As a fundamental study on recovery of valuable metals from nonferrous metallurgical slags,electrical conductivity values of MO（MO=FeO,NiO）-containing CaO-MgO-SiO2-Al2O3 slag with a low basicity were measured at diff...As a fundamental study on recovery of valuable metals from nonferrous metallurgical slags,electrical conductivity values of MO（MO=FeO,NiO）-containing CaO-MgO-SiO2-Al2O3 slag with a low basicity were measured at different temperatures using AC impedance spectroscopy.The result shows that the electrical conductivity increased from 1.4 S/m to 14.4 S/m with the increase of the temperature from 1 573 to 1 773 K and the content of MO which is less than 12% under the constant mass ratio of （CaO＋MgO） to （SiO2＋Al2O3） of 0.47.Moreover,the increase magnitude of the electrical conductivity was also promoted with the increase of the content of MO.The electrical conductivity of FeO-containing slags was close to that of NiO-containing slags when the content was less than 8%;however,it was obviously larger than that of NiO-containing slags when the content was 12%.The activation energy of the electrical conductivity decreased with the increase of MO content.展开更多
基金Project(50574011) supported by the National Natural Science Foundation of China
文摘As a fundamental study on recovery of valuable metals from nonferrous metallurgical slags,electrical conductivity values of MO（MO=FeO,NiO）-containing CaO-MgO-SiO2-Al2O3 slag with a low basicity were measured at different temperatures using AC impedance spectroscopy.The result shows that the electrical conductivity increased from 1.4 S/m to 14.4 S/m with the increase of the temperature from 1 573 to 1 773 K and the content of MO which is less than 12% under the constant mass ratio of （CaO＋MgO） to （SiO2＋Al2O3） of 0.47.Moreover,the increase magnitude of the electrical conductivity was also promoted with the increase of the content of MO.The electrical conductivity of FeO-containing slags was close to that of NiO-containing slags when the content was less than 8%;however,it was obviously larger than that of NiO-containing slags when the content was 12%.The activation energy of the electrical conductivity decreased with the increase of MO content.