To improve the wear and corrosion properties of AZ91D magnesium alloys,Cu-based amorphous composite coatings were fabricated on AZ91D magnesium alloy by laser cladding using mixed powders of Cu47Ti34Zr11Ni8 and SiC.Th...To improve the wear and corrosion properties of AZ91D magnesium alloys,Cu-based amorphous composite coatings were fabricated on AZ91D magnesium alloy by laser cladding using mixed powders of Cu47Ti34Zr11Ni8 and SiC.The wear and corrosion behaviours of the coatings were investigated.The wear resistance of the coatings was evaluated under dry sliding wear condition at room temperature.The corrosion resistance of the coatings was tested in 3.5%(mass fraction) NaCl solution.The coatings exhibit excellent wear resistance due to the recombined action of amorphous phase and different intermetallic compounds.The main wear mechanisms of the coatings and the AZ91D sample are different.The former is abrasive wear and the latter is adhesive wear.The coatings compared with AZ91D magnesium alloy also exhibit good corrosion resistance because of the presence of the amorphous phase in the coatings.展开更多
基金Project(AWPT08-10)supported by the Open Fund of the State Key Laboratory of Advanced Welding Production Technology in Harbin Institute of Technology,ChinaProject(mmlab0706)supported by the Open Fund of the State Key Laboratory of Materials Modification by Laser,Ion and Electron Beams in Dalian University of University,ChinaProject(0710908-05-K)supported by the Research Funds of the Guangxi Key Laboratory of Information Materials in Guilin University of Electronic Technology,China
文摘To improve the wear and corrosion properties of AZ91D magnesium alloys,Cu-based amorphous composite coatings were fabricated on AZ91D magnesium alloy by laser cladding using mixed powders of Cu47Ti34Zr11Ni8 and SiC.The wear and corrosion behaviours of the coatings were investigated.The wear resistance of the coatings was evaluated under dry sliding wear condition at room temperature.The corrosion resistance of the coatings was tested in 3.5%(mass fraction) NaCl solution.The coatings exhibit excellent wear resistance due to the recombined action of amorphous phase and different intermetallic compounds.The main wear mechanisms of the coatings and the AZ91D sample are different.The former is abrasive wear and the latter is adhesive wear.The coatings compared with AZ91D magnesium alloy also exhibit good corrosion resistance because of the presence of the amorphous phase in the coatings.