The hot deformation behaviors of solution treated Mg-1.8Mn-0.4Er-0.2Al alloys were investigated by means of compression tests on Gleeble-1500 in strain rate range of 0.01-10s-1,deformation temperature range of 250-450...The hot deformation behaviors of solution treated Mg-1.8Mn-0.4Er-0.2Al alloys were investigated by means of compression tests on Gleeble-1500 in strain rate range of 0.01-10s-1,deformation temperature range of 250-450℃ and a true strain of 0.6.The constitutive relationships among flow stress,strain rate and deformation temperature were described by Arrhenius-type equations,based on the fact that the material constants could be calculated under a wide range of strains.The results show that the flow stress of the experimental alloy decreases with temperature increasing and strain rate decreasing.Under the experimental conditions,the products of constant α and n in the constitutive equation are stable within certain strains,and the deformation activation energy ranges from 160 to 220 kJ/mol.It is proved that the values of calculated flow stress are close to the experimental results with average error of 2.01%.展开更多
Abstract： The hot deformation behaviors of AI-Zn-Mg-Sc-Zr alloy were investigated in a temperature range of 340-500℃ and a strain rate range of 0.001-10 s 1 using uniaxial compression test on Gleeble-1500 thermal si...Abstract： The hot deformation behaviors of AI-Zn-Mg-Sc-Zr alloy were investigated in a temperature range of 340-500℃ and a strain rate range of 0.001-10 s 1 using uniaxial compression test on Gleeble-1500 thermal simulation machine. The results show that the flow stress increases with increasing strain and tends to be constant after a peak value. The flow stress increases with increasing strain rate and decreases with increasing deformation temperature. The phenomenon of dynamic recovery and dynamic recrystallization can be observed by microstructural evolutions. Based on the hyperbolic Arrhenius-type equation, the true stress-true strain data from the tests were employed to establish the constitutive equation considering the effect of the true strain on material constants （α, β, Q, n and A）, which reveals the dependence of the flow stress on strain, strain rate and deformation temperature. The predicted stress-strain curves are in good agreement with experimental results, which confirms that the developed constitutive equations are suitable to research the hot deformation behaviors of Al-Zn-Mg-Sc-Zr alloy.展开更多
Hot-compression of aluminum alloy 5182 was carried out on a Gleeble- 1500 thermo-simulator at deformation temperature ranging from 350 ℃ to 500 ℃ and at strain rate from 0.01 s^-1 to 10 s^-1 with strain range from 0...Hot-compression of aluminum alloy 5182 was carried out on a Gleeble- 1500 thermo-simulator at deformation temperature ranging from 350 ℃ to 500 ℃ and at strain rate from 0.01 s^-1 to 10 s^-1 with strain range from 0.7 to 1.9. The microstructures and macro-textures evolution under different conditions were investigated by polarized optical microscopy and X-ray diffraction analysis, respectively. The basic trend is that the hot-compression stress increases with the decrease of temperature and increase of strain rate, which is revealed and elucidated in terms of Zener-Hollomon parameter in the hyperbolic sine equation with the hot-deformation activation energy of 143.5 kJ/mol. An empirical constitutive equation is proposed to predict the hot-deformation behavior under different conditions. As deformation temperature increases up to 400 ℃, at strain rate over 1 s^-1, dynamic recrystallization （DRX） occurs. Cube orientation { 100} （001） is detected in the recrystallized sample after hot-compression.展开更多
A new C-type subhierarchy for KP hierarchy with two new time series γn and σk （ （Tn,crk ）-CKPH）, which consists of γn-flow, σk-flow and mixed γn and σk evolution equations of eigenfunctions, is proposed. The...A new C-type subhierarchy for KP hierarchy with two new time series γn and σk （ （Tn,crk ）-CKPH）, which consists of γn-flow, σk-flow and mixed γn and σk evolution equations of eigenfunctions, is proposed. The zero-curvature representation for the （γn, σk ）-CKPH is derived. The reduction and constrained flows of （γn, σk ）-CKPH are studied.展开更多
基金Project(2008BA4036) supported by the Natural Science Foundation of Chongqing Science and Technology Commission, ChinaProject(081061130) supported by the National University Students Research Training Program and Sharing Fund of Chongqing University’s Large-scale Equipment
文摘The hot deformation behaviors of solution treated Mg-1.8Mn-0.4Er-0.2Al alloys were investigated by means of compression tests on Gleeble-1500 in strain rate range of 0.01-10s-1,deformation temperature range of 250-450℃ and a true strain of 0.6.The constitutive relationships among flow stress,strain rate and deformation temperature were described by Arrhenius-type equations,based on the fact that the material constants could be calculated under a wide range of strains.The results show that the flow stress of the experimental alloy decreases with temperature increasing and strain rate decreasing.Under the experimental conditions,the products of constant α and n in the constitutive equation are stable within certain strains,and the deformation activation energy ranges from 160 to 220 kJ/mol.It is proved that the values of calculated flow stress are close to the experimental results with average error of 2.01%.
