Coal-based Magnetic Activated Carbons （CMAC＇s） were prepared from three representative coal samples of various ranks： Baorigele lignite from Inner Mongolia; Datong bitumite from Shanxi province; and Taixi anthraci...Coal-based Magnetic Activated Carbons （CMAC＇s） were prepared from three representative coal samples of various ranks： Baorigele lignite from Inner Mongolia; Datong bitumite from Shanxi province; and Taixi anthracite from Ningxia Hui Auto- nomous Region. Fe3O4 was used as a magnetic additive. A nitrogen-adsorption analyzer was used to determine the specific surface area and pore structure of the resulting activated carbons. The adsorption capacity was assessed by the adsorption of iodine and methylene blue. X-ray diffraction was used to measure the evolution behavior of Fe304 during the preparation process. Magnetic properties were characterized with a vibrating-sample magnetometer. The effect of the activation temperature on the performance of CMAC＇s was also studied. The results show that, compared to Baorigele lignite and Taixi anthracite, the Datong bitumite is more appropriate for the preparation of CMAC＇s with a high specific surface area, an advanced pore structure and suitable magnetic properties. Fe304 can effectively enhance the magnetic properties and control the pore structure by increasing the ratio of meso- pores. An addition of 6.0% Fe304 and an activation temperature of 880 ℃ produced a CMAC having a specific surface area, an iodine adsorption, a methylene blue adsorption and a specific saturation magnetization of 1152.0 m2/g, 1216.7 mg/g, 229.5 mg/g and 4.623 emu/g, respectively. The coal used to prepare this specimen was Datong bitumite.展开更多
The role of Nil（NO3）2 in the preparation of a magnetic activated carbon is reported in this paper. Magnetic coal-based activated carbons （MCAC） were prepared from Taixi anthracite with low ash content in the prese...The role of Nil（NO3）2 in the preparation of a magnetic activated carbon is reported in this paper. Magnetic coal-based activated carbons （MCAC） were prepared from Taixi anthracite with low ash content in the presence of Ni（NO3）2. The MCAC materials were characterized by a vibrating sample magnetometer （VSM）, X-ray diffraction （XRD）, a scanning electric microscope （SEM）, and by N2 adsorption. The cylindri- cal precursors and derived char were also subjected to thermogravimetric analysis to compare their behavior of weight losses during carbonization. The results show that MCAC has a larger surface area （1074 m21g） and a higher pore volume （0.5792 cm3/g） with enhanced mesopore ratio （by about 10~）. It also has a high saturation magnetization （1.6749 emu/g） and low coercivity （43.26 Oe）, which allows the material to be magnetically separated. The MCAC is easily magnetized because the nickel salt is con- vetted into Ni during carbonization and activation. Metallic Ni has a strong magnetism on account of electrostatic interaction. Added Ni（NO3）2 catalyzes the carbonization and activation process by accelerat- ing burn off of the carbon, which contributes to the development of mesopores and macropores in the activated carbon.展开更多
Heteroatom doping, especially dual-doped carbon materials have attracted much attention for the past few years, and have been regarded as one of the most efficient strategies to enhance the capacitance behavior of por...Heteroatom doping, especially dual-doped carbon materials have attracted much attention for the past few years, and have been regarded as one of the most efficient strategies to enhance the capacitance behavior of porous carbon materials. In this work, a facile two-step synthetic route was developed to fab- ricate nitrogen and sulfur co-doped carbon microsphere （NSCM） by using thiourea as dopant. The NJS doping content is controlled via varying the carbonization temperature. It has been proved that a suitable quantity of N and S groups could not only provide pseudo-capacitance but also promote the electron transfer for carbon materials, which ensures the further utilization of the exposed surfaces for charge storage. The optimized NSCM prepared at a carbonization temperature of 800 ℃ （NSCM-800） achieves a capacitance of 277.1 F g^-1 at a current density of 0.3 A g^-1 in 6.0 mol L^-1 KOH electrolyte, which is 71% higher than that of undoped carbon microsphere. Besides, NSCM-800 shows an excellent cycling stability, 98.2% of the initial capacitance is retained after 5,000 cvcles at a current densitv of 3.0 A g^-1.展开更多
基金supported by the National Natural Science Foundation of China (No20776150)the National High Technology Research and Development Program of China (No2008AA05Z308)
