The effect of heat treatment on microstructure and mechanical properties of the Ti-steel explosive-rolling clad plate was elaborated by optical microscopy （OM）, scanning electron microscopy （SEM）, X-ray diffracti...The effect of heat treatment on microstructure and mechanical properties of the Ti-steel explosive-rolling clad plate was elaborated by optical microscopy （OM）, scanning electron microscopy （SEM）, X-ray diffraction （XRD）, transmission electron microscopy （TEM）, micro-hardness test and shear test. The composites were subjected to heat treatment at temperature of 650-950 ~C for 60 min. The results show that the heat treatment process results in a great enhancement of diffusion and microstructural transformation. The shear strength decreases as the treatment temperature increases. Heated at 850 ℃ or below, their shear strength decreases slowly as a result of the formation of TiC in the diffusion interaction layer; while at the temperature of 850 ℃ or above, the shear strength decreases obviously, which is the consequence of a large amount of Ti-Fe intermetaUics （Fe2Ti/FeTi） along with some TiC distributing continuously at diffusion reaction layer.展开更多
文摘The effect of heat treatment on microstructure and mechanical properties of the Ti-steel explosive-rolling clad plate was elaborated by optical microscopy （OM）, scanning electron microscopy （SEM）, X-ray diffraction （XRD）, transmission electron microscopy （TEM）, micro-hardness test and shear test. The composites were subjected to heat treatment at temperature of 650-950 ~C for 60 min. The results show that the heat treatment process results in a great enhancement of diffusion and microstructural transformation. The shear strength decreases as the treatment temperature increases. Heated at 850 ℃ or below, their shear strength decreases slowly as a result of the formation of TiC in the diffusion interaction layer; while at the temperature of 850 ℃ or above, the shear strength decreases obviously, which is the consequence of a large amount of Ti-Fe intermetaUics （Fe2Ti/FeTi） along with some TiC distributing continuously at diffusion reaction layer.