The growth behavior of the complex intermetallic compounds(IMCs)formed at the interface of Cu/SnPbInBiSb high entropy alloy solder joints was explored.The growth inhibition mechanism of the IMCs at the Cu/SnPbInBiSb s...The growth behavior of the complex intermetallic compounds(IMCs)formed at the interface of Cu/SnPbInBiSb high entropy alloy solder joints was explored.The growth inhibition mechanism of the IMCs at the Cu/SnPbInBiSb solid−liquid reaction interface was revealed.The results showed that the growth rate of the complex IMCs obviously decreased at the Cu/SnPbInBiSb solid−liquid reaction interface.The maximum average thickness of IMCs only reached up to 1.66μm after reflowing at 200℃for 10 min.The mechanism for the slow growth of the complex IMCs was analyzed into three aspects.Firstly,the high entropy of the liquid SnPbInBiSb alloy reduced the growth rate of the complex IMCs.Secondly,the distorted lattice of complex IMCs restrained the diffusion of Cu atoms.Lastly,the higher activation energy(40.9 kJ/mol)of Cu/SnPbInBiSb solid−liquid interfacial reaction essentially impeded the growth of the complex IMCs.展开更多
Effect of thermal stabilization on the microstructure and mechanical property of directionally solidified Ti-46Al-0.5W-0.5Si （mole fraction, %） alloy was investigated. The specimens were thermal stabilized for diffe...Effect of thermal stabilization on the microstructure and mechanical property of directionally solidified Ti-46Al-0.5W-0.5Si （mole fraction, %） alloy was investigated. The specimens were thermal stabilized for different time （t） and directionally solidified at a constant growth rate of 30 μm/s and temperature gradient of 20 K/mm. Dependencies of the primary dendritic spacing （λ1）, secondary dendritic spacing （λ2）, interlamellar spacing （λL） and microhardness （HV） on holding time were determined. The values of the λ1, λ2 and λL increase with the increase of t, and the value of HV decreases with the increase of t. The increase of t is helpful to obtain a good directional solidification structure. However, it reduces the mechanical property of the directionally solidified TiAl alloy. The optimized value of t is about 30 min.展开更多
A study was conducted to evaluate the effects of meat and bone meal (MBM) and poultry by-product meal (PBM) as the replacement of fish meal in the diets on the growth performance, survival and apparent digestibility c...A study was conducted to evaluate the effects of meat and bone meal (MBM) and poultry by-product meal (PBM) as the replacement of fish meal in the diets on the growth performance, survival and apparent digestibility coefficients (ADC) of Litopenaeus vannamei. The basal diets were formulated with 22% fish meal and other ingredients which provided about 40% protein and 9% lipid in the diet. The experimental diets included MBM or PBM to replace 0, 20%, 40%, 60% and 80% of total fish meal respectively. All diets were iso-nitrogenous and isocaloric in gross terms. The results showed that there were no significant differences (P>0.05) in growth performance and ADC among the treatments fed with the diets in which 0-60% fish meal had been replaced with MBM, while the percent weight gain (WG, %), body length gain (BLG, %) and ADC significantly decreased when the MBM was up to 80% of the fish meal. There were no significant differences (P>0.05) in growth performance and ADC among all the treatments fed with the diets in which 0-80% fish meal had been replaced with PBM.展开更多
The surface morphology of Ti-Mg supported catalyst and the polyethyleneparticles are studied using scanning electron microscope(SEM) technology. The results show thateithen the catalyst's surface or polymer partic...The surface morphology of Ti-Mg supported catalyst and the polyethyleneparticles are studied using scanning electron microscope(SEM) technology. The results show thateithen the catalyst's surface or polymer particle's surface is irregular and has fractalcharacteristics, which can be described by fractal parameter. The more interesting discovery is thatthe surface fractal dimension values of the polymer particles vary periodically with thepolymerization time. We call this phenomenon fractal evolution, which can be divided into the'revolution' stage and the 'evolution' stage. And then we present polymerization fractal growingmodel (PFGM), and successfully describe and/or predict the whole evolving process of thepolyethylene particle morphology under the different slurry polymerization (includingpre-polymerization) conditions without H_2.展开更多
Porous anodic oxide films were fabricated galvanostatically on titanium alloy Ti-10V-2Fe-3Al in ammonium tartrate solution with different anodizing time.Scanning electron microscopy(SEM) and field emission scanning el...Porous anodic oxide films were fabricated galvanostatically on titanium alloy Ti-10V-2Fe-3Al in ammonium tartrate solution with different anodizing time.Scanning electron microscopy(SEM) and field emission scanning electron microscopy(FE-SEM) were used to investigate the morphology evolution of the anodic oxide film.It is shown that above the breakdown voltage,oxygen is generated with the occurrence of drums morphology.These drums grow and extrude,which yields the compression stress.Subsequently,microcracks are generated.With continuous anodizing,porous oxides form at the microcracks.Those oxides grow and connect to each other,finally replace the microcrack morphology.The depth profile of the anodic oxide film formed at 1 800 s was examined by Auger electron spectroscopy(AES).It is found that the film is divided into three layers according to the molar fractions of elements.The outer layer is incorporated by carbon,which may come from electrolyte solution.The thickness of the outer layer is approximately 0.2-0.3 μm.The molar fractions of elements in the intermediate layer are extraordinarily stable,while those in the inner layer vary significantly with sputtering depth.The thicknesses of the intermediate layer and the inner layer are 2 μm and 1.0-1.5 μm,respectively.Moreover,the growth mechanism of porous anodic oxide films in neutral tartrate solution was proposed.展开更多
基金supported by the National Natural Science Foundation of China (No.U2241223)the Heilongjiang Touyan Innovation Team Program,China (No.HITTY-20190013)the Fundamental Research Funds for the Central Universities,China (No.AUEA5770400622)。
文摘The growth behavior of the complex intermetallic compounds(IMCs)formed at the interface of Cu/SnPbInBiSb high entropy alloy solder joints was explored.The growth inhibition mechanism of the IMCs at the Cu/SnPbInBiSb solid−liquid reaction interface was revealed.The results showed that the growth rate of the complex IMCs obviously decreased at the Cu/SnPbInBiSb solid−liquid reaction interface.The maximum average thickness of IMCs only reached up to 1.66μm after reflowing at 200℃for 10 min.The mechanism for the slow growth of the complex IMCs was analyzed into three aspects.Firstly,the high entropy of the liquid SnPbInBiSb alloy reduced the growth rate of the complex IMCs.Secondly,the distorted lattice of complex IMCs restrained the diffusion of Cu atoms.Lastly,the higher activation energy(40.9 kJ/mol)of Cu/SnPbInBiSb solid−liquid interfacial reaction essentially impeded the growth of the complex IMCs.