文摘Coal-based Magnetic Activated Carbons （CMAC＇s） were prepared from three representative coal samples of various ranks： Baorigele lignite from Inner Mongolia; Datong bitumite from Shanxi province; and Taixi anthracite from Ningxia Hui Auto- nomous Region. Fe3O4 was used as a magnetic additive. A nitrogen-adsorption analyzer was used to determine the specific surface area and pore structure of the resulting activated carbons. The adsorption capacity was assessed by the adsorption of iodine and methylene blue. X-ray diffraction was used to measure the evolution behavior of Fe304 during the preparation process. Magnetic properties were characterized with a vibrating-sample magnetometer. The effect of the activation temperature on the performance of CMAC＇s was also studied. The results show that, compared to Baorigele lignite and Taixi anthracite, the Datong bitumite is more appropriate for the preparation of CMAC＇s with a high specific surface area, an advanced pore structure and suitable magnetic properties. Fe304 can effectively enhance the magnetic properties and control the pore structure by increasing the ratio of meso- pores. An addition of 6.0% Fe304 and an activation temperature of 880 ℃ produced a CMAC having a specific surface area, an iodine adsorption, a methylene blue adsorption and a specific saturation magnetization of 1152.0 m2/g, 1216.7 mg/g, 229.5 mg/g and 4.623 emu/g, respectively. The coal used to prepare this specimen was Datong bitumite.
基金support by the National Natural Science Foundation of China (No. 20776150)the National Hi-Tech Research and Development Program of China(No. 2008AA05Z308)the Special Fund for Basic Scientific Research of Central Colleges (No. 2009QH15)
文摘The role of Nil（NO3）2 in the preparation of a magnetic activated carbon is reported in this paper. Magnetic coal-based activated carbons （MCAC） were prepared from Taixi anthracite with low ash content in the presence of Ni（NO3）2. The MCAC materials were characterized by a vibrating sample magnetometer （VSM）, X-ray diffraction （XRD）, a scanning electric microscope （SEM）, and by N2 adsorption. The cylindri- cal precursors and derived char were also subjected to thermogravimetric analysis to compare their behavior of weight losses during carbonization. The results show that MCAC has a larger surface area （1074 m21g） and a higher pore volume （0.5792 cm3/g） with enhanced mesopore ratio （by about 10~）. It also has a high saturation magnetization （1.6749 emu/g） and low coercivity （43.26 Oe）, which allows the material to be magnetically separated. The MCAC is easily magnetized because the nickel salt is con- vetted into Ni during carbonization and activation. Metallic Ni has a strong magnetism on account of electrostatic interaction. Added Ni（NO3）2 catalyzes the carbonization and activation process by accelerat- ing burn off of the carbon, which contributes to the development of mesopores and macropores in the activated carbon.
基金supported by the National Natural Science Foundation of China(21306060,21573083)the Program for New Century Excellent Talents in Universities of China(NCET-13-0237)+3 种基金the Doctoral Fund of Ministry of Education of China(20130142120039)the Thousand Talents Plan,and the Initiatory Financial Support from Huazhong University of Science and Technology(HUST)Analytical and Testing Center of Huazhong University of Science and Technologythe support of the China Scholarship Council(CSC)
文摘Heteroatom doping, especially dual-doped carbon materials have attracted much attention for the past few years, and have been regarded as one of the most efficient strategies to enhance the capacitance behavior of porous carbon materials. In this work, a facile two-step synthetic route was developed to fab- ricate nitrogen and sulfur co-doped carbon microsphere （NSCM） by using thiourea as dopant. The NJS doping content is controlled via varying the carbonization temperature. It has been proved that a suitable quantity of N and S groups could not only provide pseudo-capacitance but also promote the electron transfer for carbon materials, which ensures the further utilization of the exposed surfaces for charge storage. The optimized NSCM prepared at a carbonization temperature of 800 ℃ （NSCM-800） achieves a capacitance of 277.1 F g^-1 at a current density of 0.3 A g^-1 in 6.0 mol L^-1 KOH electrolyte, which is 71% higher than that of undoped carbon microsphere. Besides, NSCM-800 shows an excellent cycling stability, 98.2% of the initial capacitance is retained after 5,000 cvcles at a current densitv of 3.0 A g^-1.