Zirconia-mullite-corundum composites were successfully prepared from fly ash,zircon and alumina powder by a reaction sintering process.The phase and microstructure evolutions of the composite synthesized at desired te...Zirconia-mullite-corundum composites were successfully prepared from fly ash,zircon and alumina powder by a reaction sintering process.The phase and microstructure evolutions of the composite synthesized at desired temperatures of 1 400,1 500 and 1 600°C for 4 h were characterized by X-ray diffractometry and scanning electronic microscopy,respectively.The influences of sintering temperature on shrinkage ratio,apparent porosity and bulk density of the synthesized composite were investigated.The formation process of the composites was discussed in detail.The results show that the zirconia-mullite-corundum composites with good sintering properties can be prepared at 1 600°C for 4 h.Zirconia particles can be homogeneously distributed in mullite matrix,and the zirconia particles are around 5μm.The formation process of zirconia-mullite-corundum composites consists of decomposition of zircon and mullitization process.展开更多
基金Project(N100302002)supported by the Fundamental Research Funds for the Central Universities,ChinaProject(20100471467)supported by the China Postdoctoral Science Foundation
文摘Zirconia-mullite-corundum composites were successfully prepared from fly ash,zircon and alumina powder by a reaction sintering process.The phase and microstructure evolutions of the composite synthesized at desired temperatures of 1 400,1 500 and 1 600°C for 4 h were characterized by X-ray diffractometry and scanning electronic microscopy,respectively.The influences of sintering temperature on shrinkage ratio,apparent porosity and bulk density of the synthesized composite were investigated.The formation process of the composites was discussed in detail.The results show that the zirconia-mullite-corundum composites with good sintering properties can be prepared at 1 600°C for 4 h.Zirconia particles can be homogeneously distributed in mullite matrix,and the zirconia particles are around 5μm.The formation process of zirconia-mullite-corundum composites consists of decomposition of zircon and mullitization process.