The effects of CaO content,MgO content and smelting temperature on the vanadium behavior during the smelting of vanadium titanomagnetite metallized pellets were investigated.The thermodynamics of reduction and distrib...The effects of CaO content,MgO content and smelting temperature on the vanadium behavior during the smelting of vanadium titanomagnetite metallized pellets were investigated.The thermodynamics of reduction and distribution of vanadium was analyzed and the high-temperature smelting experiments were carried out.The thermodynamic calculations show that the distribution ratio of vanadium between the slag and the hot metal decreases with the increments of CaO and MgO content in the slag as well as the increase of the smelting temperature.The smelting experiments demonstrate that the vanadium content in iron and the recovery rate of vanadium in pig iron increase as the CaO content,MgO content and smelting temperature increase,whereas the vanadium distribution ratio between the slag and iron tends to decrease.Moreover,the recovery rate of vanadium in pig iron has a rising trend with increasing the optical basicity of the slag.The addition of MgO in the slag to increase the slag optical basicity can not only improve the vanadium reduction but also promote the formation of magnesium-containing anosovite,which is beneficial to following titanium extraction.展开更多
Extracting vanadium and removing phosphorus simultaneously by adding CaO containing materials to V-bearing hot metal were investigated under the condition of simulating the process of vanadium extraction with insuffic...Extracting vanadium and removing phosphorus simultaneously by adding CaO containing materials to V-bearing hot metal were investigated under the condition of simulating the process of vanadium extraction with insufficiently supplying oxygen in converter. Through preliminary experiments, 3 h and 1375 °C were chosen as the optimum holding time and reaction temperature for formal experiments, respectively. The results of the formal experiments suggest that making basic slag can extract vanadium and remove phosphorus simultaneously. The vanadium extraction rate(ηV) and phosphorus removal rate(ηP) both increase with an increase in the basicity of the original slag materials and the Fe2O3 contents. The vanadium distribution ratio)(V L′is about an order of magnitude greater than the phosphorus distribution ratio),(P L′but the latter is more sensitive to slag basicity than the former. The phosphorus distribution ratio is beyond 6 when the basicity of the original slag materials is beyond 1, which indicates a much better performance of phosphorus removal compared to the phosphorus removal in the current process. Therefore, it is very feasible to properly raise slag basicity to remove phosphorus with consideration of the grade of vanadium slag. The relations between ηV and ηP, and between L′V and L′P are linear under the experimental conditions.展开更多
基金Project(2019JJ50816)supported by the Natural Science Foundation of Hunan Province,China。
文摘The effects of CaO content,MgO content and smelting temperature on the vanadium behavior during the smelting of vanadium titanomagnetite metallized pellets were investigated.The thermodynamics of reduction and distribution of vanadium was analyzed and the high-temperature smelting experiments were carried out.The thermodynamic calculations show that the distribution ratio of vanadium between the slag and the hot metal decreases with the increments of CaO and MgO content in the slag as well as the increase of the smelting temperature.The smelting experiments demonstrate that the vanadium content in iron and the recovery rate of vanadium in pig iron increase as the CaO content,MgO content and smelting temperature increase,whereas the vanadium distribution ratio between the slag and iron tends to decrease.Moreover,the recovery rate of vanadium in pig iron has a rising trend with increasing the optical basicity of the slag.The addition of MgO in the slag to increase the slag optical basicity can not only improve the vanadium reduction but also promote the formation of magnesium-containing anosovite,which is beneficial to following titanium extraction.
基金Project(41603004)supported by the Independent Research Program of State Key Laboratory of Advanced Metallurgy(University of Science and Technology Beijing),China
文摘Extracting vanadium and removing phosphorus simultaneously by adding CaO containing materials to V-bearing hot metal were investigated under the condition of simulating the process of vanadium extraction with insufficiently supplying oxygen in converter. Through preliminary experiments, 3 h and 1375 °C were chosen as the optimum holding time and reaction temperature for formal experiments, respectively. The results of the formal experiments suggest that making basic slag can extract vanadium and remove phosphorus simultaneously. The vanadium extraction rate(ηV) and phosphorus removal rate(ηP) both increase with an increase in the basicity of the original slag materials and the Fe2O3 contents. The vanadium distribution ratio)(V L′is about an order of magnitude greater than the phosphorus distribution ratio),(P L′but the latter is more sensitive to slag basicity than the former. The phosphorus distribution ratio is beyond 6 when the basicity of the original slag materials is beyond 1, which indicates a much better performance of phosphorus removal compared to the phosphorus removal in the current process. Therefore, it is very feasible to properly raise slag basicity to remove phosphorus with consideration of the grade of vanadium slag. The relations between ηV and ηP, and between L′V and L′P are linear under the experimental conditions.