Titanium silicalite-1(TS-1)films were synthesized on stainless steel plate,glass slide and monolith supports via an in-situ hydrothermal method.Characterization data showed that the formation of TS-1 films was easier ...Titanium silicalite-1(TS-1)films were synthesized on stainless steel plate,glass slide and monolith supports via an in-situ hydrothermal method.Characterization data showed that the formation of TS-1 films was easier on the porous flat support with rough surface such as monolith than on the smooth non-porous supports like glass slide and stainless steel plate.The film on the monolith had the highest uniformity and smallest size of crystals.The catalytic property of monolithsupported film was tested for epoxidation of allyl chloride(ACH)by H2O2in a fixed bed reactor.Under the condition of a methanol(solvent)/ACH(90% )/H2O2(30% )ratio of 12:1:1,a LHSV of 1.35 h-1and a temperature of 318 K,the conversion of allyl chloride and the selectivity to epichlorohydrin reached 79% and 51% ,respectively.展开更多
Ni-based, Fe-based and Co-based oxygen carriers with perovskite oxides used as the supports were prepared by citric acid complexation method, The oxygen carriers were characterized by thermal analysis, H2-temperature-...Ni-based, Fe-based and Co-based oxygen carriers with perovskite oxides used as the supports were prepared by citric acid complexation method, The oxygen carriers were characterized by thermal analysis, H2-temperature-programmed reduction and X-ray diffraction methods. Performance tests were evaluated through Chemical-Looping Hydrogen Genera- tion in a fixed-bed reactor operating at atmospheric pressure. The characterization results showed that all samples were composed of metal oxides and perovskite oxides. Performance results indicated that CH4 conversion over the oxygen car- riers decreased in the lbllowing order： NiO/LaNiO3〉Co203/LaCoO3〉Fe203/LaFeO3. The ability of NiO/LaNiO3 and F%O3/ LaFeO3 to decompose water was stronger than that of Co203/LaCoO3 as evidenced by our experiments. H2 amounting to 80 mL upon reacting on methane in every cycle could be completely oxidized by NiO/LaNiO3 at 900℃ in the period from the third cycle to the eighth cycle.展开更多
基金the Natural Science Foundation of Shanxi Province,China(No.2011011023-2)for financial support
文摘Titanium silicalite-1(TS-1)films were synthesized on stainless steel plate,glass slide and monolith supports via an in-situ hydrothermal method.Characterization data showed that the formation of TS-1 films was easier on the porous flat support with rough surface such as monolith than on the smooth non-porous supports like glass slide and stainless steel plate.The film on the monolith had the highest uniformity and smallest size of crystals.The catalytic property of monolithsupported film was tested for epoxidation of allyl chloride(ACH)by H2O2in a fixed bed reactor.Under the condition of a methanol(solvent)/ACH(90% )/H2O2(30% )ratio of 12:1:1,a LHSV of 1.35 h-1and a temperature of 318 K,the conversion of allyl chloride and the selectivity to epichlorohydrin reached 79% and 51% ,respectively.
基金supported by China Petrochemical Corporation(SINOPEC)(Contact No.106002000284)
文摘Ni-based, Fe-based and Co-based oxygen carriers with perovskite oxides used as the supports were prepared by citric acid complexation method, The oxygen carriers were characterized by thermal analysis, H2-temperature-programmed reduction and X-ray diffraction methods. Performance tests were evaluated through Chemical-Looping Hydrogen Genera- tion in a fixed-bed reactor operating at atmospheric pressure. The characterization results showed that all samples were composed of metal oxides and perovskite oxides. Performance results indicated that CH4 conversion over the oxygen car- riers decreased in the lbllowing order： NiO/LaNiO3〉Co203/LaCoO3〉Fe203/LaFeO3. The ability of NiO/LaNiO3 and F%O3/ LaFeO3 to decompose water was stronger than that of Co203/LaCoO3 as evidenced by our experiments. H2 amounting to 80 mL upon reacting on methane in every cycle could be completely oxidized by NiO/LaNiO3 at 900℃ in the period from the third cycle to the eighth cycle.