基金Projects (50801019, 51071062, 50771041) supported by the National Natural Science Foundation of ChinaProject (2011CB605504) supported by the National Basic Research Program of China
文摘Effect of thermal stabilization on the microstructure and mechanical property of directionally solidified Ti-46Al-0.5W-0.5Si （mole fraction, %） alloy was investigated. The specimens were thermal stabilized for different time （t） and directionally solidified at a constant growth rate of 30 μm/s and temperature gradient of 20 K/mm. Dependencies of the primary dendritic spacing （λ1）, secondary dendritic spacing （λ2）, interlamellar spacing （λL） and microhardness （HV） on holding time were determined. The values of the λ1, λ2 and λL increase with the increase of t, and the value of HV decreases with the increase of t. The increase of t is helpful to obtain a good directional solidification structure. However, it reduces the mechanical property of the directionally solidified TiAl alloy. The optimized value of t is about 30 min.
文摘A study was conducted to evaluate the effects of meat and bone meal (MBM) and poultry by-product meal (PBM) as the replacement of fish meal in the diets on the growth performance, survival and apparent digestibility coefficients (ADC) of Litopenaeus vannamei. The basal diets were formulated with 22% fish meal and other ingredients which provided about 40% protein and 9% lipid in the diet. The experimental diets included MBM or PBM to replace 0, 20%, 40%, 60% and 80% of total fish meal respectively. All diets were iso-nitrogenous and isocaloric in gross terms. The results showed that there were no significant differences (P>0.05) in growth performance and ADC among the treatments fed with the diets in which 0-60% fish meal had been replaced with MBM, while the percent weight gain (WG, %), body length gain (BLG, %) and ADC significantly decreased when the MBM was up to 80% of the fish meal. There were no significant differences (P>0.05) in growth performance and ADC among all the treatments fed with the diets in which 0-80% fish meal had been replaced with PBM.
基金Supported by the National Natural Science Foundation of China (No. 29706010, No. 20203016).
文摘The surface morphology of Ti-Mg supported catalyst and the polyethyleneparticles are studied using scanning electron microscope(SEM) technology. The results show thateithen the catalyst's surface or polymer particle's surface is irregular and has fractalcharacteristics, which can be described by fractal parameter. The more interesting discovery is thatthe surface fractal dimension values of the polymer particles vary periodically with thepolymerization time. We call this phenomenon fractal evolution, which can be divided into the'revolution' stage and the 'evolution' stage. And then we present polymerization fractal growingmodel (PFGM), and successfully describe and/or predict the whole evolving process of thepolyethylene particle morphology under the different slurry polymerization (includingpre-polymerization) conditions without H_2.
基金Project(50571003) supported by the National Natural Science Foundation of China
文摘Porous anodic oxide films were fabricated galvanostatically on titanium alloy Ti-10V-2Fe-3Al in ammonium tartrate solution with different anodizing time.Scanning electron microscopy(SEM) and field emission scanning electron microscopy(FE-SEM) were used to investigate the morphology evolution of the anodic oxide film.It is shown that above the breakdown voltage,oxygen is generated with the occurrence of drums morphology.These drums grow and extrude,which yields the compression stress.Subsequently,microcracks are generated.With continuous anodizing,porous oxides form at the microcracks.Those oxides grow and connect to each other,finally replace the microcrack morphology.The depth profile of the anodic oxide film formed at 1 800 s was examined by Auger electron spectroscopy(AES).It is found that the film is divided into three layers according to the molar fractions of elements.The outer layer is incorporated by carbon,which may come from electrolyte solution.The thickness of the outer layer is approximately 0.2-0.3 μm.The molar fractions of elements in the intermediate layer are extraordinarily stable,while those in the inner layer vary significantly with sputtering depth.The thicknesses of the intermediate layer and the inner layer are 2 μm and 1.0-1.5 μm,respectively.Moreover,the growth mechanism of porous anodic oxide films in neutral tartrate solution was proposed.