Fine-grained ZK60 magnesium alloy sheets of 2.0 mm in thickness were successfully joined by laser beam welding （LBW）. The effects of welding parameters including laser power and welding speed on the microstructures ...Fine-grained ZK60 magnesium alloy sheets of 2.0 mm in thickness were successfully joined by laser beam welding （LBW）. The effects of welding parameters including laser power and welding speed on the microstructures and mechanical properties of the joints were investigated. A sound bead, with the ultimate tensile strength （UTS） of 300 MPa and elongation of 12.0%, up to 92.5% and 65% of those of the base metal, respectively, is obtained with the optimized welding parameters. No liquation cracking is visible in the partially melted zone （PMZ） owing to the inhibitory action of the fine dispersed precipitates and the fine-grained microstructure in the as-rolled magnesium alloy sheets. The fusion zone （FZ） is featured with the equiaxed dendritic grains of the average grain size about 8 μm, which are similar to those in the heat affected zone （HAZ）, and this contributes to the relatively high joint efficiency.展开更多
Nylon 10 T and Nylon 10T/1010 samples were synthesized by direct melt polymerization. The non-isothermal crystallization kinetics of Nylon 10 T and Nylon 10T/1010 was investigated by means of differential scanning cal...Nylon 10 T and Nylon 10T/1010 samples were synthesized by direct melt polymerization. The non-isothermal crystallization kinetics of Nylon 10 T and Nylon 10T/1010 was investigated by means of differential scanning calorimetry(DSC). Jeziorny equation and Mo equation were applied to describe the non-isothermal crystallization kinetics of the Nylon 10 T and the Nylon 10T/1010. The activation energies for non-isothermal crystallization were obtained by Vyazovkin's method and Friedman's method, respectively. These results showed that Jeziorny equation and Mo equation well described the non-isothermal crystallization kinetics of the Nylon 10 T and the Nylon 10T/1010. It was found that the values of the activation energy for non-isothermal crystallization of the Nylon 10T/1010 were lower than those of the Nylon 10 T at a given temperature or relative crystallinity degree,which revealed that crystallization ability of the Nylon 10T/1010 was higher. The crystal morphology was observed by means of a polarized optical microscope(POM) and X-ray diffraction(XRD). It was found that the addition of sebacic acid comonomer not only did not change the crystal form of the Nylon 10 T, but also significantly increased the number and decreased the size of spherulites. Comparing with the Nylon 10 T, the crystallization rate was increased with the addition of the sebacic acid comonomer.展开更多
A novel and environmentally friendly route to directly prepare metallic vanadium from NaV03 by molten salt electrolysis is proposed. The feasibility about the direct electro-reduction of NaV03 to metallic vanadi- um i...A novel and environmentally friendly route to directly prepare metallic vanadium from NaV03 by molten salt electrolysis is proposed. The feasibility about the direct electro-reduction of NaV03 to metallic vanadi- um is analyzed based on the thermodynamic calculations and experimental verifications. The theoretical decomposition voltage of NaV03 to metallic vanadium is only 0.47 V at 800 ℃ and much lower than that of the alkali and alkali earth metal chloride salts. The value is slightly higher than that of low-valence vanadium oxides such as V203, V305 and VO. However, the low-valence vanadium oxides can he further electro-reduced to metallic vanadium thermodynamically. The thermodynamic analysis is verified by the experimental results. The direct preparation of metallic vanadium from NaV03 by molten salt electrolysis is feasible.展开更多
基金Project(51274092)supported by the National Natural Science Foundation of ChinaProject(20120161110040)supported by the Doctoral Program of Higher Education of China
文摘Fine-grained ZK60 magnesium alloy sheets of 2.0 mm in thickness were successfully joined by laser beam welding （LBW）. The effects of welding parameters including laser power and welding speed on the microstructures and mechanical properties of the joints were investigated. A sound bead, with the ultimate tensile strength （UTS） of 300 MPa and elongation of 12.0%, up to 92.5% and 65% of those of the base metal, respectively, is obtained with the optimized welding parameters. No liquation cracking is visible in the partially melted zone （PMZ） owing to the inhibitory action of the fine dispersed precipitates and the fine-grained microstructure in the as-rolled magnesium alloy sheets. The fusion zone （FZ） is featured with the equiaxed dendritic grains of the average grain size about 8 μm, which are similar to those in the heat affected zone （HAZ）, and this contributes to the relatively high joint efficiency.
基金Supported by the National Science and Technology Support Program of China(No.2013BAE02B01)the Special Project on the Integration of Industry,Education and Research of Guangdong Province(No.2013B090500003)the Commissioner Workstation Project of Guangdong Province(No.2014A090906002)
文摘Nylon 10 T and Nylon 10T/1010 samples were synthesized by direct melt polymerization. The non-isothermal crystallization kinetics of Nylon 10 T and Nylon 10T/1010 was investigated by means of differential scanning calorimetry(DSC). Jeziorny equation and Mo equation were applied to describe the non-isothermal crystallization kinetics of the Nylon 10 T and the Nylon 10T/1010. The activation energies for non-isothermal crystallization were obtained by Vyazovkin's method and Friedman's method, respectively. These results showed that Jeziorny equation and Mo equation well described the non-isothermal crystallization kinetics of the Nylon 10 T and the Nylon 10T/1010. It was found that the values of the activation energy for non-isothermal crystallization of the Nylon 10T/1010 were lower than those of the Nylon 10 T at a given temperature or relative crystallinity degree,which revealed that crystallization ability of the Nylon 10T/1010 was higher. The crystal morphology was observed by means of a polarized optical microscope(POM) and X-ray diffraction(XRD). It was found that the addition of sebacic acid comonomer not only did not change the crystal form of the Nylon 10 T, but also significantly increased the number and decreased the size of spherulites. Comparing with the Nylon 10 T, the crystallization rate was increased with the addition of the sebacic acid comonomer.
基金Supported by the National Basic Research Program of China(2013CB632606)the National Natural Science Foundation of China(51474200)+1 种基金the Youth Innovation Promotion AssociationCAS(2015036)
文摘A novel and environmentally friendly route to directly prepare metallic vanadium from NaV03 by molten salt electrolysis is proposed. The feasibility about the direct electro-reduction of NaV03 to metallic vanadi- um is analyzed based on the thermodynamic calculations and experimental verifications. The theoretical decomposition voltage of NaV03 to metallic vanadium is only 0.47 V at 800 ℃ and much lower than that of the alkali and alkali earth metal chloride salts. The value is slightly higher than that of low-valence vanadium oxides such as V203, V305 and VO. However, the low-valence vanadium oxides can he further electro-reduced to metallic vanadium thermodynamically. The thermodynamic analysis is verified by the experimental results. The direct preparation of metallic vanadium from NaV03 by molten salt electrolysis is feasible.