IPS-Empress 2玻璃陶瓷结构及性能的研究

目的 研究新型IPS Empress2牙科高强度陶瓷的显微结构和机械性能。方法 采用原子力显微镜、扫描电子显微镜和X射线衍射仪,分析IPS Empress2的显微结构和晶相,用三点弯曲实验和压痕法测试其弯曲强度和断裂韧性。结果 IPS Empress2玻璃陶瓷主要由二硅酸锂晶体和磷酸锂晶体组成,二者形成相互交错的三维网络式结构;这种玻璃陶瓷在热压铸前后晶体相保持不变,其三点弯曲强度和断裂韧性分别为 300MPa和 3 1MPam1 /2。结论 IPS Empress2玻璃陶瓷的高强度和韧性与高含量的二硅酸锂晶体、相互锁结的网络结构和裂纹偏转有关。

Microstructure and microwave dielectric properties of lead borosilicate glass ceramics with Al_2O_3

The effects of Al2O3 addition on both the sintering behavior and microwave dielectric properties of PbO-B203-SiO2 glass ceramics were investigated by Fourier transform infrared spectroscope （FTIR）, differential thermal analysis （DTA）, X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The results show that with the increase of Al2O3 content the bands assigned to [SiO4] nearly disappear. Aluminum replaces silicon in the glass network, which is helpful for the formation of boron-oxygen rings. The increase of the transition temperature Tg and softening temperature Tf of PbO-B2O3-SiO2 glass ceramics leads to the increase of liquid phase precipitation temperature and promotes the structure stability in the glasses, and consequently contributes to the decreasing trend of crystallization. Densification and dielectric constants increase with the increase of Al2O3 content, but the dielectric loss is worsened. By contrast, the 3% （mass fraction） Al2O3-doped glass ceramics sintered at 725℃ have better properties of density p=2.72 g/cm3, dielectric constant Er=6.78, dielectric loss tan8=2.6×10^-3 （measured at 9.8 GHz）, which suggest that the glass ceramics can be applied in multilayer microwave devices requiring low sintering temperatures.

Microstructure and microwave dielectric properties of CaO-B_2O_3-SiO_2 glass ceramics with various B_2O_3 contents

The effects of B2O3 addition on both the sintering behavior and microwave dielectric properties of CaO-B2O3-SiO2 （CBS） glass ceramics were investigated by Fourier transform infrared spectroscopy （FTIR）, X-ray diffractometry （XRD） and scanning electron microscopy （SEM）. The results show that the increasing amount of B203 causes the increase of the contents of [BO3], [BO4] and [SiO4], which deduces the increase of CaB204 and a-SiO2 and the decrease of CaSiO3 correspondingly. No new phase is observed throughout the entire experiments. A bulk density of 2.54 g/cm3, a thermal expansion coefficient value of 11.95× 10-6 ℃-1 （20-500℃）, a dielectric constant er value of 6.42 and a dielectric loss tanδ value of 0.000 9 （measured at 9.7 GHz） are obtained for CBS glass ceramics containing 35%-B203 （mass fraction） sintered at 850 ℃ for 15 min.

Effect of nucleating agents on microstructure and mechanical properties of SiO_2-Al_2O_3-ZrO_2 glass-ceramics

SiO2-Al2O3-ZrO2 glasses with different nucleating agents were crystallized under special processing schedule. The microstructure and mechanical properties of the glass-ceramics in SiO2-Al2O3-ZrO2 system were investigated by differential scanning calorimetry, scanning electron microscopy, X-ray diffraction and three-point bending method. The results show that ZrO2 is not an effective nucleating agent in SiO2-Al2O3-ZrO2 system, while TiO2 is effective for the separation of spinel, and P2O5 facilitates solubility of ZrO2 in glass and crystallization. The main crystalline phases of the glass-ceramics are spinel, anorthite and tetragonal zirconia. With the increase of ZrO2 content in the glass, glass-ceramics show higher bending strength （120MPa） than others.

Effects of ZrO_2 on the Microstructure of a Mica Glass-ceramic

The effects of ZrO2 on the crystallinity of mica and microstructure of a machina- ble glassceramic were studied. It was found that ZrO2 is an effective nucleation agent in mica glass- ceramics. Stabilized by Ca2+, a lot of t--ZrO2 particles precipitate from ZrO2-mica glass-ceramics. The ZrO2 particles can effectively limit the growth of mica crystal and benefit the mechanical properties of glass-ceramics.

Structural characteristics and dielectric properties of glass-ceramic nanocomposites of(Pb,Sr)Nb_2O_6-NaNbO_3-SiO_2

The structure and dielectric properties of （Pb,Sr）Nb2O6-NaNbO3-SiO2 glass-ceramics with different Pb and Sr contents were investigated. The XRD pattern of glass-ceramics without Sr substitution is different from that with Sr substitution, which indicates the existence of orthorhombic phase in the latter ones. TEM bright field observation shows nanosized microstructures, while for samples with Sr, typical eutectic microstrncture with separated crystallized bands is found in the glass matrix. Dielectric properties measurement of the samples indicates an obvious improvement of dielectric constant, dielectric loss, DC field and temperature dependence of dielectric constant when the molar ratio of Sr to Pb is 4：6.

Upconversion Luminescence of Er^3＋ and Co-Doped Er^3＋/Yb^3＋ Novel Transparent Oxyfluoride Glasses and Glass Ceramics： Spectral and Structural Properties

Transparent oxyfluoride silicate precursor glasses and glass ceramics with the novel composition （1） SiO2-PbO-PbFE-Er2O3, （2） SiO2-GeOE-PbO-PbFE-Er2O3 （3） SiO2-Al2O3-Y2O3-Na2O-NaF-LiF-Er2O3-YbF3 doped with Er^3＋ and co-doped with Er^3＋/Yb^3＋ ions were synthesized. X-ray diffraction analysis （XRD） and Er3＋ absorption spectra revealed precipitation of PbF2 nanocrystals dispersed in the glassy matrix. Under 980 nm laser excitation, intense green, red and near IR bands of upconversion luminescence （UCL） were recorded both before and after heat treatment. In the glass ceramics the upconversion intensity increased significantly. To our knowledge, for the first time the composition of the glass ceramics characterized by the small-angle neutron scattering （SANS） showed the cluster organization of PbF2 nanocrystals.