures.展开更多
The effects of laser beam welding process parameters such as laser power,welding speed and focal position on mechanical properties and microstructure of AZ31B magnesium alloy were studied.Nine joints were fabricated u...The effects of laser beam welding process parameters such as laser power,welding speed and focal position on mechanical properties and microstructure of AZ31B magnesium alloy were studied.Nine joints were fabricated using different levels of laser power,welding speed and focal position.Tensile properties of the welded joints were evaluated and correlated with the weld zone microstructure and hardness.It is found that the joints fabricated using a laser power of 2 500 W,welding speed of 5.5 m/min and focal position of-1.5 mm yield superior tensile properties compared with the other joints.The formation of very fine grains in weld region,higher fusion zone hardness and uniformly distributed finer precipitates are the main reasons for superior tensile properties of these joints.展开更多
The mechanical properties of Ti-23Al-17Nb (mole fraction,%) laser beam welding alloy joint at room temperature are comparable to that of the base materials.However,the strength and ductility of the as-welded joint det...The mechanical properties of Ti-23Al-17Nb (mole fraction,%) laser beam welding alloy joint at room temperature are comparable to that of the base materials.However,the strength and ductility of the as-welded joint deteriorate seriously after high temperature circulation.The effect of post-welded heat treatment on the microstructure and mechanical properties of the joint was investigated.The heat treatment was taken at 980 ℃ for 1.5 h,then furnace cooling and air cooling were performed separately.The results indicate that proper post-welded heat treatment improves the ductility of the joint at high temperature.展开更多
基金the Combat Vehicle Research and Development Establishment(CVRDE),Avadi,Chennai,Government of India for providing financial support to carry out this investigation through a Contract Acquisition for Research Services project,No.CVRDE/MMG/09-10/0043/CARS
文摘Titanium alloys have been successfully applied for aerospace, ship and chemical industries because they possess many good characteristics such as high specific strength, superior corrosion resistance and excellent high temperature resistance. Though these alloys show reasonable weldability characteristics, the joint properties are greatly influenced by the welding processes. Weld thermal cycle of the processes will control the weld metal solidification and subsequent phase transformation and resultant microstructure. The welded joints of Ti-6Al-4V alloy were fabricated by gas tungsten arc welding （GTAW）, laser beam welding （LBW） and electron beam welding （EBW） processes. The joints fabricated by EBW process exhibit higher strength compared with the GTAW and LBW joints; but the joints by GTAW process exhibit higher impact toughness compared with the LBW and EBW joints. The resultant tensile and impact properties of the welded joints were correlated with the weld metal microstructures.
文摘The effects of laser beam welding process parameters such as laser power,welding speed and focal position on mechanical properties and microstructure of AZ31B magnesium alloy were studied.Nine joints were fabricated using different levels of laser power,welding speed and focal position.Tensile properties of the welded joints were evaluated and correlated with the weld zone microstructure and hardness.It is found that the joints fabricated using a laser power of 2 500 W,welding speed of 5.5 m/min and focal position of-1.5 mm yield superior tensile properties compared with the other joints.The formation of very fine grains in weld region,higher fusion zone hardness and uniformly distributed finer precipitates are the main reasons for superior tensile properties of these joints.
文摘The mechanical properties of Ti-23Al-17Nb (mole fraction,%) laser beam welding alloy joint at room temperature are comparable to that of the base materials.However,the strength and ductility of the as-welded joint deteriorate seriously after high temperature circulation.The effect of post-welded heat treatment on the microstructure and mechanical properties of the joint was investigated.The heat treatment was taken at 980 ℃ for 1.5 h,then furnace cooling and air cooling were performed separately.The results indicate that proper post-welded heat treatment improves the ductility of the joint at high temperature.