不同炉型潞安煤灰理化及酸/碱溶解特性

对潞安煤经循环流化床、煤粉炉和气化炉处理后得到的煤灰进行了化学组成、矿物组成、特征基团、粒径分布、比表面积及微观形貌等理化性质的对比研究,并考察了其在酸浸和碱浸过程中Al^3+,Si^4+,Fe^3+,Ca^2+,K^+和Ti^4+等离子的溶解特性。结果表明:不同炉型潞安煤灰中铝、钙、硫等元素的含量有明显的差异;矿物组成包括晶相的鳞石英、方石英、莫来石、硬石膏及非晶相的偏高岭石、假莫来石、无定型二氧化硅等;相比较而言,气化炉灰中铝硅酸盐矿物结构更加不稳定。循环流化床灰颗粒呈具有一定孔洞结构的不规则状,而煤粉炉灰和气化炉灰均为光滑球形颗粒,循环流化床灰的粒径>煤粉炉灰的粒径>气化炉灰的粒径,循环流化床灰的比表面积>气化炉灰的比表面积>煤粉炉灰的比表面积。在HCl溶液中,Al^3+,Fe^3+,Ca^2+,K^+,Ti^4+的溶出率均较高;在NaOH溶液中,仅Si^4+和K^+的溶出率较高。不同炉型潞安煤灰中各元素的溶出率具有较大差异,主要与其矿物组成、结构稳定性、粒径和比表面积等相关。

Effects of Characteristics of Fly Ash on the Properties of Geopolymer

The properties of two types of fly ash geopolymers made from class F fly ashes produced in wet bottom and dry bottom boilers were investigated in the present study. The source material used in the geopolymer concrete was activated with sodium hydroxide and sodium silicate solution. The results revealed that the geopolymer produced with wet bottom boiler fly ash(CZ-FA)hardened quickly, and had higher early-age strength and lower shrinkage than the geopolymer produced with dry bottom boiler fly ash(SX-FA). The compressive strength of the two geopolymers made from CZ-FA and SX-FA was 45 MPa and 15 MPa respectively when cured at 60 ℃ and delayed for 14 d. However, after 90 days' delay, the compressive strength of both the samples is almost the same, up to 80 MPa. Nearly 20% volume shrinkage of the samples made from SX-FA was much higher than that made from CZ-FA, which was almost zero. XRD, SEM/EDS and FT-IR were used to analyze the main reason of the differences.