Herein,a facile and highly efficient synthetic method to prepare organic photothermal materials with high photo-stability and outstanding photothermal performance is reported.Through direct polymerization of commercia...Herein,a facile and highly efficient synthetic method to prepare organic photothermal materials with high photo-stability and outstanding photothermal performance is reported.Through direct polymerization of commercial aromatic monomers in the presence of anhydrous aluminium chloride and dichloromethane,four kinds of conjugated microporous polymers(CMPs)were obtained.Detailed structural analysis confirmed that the resultant CMPs possessed abundant micropores with an extendedπ-conjugated skeleton.Under near-infrared(NIR)light irradiation(808 nm,1.0 W cm−2),all the CMPs showed fast heating-up behavior with their maximum temperatures higher than 150℃.Moreover,the efficiency of photothermal conversion(η)of the CMPs was found to increase linearly with the increase in the number of conjugated benzene rings within the monomer.Poly-TPE from tetraphenylethylene(TPE)and Poly-TP from o-terphenyl(TP)showed highηvalues of over 47%.Poly-TPE was additionally used as a photothermal filler to remotely and spatially control the shape recovery of thermal-sensitive shape memory polymers(SMPs),while its introduction(1 wt%)had little influence on the thermal and mechanical properties of the polymer matrixes.Owing to their excellent NIR photothermal performance as well as a one-step synthetic preparation,these CMPs may be promising photothermal materials for practical applications.展开更多
基金the National Natural Science Foundation of China(51503231 and 21374136)Guangdong Innovative and Entrepreneurial Research Team Program(2013S086)the Fundamental Research Funds for the Central Universities(17lgjc03 and 18lgpy04)。
文摘Herein,a facile and highly efficient synthetic method to prepare organic photothermal materials with high photo-stability and outstanding photothermal performance is reported.Through direct polymerization of commercial aromatic monomers in the presence of anhydrous aluminium chloride and dichloromethane,four kinds of conjugated microporous polymers(CMPs)were obtained.Detailed structural analysis confirmed that the resultant CMPs possessed abundant micropores with an extendedπ-conjugated skeleton.Under near-infrared(NIR)light irradiation(808 nm,1.0 W cm−2),all the CMPs showed fast heating-up behavior with their maximum temperatures higher than 150℃.Moreover,the efficiency of photothermal conversion(η)of the CMPs was found to increase linearly with the increase in the number of conjugated benzene rings within the monomer.Poly-TPE from tetraphenylethylene(TPE)and Poly-TP from o-terphenyl(TP)showed highηvalues of over 47%.Poly-TPE was additionally used as a photothermal filler to remotely and spatially control the shape recovery of thermal-sensitive shape memory polymers(SMPs),while its introduction(1 wt%)had little influence on the thermal and mechanical properties of the polymer matrixes.Owing to their excellent NIR photothermal performance as well as a one-step synthetic preparation,these CMPs may be promising photothermal materials for practical applications.