Stabilized ZnTiO4 was prepared by doping magnesium oxide through traditional solid state reaction. The experimental results indicate that zinc titanate crystals doped with magnesium oxide grow well and the decompositi...Stabilized ZnTiO4 was prepared by doping magnesium oxide through traditional solid state reaction. The experimental results indicate that zinc titanate crystals doped with magnesium oxide grow well and the decomposition into Zn2TiO4 and TiO2 is restrained through traditional solid state reaction, By adjusting molar ratio of MgO, better properties can be obtained The dielectric properties of the ceramics doped with 30% MgO（ molar percentage） sintered at 1060℃ are as follows：the value of quality factor is greater than 20000（6.5 GHz ）, the temperature coefficient of resonance frequency is about 2 ± 10^-6 /℃,the dielectric constant ranges from 180 to 22.Besides,it is proved that heat treatment can optimize microstructure and the value of quality factor, which increases from 23833.93 to 47584.00 after 2h of heat treatment at 1040℃.展开更多
基金SUPPORTED BY NATIONAL NATURAL SCIENCE FOUNDATION OF CHINA( NO. 50172035).
文摘Stabilized ZnTiO4 was prepared by doping magnesium oxide through traditional solid state reaction. The experimental results indicate that zinc titanate crystals doped with magnesium oxide grow well and the decomposition into Zn2TiO4 and TiO2 is restrained through traditional solid state reaction, By adjusting molar ratio of MgO, better properties can be obtained The dielectric properties of the ceramics doped with 30% MgO（ molar percentage） sintered at 1060℃ are as follows：the value of quality factor is greater than 20000（6.5 GHz ）, the temperature coefficient of resonance frequency is about 2 ± 10^-6 /℃,the dielectric constant ranges from 180 to 22.Besides,it is proved that heat treatment can optimize microstructure and the value of quality factor, which increases from 23833.93 to 47584.00 after 2h of heat treatment at 1040℃.