A promising Co3O4/Cu O composite electrode material was successfully synthesized through a facile hydrothermal and calcination process. Effects of the surfactants hexadecyltrimethyl ammonium bromide（CTAB） and polyvi...A promising Co3O4/Cu O composite electrode material was successfully synthesized through a facile hydrothermal and calcination process. Effects of the surfactants hexadecyltrimethyl ammonium bromide（CTAB） and polyvinylpyrrolidone（PVP） on the morphology and electrochemical performance of the composite were investigated. Powder X-ray diffraction（XRD）, scanning electron microscopy（SEM）, transmission electron microscopy（TEM） and nitrogen adsorption-desorption experiment were employed to characterize the microstructures and morphologies of the composite. Meanwhile, the electrochemical performances of the samples were studied using cyclic voltammetry（CV）, galvanostatic charge-discharge test and electrochemical impedance spectroscopy（EIS）. The results show that the porous Co3O4/Cu O-CTAB nanoplates own the best performance and exhibits a high specific capacitance of 398 F/g at 1 A/g with almost 100% capacitance retention over 2000 cycles, and it retains 90% of capacitance at 10 A/g.展开更多
基金Project(21471162)supported by the National Natural Science Foundation of ChinaProject(2014LY36)supported by the Science and Technology Project of Longyan CityChina
文摘A promising Co3O4/Cu O composite electrode material was successfully synthesized through a facile hydrothermal and calcination process. Effects of the surfactants hexadecyltrimethyl ammonium bromide（CTAB） and polyvinylpyrrolidone（PVP） on the morphology and electrochemical performance of the composite were investigated. Powder X-ray diffraction（XRD）, scanning electron microscopy（SEM）, transmission electron microscopy（TEM） and nitrogen adsorption-desorption experiment were employed to characterize the microstructures and morphologies of the composite. Meanwhile, the electrochemical performances of the samples were studied using cyclic voltammetry（CV）, galvanostatic charge-discharge test and electrochemical impedance spectroscopy（EIS）. The results show that the porous Co3O4/Cu O-CTAB nanoplates own the best performance and exhibits a high specific capacitance of 398 F/g at 1 A/g with almost 100% capacitance retention over 2000 cycles, and it retains 90% of capacitance at 10 A/g.