The blast resistance of structures used in buildings needs to be investigated due to the increased threat of a terrorist attack. The damage done by Composition B or Powergel to steel fibre reinforced reactive powder c...The blast resistance of structures used in buildings needs to be investigated due to the increased threat of a terrorist attack. The damage done by Composition B or Powergel to steel fibre reinforced reactive powder concrete (SFRPC) panels and ordinary reinforced concrete (RC) panels of equivalent static flexural strength is compared. A 0.5 kg charge was detonated at a distance of 0.1 m from the 1.3 m×1.0 m×0. 1 m (thick) panels, which were simply supported and spaning 1.3m. Dynamic displacement measurements, high-speed video recording and visual examination of the panels for spall and breach were undertaken. The SFRPC panels withstood the bare charge blast better than the reinforced ordinary concrete panels. Neither type of panel was breached using a 0.5 kg charge. The RC panel exhibited more spalling when Composition B was used. Under successive Composition B loading conditions, the RC panel was breached. In comparison the SFRPC panel was not breached. Exposure to fragmenting charge loading conditions confirmed these performance differences between the SFRPC panel and the reinforced ordinary concrete panel.展开更多
Surface contact explosion experiments have been performed for the study of dynamic response of the hard-soft-hard sandwich panel under blast loading. Experimental results have shown that there are four damage modes, i...Surface contact explosion experiments have been performed for the study of dynamic response of the hard-soft-hard sandwich panel under blast loading. Experimental results have shown that there are four damage modes, including explosion cratering, scabbing of the backside, radial cracking induced failure and circumferential cracking induced failure. It also illustrates that the foam material sandwiched in the multi-layered media has an important effect on damage patterns. The phenomena encountered have been analyzed by the calculation with ALE method. Meanwhile, the optimal analysis of foam material thickness and position in the sandwich panel were performed in terms of experimental and numerical analysis. The proper thickness proportion of the soft layer is about 20% to the thickness of sandwich panel and the thickness of the upper hard layer and lower hard layer is in the ratio of 7 to 3 under the condition in this paper when the total thickness of soft layer remains constant.展开更多
文摘The blast resistance of structures used in buildings needs to be investigated due to the increased threat of a terrorist attack. The damage done by Composition B or Powergel to steel fibre reinforced reactive powder concrete (SFRPC) panels and ordinary reinforced concrete (RC) panels of equivalent static flexural strength is compared. A 0.5 kg charge was detonated at a distance of 0.1 m from the 1.3 m×1.0 m×0. 1 m (thick) panels, which were simply supported and spaning 1.3m. Dynamic displacement measurements, high-speed video recording and visual examination of the panels for spall and breach were undertaken. The SFRPC panels withstood the bare charge blast better than the reinforced ordinary concrete panels. Neither type of panel was breached using a 0.5 kg charge. The RC panel exhibited more spalling when Composition B was used. Under successive Composition B loading conditions, the RC panel was breached. In comparison the SFRPC panel was not breached. Exposure to fragmenting charge loading conditions confirmed these performance differences between the SFRPC panel and the reinforced ordinary concrete panel.
文摘Surface contact explosion experiments have been performed for the study of dynamic response of the hard-soft-hard sandwich panel under blast loading. Experimental results have shown that there are four damage modes, including explosion cratering, scabbing of the backside, radial cracking induced failure and circumferential cracking induced failure. It also illustrates that the foam material sandwiched in the multi-layered media has an important effect on damage patterns. The phenomena encountered have been analyzed by the calculation with ALE method. Meanwhile, the optimal analysis of foam material thickness and position in the sandwich panel were performed in terms of experimental and numerical analysis. The proper thickness proportion of the soft layer is about 20% to the thickness of sandwich panel and the thickness of the upper hard layer and lower hard layer is in the ratio of 7 to 3 under the condition in this paper when the total thickness of soft layer remains constant.