Carbonation decomposition of hydrogarnet is a significant reaction of the calcification-carbonation new method for alumina production by using low-grade bauxite.In this work,non-isothermal decomposition kinetics of hy...Carbonation decomposition of hydrogarnet is a significant reaction of the calcification-carbonation new method for alumina production by using low-grade bauxite.In this work,non-isothermal decomposition kinetics of hydrogarnet in sodium carbonate solution was studied by high-pressure differential scanning calorimetry(HPDSC) at different heating rates of 2,5,8,10,15 and 20 K·min^(-1),respectively.The activation energy(E_α) was calculated with the help of isoconversional method(model-free),and the reaction mechanism was determined by the differential equation method.The calculated activation energy of this reaction was 115.66 kJ·mol^(-1).Furthermore,the mechanism for decomposition reaction is Avrami-Erofeev(n=1.5),and the decomposition process is diffusion-controlled.展开更多
Micro-coiled carbon fibers were prepared by catalytic pyrolysisof acetylene with nano-sized nickel powder catalyst using the substrate method. The morphology of micro-coiled carbon fibers was observed through field em...Micro-coiled carbon fibers were prepared by catalytic pyrolysisof acetylene with nano-sized nickel powder catalyst using the substrate method. The morphology of micro-coiled carbon fibers was observed through field emission scanning electron microscopy. It was found that the fiber and coil diameter of the obtained micro-coiled carbon fibers is about 500—600 nm and 4—5 μm, respectively. Most of the micro-coiled carbon fibers obtained were regular double carbon coils, but a few irregular ones were also observed. On the basis of the experimental observation, a solid catalytic growth mechanism of micro-coiled carbon fibers was proposed.展开更多
基金Supported by the Joint Funds of the National Natural Science Foundation of China(U1202274)the National Natural Science Foundation of China(51204040)+1 种基金the Research Fund for the Doctoral Program of Higher Education of China(201200421100 11)the Doctor Start-up Foundation in Taiyuan University of Science and Technology(20142001)
文摘Carbonation decomposition of hydrogarnet is a significant reaction of the calcification-carbonation new method for alumina production by using low-grade bauxite.In this work,non-isothermal decomposition kinetics of hydrogarnet in sodium carbonate solution was studied by high-pressure differential scanning calorimetry(HPDSC) at different heating rates of 2,5,8,10,15 and 20 K·min^(-1),respectively.The activation energy(E_α) was calculated with the help of isoconversional method(model-free),and the reaction mechanism was determined by the differential equation method.The calculated activation energy of this reaction was 115.66 kJ·mol^(-1).Furthermore,the mechanism for decomposition reaction is Avrami-Erofeev(n=1.5),and the decomposition process is diffusion-controlled.
基金This work was supported by the National Natural Science Foundation of China ( Grant Nos. 59902009, 50025204) by the Chinese Academy of Sciences.
文摘Micro-coiled carbon fibers were prepared by catalytic pyrolysisof acetylene with nano-sized nickel powder catalyst using the substrate method. The morphology of micro-coiled carbon fibers was observed through field emission scanning electron microscopy. It was found that the fiber and coil diameter of the obtained micro-coiled carbon fibers is about 500—600 nm and 4—5 μm, respectively. Most of the micro-coiled carbon fibers obtained were regular double carbon coils, but a few irregular ones were also observed. On the basis of the experimental observation, a solid catalytic growth mechanism of micro-coiled carbon fibers was proposed.