A Thermecmastor-Z hot deformation simulator,optical microscopy,XRD and TEM were employed to characterize the flow stress behavior and microstructure of twin roll cast ZK60 magnesium alloy during initial stage of hot c...A Thermecmastor-Z hot deformation simulator,optical microscopy,XRD and TEM were employed to characterize the flow stress behavior and microstructure of twin roll cast ZK60 magnesium alloy during initial stage of hot compression at elevated temperature of 300 ℃ and 400 ℃ and a given strain rate of 10-2s-1.The results suggest that flow stress drop during initial stage of hot compression at 300℃,generally led by dynamic recrystallization,is attributed to twinning,correspondingly to dynamic recrystallization as deformation temperature is raised to 400 ℃.展开更多
The microstructures of ZK60 alloy under conventional direct as-casting (DC),twin roll casting (TRC) and twin roll casting followed by hot compression (TRC-HC) were analyzed by optical morphology (OM),electron backscat...The microstructures of ZK60 alloy under conventional direct as-casting (DC),twin roll casting (TRC) and twin roll casting followed by hot compression (TRC-HC) were analyzed by optical morphology (OM),electron backscatter diffraction (EBSD) and X-ray diffraction (XRD).The deformation condition of hot compression is 350 ℃,0.1 s?1.The microstructural evolution under TRC-HC deformation followed by annealing at different temperatures and time was discussed.The results show that TRC provides more modified microstructure compared with DC.Twins are found in TRC processing;dynamic recrystallization (DRX),shear bands and twins are found in TRC-HC.A short annealing time has little effect on hardness,while during a long time annealing,it is found that low annealing temperatures increase the micro-hardness and high temperature decreases it.展开更多
基金Project(10020072) supported by Brain Pool Program of Korea Government and Core Technology R & D Program for the Development of High Performance Eco-friendly Structural Materials of the Korean Ministry of Commerce, Industry and Energy
文摘A Thermecmastor-Z hot deformation simulator,optical microscopy,XRD and TEM were employed to characterize the flow stress behavior and microstructure of twin roll cast ZK60 magnesium alloy during initial stage of hot compression at elevated temperature of 300 ℃ and 400 ℃ and a given strain rate of 10-2s-1.The results suggest that flow stress drop during initial stage of hot compression at 300℃,generally led by dynamic recrystallization,is attributed to twinning,correspondingly to dynamic recrystallization as deformation temperature is raised to 400 ℃.
基金Project(10020072) supported by the Korean Ministry of Commerce,Industry and EnergyProject(Y2008F27) supported by the Natural Science Foundation of Shandong Province,China
文摘The microstructures of ZK60 alloy under conventional direct as-casting (DC),twin roll casting (TRC) and twin roll casting followed by hot compression (TRC-HC) were analyzed by optical morphology (OM),electron backscatter diffraction (EBSD) and X-ray diffraction (XRD).The deformation condition of hot compression is 350 ℃,0.1 s?1.The microstructural evolution under TRC-HC deformation followed by annealing at different temperatures and time was discussed.The results show that TRC provides more modified microstructure compared with DC.Twins are found in TRC processing;dynamic recrystallization (DRX),shear bands and twins are found in TRC-HC.A short annealing time has little effect on hardness,while during a long time annealing,it is found that low annealing temperatures increase the micro-hardness and high temperature decreases it.