Ceramic foams were prepared using red mud and fly ash as raw materials with sodium borate as sintering aid agent,starchand MnO2as foaming agent,respectively.The influence of the amount of starch or MnO2on the crystall...Ceramic foams were prepared using red mud and fly ash as raw materials with sodium borate as sintering aid agent,starchand MnO2as foaming agent,respectively.The influence of the amount of starch or MnO2on the crystalline phase,pore morphologyand physical–chemical porosities was studied.The results showed that the main crystal phases of samples with starch addition andMnO2addition were sodalite phase Na6(AlSiO4)6and Na8(SiAlO4)6MnO4,respectively.The SEM images showed that the variation ofporous structure was mainly dominated by the addition of foaming agent.With the increase of foaming agent,the samples exhibitedbetter comprehensive properties:bulk density of0.59?0.96g/cm3,porosity of41.82%?63.51%,water absorption of3.16%?9.17%,compressive strength of4.22?8.38MPa,flexural strength of2.44?5.82MPa,acid resistance of95.59%?99.60%,alkali resistance of99.82%?99.99%.Based on these properties,the ceramic foams can be used in building field.展开更多
基金Project(K1003027-11) supported by the Key Project Foundation of Science and Technology Plans of Changsha,China
文摘Ceramic foams were prepared using red mud and fly ash as raw materials with sodium borate as sintering aid agent,starchand MnO2as foaming agent,respectively.The influence of the amount of starch or MnO2on the crystalline phase,pore morphologyand physical–chemical porosities was studied.The results showed that the main crystal phases of samples with starch addition andMnO2addition were sodalite phase Na6(AlSiO4)6and Na8(SiAlO4)6MnO4,respectively.The SEM images showed that the variation ofporous structure was mainly dominated by the addition of foaming agent.With the increase of foaming agent,the samples exhibitedbetter comprehensive properties:bulk density of0.59?0.96g/cm3,porosity of41.82%?63.51%,water absorption of3.16%?9.17%,compressive strength of4.22?8.38MPa,flexural strength of2.44?5.82MPa,acid resistance of95.59%?99.60%,alkali resistance of99.82%?99.99%.Based on these properties,the ceramic foams can be used in building field.