A theoretical model of phase change heat sink was established in terms of thermal resistance network. The influence of different parameters on the thermal resistance was analyzed and the crucial impact factors were de...A theoretical model of phase change heat sink was established in terms of thermal resistance network. The influence of different parameters on the thermal resistance was analyzed and the crucial impact factors were determined. Subsequently, the forming methods including ploughing-extrusion and stamping method of boiling enhancement structure at evaporation surface were investigated, upon which three-dimensional microgroove structure was fabricated to improve the efficiency of evaporation. Moreover, the crucial parameters related to the fabrication of miniaturized phase change heat sink were optimized. The heat transfer performance of the heat sink was tested. Results show that the developed phase change heat sink has excellent heat transfer performance and is suitable for high power LED applications.展开更多
Dual equal channel lateral extrusion(DECLE)process with various passes followed by sheet extrusion process was performed to produce fine-grained ZK60 alloy sheets.The coarse grain structure of the annealed sample afte...Dual equal channel lateral extrusion(DECLE)process with various passes followed by sheet extrusion process was performed to produce fine-grained ZK60 alloy sheets.The coarse grain structure of the annealed sample after applying sheet extrusion(size:68μm)changed to fine grains of 6.0 and 5.2μm after 3 and 5 passes of DECLE and following extrusion.The hot shear deformation behavior of samples was studied by developing constitutive equations based on shear punch test(SPT)results.SPT was carried out in the temperature range of 200−300℃ and strain rate range of 0.003−0.33 s^(–1).The activation energy of 125−139 kJ/mol and the stress exponent of 3.5−4.2 were calculated for all conditions,which indicated that dislocation creep,controlled by dislocation climb and solute drag mechanism,acted as the main hot deformation mechanism.It was concluded that material constants of n and Q are dependent on the microstructural factors such as grain size and second phase particle fraction,and the relationship of which was anticipated using a 3D surface curve.Moreover,the similar strong basal texture of extruded sheets gave rise to the same deformation mechanisms during SPT and similar n and Q values for ZK60 alloy.展开更多
基金Projects(51575115,51775122) supported by the National Natural Science Foundation of China
文摘A theoretical model of phase change heat sink was established in terms of thermal resistance network. The influence of different parameters on the thermal resistance was analyzed and the crucial impact factors were determined. Subsequently, the forming methods including ploughing-extrusion and stamping method of boiling enhancement structure at evaporation surface were investigated, upon which three-dimensional microgroove structure was fabricated to improve the efficiency of evaporation. Moreover, the crucial parameters related to the fabrication of miniaturized phase change heat sink were optimized. The heat transfer performance of the heat sink was tested. Results show that the developed phase change heat sink has excellent heat transfer performance and is suitable for high power LED applications.
文摘Dual equal channel lateral extrusion(DECLE)process with various passes followed by sheet extrusion process was performed to produce fine-grained ZK60 alloy sheets.The coarse grain structure of the annealed sample after applying sheet extrusion(size:68μm)changed to fine grains of 6.0 and 5.2μm after 3 and 5 passes of DECLE and following extrusion.The hot shear deformation behavior of samples was studied by developing constitutive equations based on shear punch test(SPT)results.SPT was carried out in the temperature range of 200−300℃ and strain rate range of 0.003−0.33 s^(–1).The activation energy of 125−139 kJ/mol and the stress exponent of 3.5−4.2 were calculated for all conditions,which indicated that dislocation creep,controlled by dislocation climb and solute drag mechanism,acted as the main hot deformation mechanism.It was concluded that material constants of n and Q are dependent on the microstructural factors such as grain size and second phase particle fraction,and the relationship of which was anticipated using a 3D surface curve.Moreover,the similar strong basal texture of extruded sheets gave rise to the same deformation mechanisms during SPT and similar n and Q values for ZK60 alloy.