基金Project(2012CB619503)supported by National Basic Research Program of China
文摘Abstract： The hot deformation behaviors of AI-Zn-Mg-Sc-Zr alloy were investigated in a temperature range of 340-500℃ and a strain rate range of 0.001-10 s 1 using uniaxial compression test on Gleeble-1500 thermal simulation machine. The results show that the flow stress increases with increasing strain and tends to be constant after a peak value. The flow stress increases with increasing strain rate and decreases with increasing deformation temperature. The phenomenon of dynamic recovery and dynamic recrystallization can be observed by microstructural evolutions. Based on the hyperbolic Arrhenius-type equation, the true stress-true strain data from the tests were employed to establish the constitutive equation considering the effect of the true strain on material constants （α, β, Q, n and A）, which reveals the dependence of the flow stress on strain, strain rate and deformation temperature. The predicted stress-strain curves are in good agreement with experimental results, which confirms that the developed constitutive equations are suitable to research the hot deformation behaviors of Al-Zn-Mg-Sc-Zr alloy.
基金Project(50905188) supported by the National Natural Science FoundationProject(2012CB619500) supported by Key Basic Research Program of China
文摘Hot-compression of aluminum alloy 5182 was carried out on a Gleeble- 1500 thermo-simulator at deformation temperature ranging from 350 ℃ to 500 ℃ and at strain rate from 0.01 s^-1 to 10 s^-1 with strain range from 0.7 to 1.9. The microstructures and macro-textures evolution under different conditions were investigated by polarized optical microscopy and X-ray diffraction analysis, respectively. The basic trend is that the hot-compression stress increases with the decrease of temperature and increase of strain rate, which is revealed and elucidated in terms of Zener-Hollomon parameter in the hyperbolic sine equation with the hot-deformation activation energy of 143.5 kJ/mol. An empirical constitutive equation is proposed to predict the hot-deformation behavior under different conditions. As deformation temperature increases up to 400 ℃, at strain rate over 1 s^-1, dynamic recrystallization （DRX） occurs. Cube orientation { 100} （001） is detected in the recrystallized sample after hot-compression.
基金Supported by National Basic Research Program of China(973 Program) under Grant No.2007CB814800National Natural Science Foundation of China under Grant Nos.10901090,10801083,11171175+1 种基金Chinese Universities Scientific Fund under Grant No.2011JS041China Postdoctoral Science Foundation Funded Project under Grant No.20110490408
文摘A new C-type subhierarchy for KP hierarchy with two new time series γn and σk （ （Tn,crk ）-CKPH）, which consists of γn-flow, σk-flow and mixed γn and σk evolution equations of eigenfunctions, is proposed. The zero-curvature representation for the （γn, σk ）-CKPH is derived. The reduction and constrained flows of （γn, σk ）-CKPH are studied.