This study aimed to effectively reduce the cracking susceptibility of the laser clad coating by enhancing the environmental temperature during laser cladding,and reveal the residual stress distribution in different de...This study aimed to effectively reduce the cracking susceptibility of the laser clad coating by enhancing the environmental temperature during laser cladding,and reveal the residual stress distribution in different depths of the coating.The TiNi/Ti2Ni-based coatings were prepared on Ti6Al4V by laser cladding at different environmental temperatures of25,400,600and800°C.The changes in residual stress along the depth of the coatings were investigated in detail by the nanoindentation method.Results showed that the average residual stress of2.90GPa in the coating prepared at25°C was largest.With the increase in environmental temperature,the average residual stress was reduced to1.34GPa(400°C),0.70GPa(600°C)and0GPa(800°C).For all the coatings,the residual stress was increased with increasing the distance from the coating surface.Enhancing the environmental temperature can effectively reduce the cracking susceptibility of the coatings.展开更多
基金Project (51471105) supported by the National Natural Science Foundation of ChinaProject (12SG44) supported by the "Shu Guang" Project of Shanghai Municipal Education Commission and Shanghai Education Development Foundation,ChinaProject (15KY0504) supported by the "Graduate Innovation" Project of Shanghai University of Engineering Science,China
文摘This study aimed to effectively reduce the cracking susceptibility of the laser clad coating by enhancing the environmental temperature during laser cladding,and reveal the residual stress distribution in different depths of the coating.The TiNi/Ti2Ni-based coatings were prepared on Ti6Al4V by laser cladding at different environmental temperatures of25,400,600and800°C.The changes in residual stress along the depth of the coatings were investigated in detail by the nanoindentation method.Results showed that the average residual stress of2.90GPa in the coating prepared at25°C was largest.With the increase in environmental temperature,the average residual stress was reduced to1.34GPa(400°C),0.70GPa(600°C)and0GPa(800°C).For all the coatings,the residual stress was increased with increasing the distance from the coating surface.Enhancing the environmental temperature can effectively reduce the cracking susceptibility of the coatings.