A star network polymer with a pentaerythritol core linking four PEG-block polymeric arms was synthesized, and its corresponding gel polymer electrolyte based on lithium perchlorate and plasticizers EC/PC with the char...A star network polymer with a pentaerythritol core linking four PEG-block polymeric arms was synthesized, and its corresponding gel polymer electrolyte based on lithium perchlorate and plasticizers EC/PC with the character being colorless and highly transparent has been also prepared. The polymer host was characterized and confirmed to be of a star network and an amorphous structure by FTIR, ^1H NMR and XRD studies. The polymer host hold good mechanical properties for pentaerythritol cross-linking. Maximum ionic conductivity of the prepared polymer electrolyte has reached 8.83 × 10 ^-4 S·cm^-1 at room temperature. Thermogravimetry （TG） of the polymer electrolyte showed that the thermal stability was up to at least 150 ℃. The gel polymer electrolyte was further evaluated in electrochromic devices fabricated by transparent PET-ITO and electrochromically active viologen derivative films, and its excellent performance promised the usage of the gel polymer electrolyte as ionic conductor material in electrochrornic devices.展开更多
The effects of mesogen-jacketed liquid crystalline polymer poly(dipropyl vinylterephthalate)(PDPVT) on the mechanical and thermal properties of diglycidyl ether of bisphenol-A(DGEBA) epoxy resin were investigated by i...The effects of mesogen-jacketed liquid crystalline polymer poly(dipropyl vinylterephthalate)(PDPVT) on the mechanical and thermal properties of diglycidyl ether of bisphenol-A(DGEBA) epoxy resin were investigated by impact test, tensile test and thermogravimetric analysis(TGA). The mechanism underlying the enhancement of mechanical properties of epoxy resin was studied using 1D wide-angle X-ray diffraction(WAXD) and scanning electron microscope(SEM). It was found that the mechanical properties of 1 wt%–5 wt% PDPVT/DGEBA composites were significantly improved compared to neat epoxy resin. Especially, the epoxy resin with 3 wt% PDPVT had the greatest increase in mechanical properties, with the impact strength, tensile strength and elongation while breaking increased by 87%, 59% and 174%, respectively. The increased mechanical strength was due to the fact that PDPVT maintained liquid crystalline phase in cured PDPVT/DGEBA composites, which would blunt the crack tip and prevent crack propagation. Moreover, PDPVT had slight effect on the thermal stability properties of epoxy resin.展开更多
文摘A star network polymer with a pentaerythritol core linking four PEG-block polymeric arms was synthesized, and its corresponding gel polymer electrolyte based on lithium perchlorate and plasticizers EC/PC with the character being colorless and highly transparent has been also prepared. The polymer host was characterized and confirmed to be of a star network and an amorphous structure by FTIR, ^1H NMR and XRD studies. The polymer host hold good mechanical properties for pentaerythritol cross-linking. Maximum ionic conductivity of the prepared polymer electrolyte has reached 8.83 × 10 ^-4 S·cm^-1 at room temperature. Thermogravimetry （TG） of the polymer electrolyte showed that the thermal stability was up to at least 150 ℃. The gel polymer electrolyte was further evaluated in electrochromic devices fabricated by transparent PET-ITO and electrochromically active viologen derivative films, and its excellent performance promised the usage of the gel polymer electrolyte as ionic conductor material in electrochrornic devices.
基金financially supported by the National Natural Science Foundation of China(51343008)
文摘The effects of mesogen-jacketed liquid crystalline polymer poly(dipropyl vinylterephthalate)(PDPVT) on the mechanical and thermal properties of diglycidyl ether of bisphenol-A(DGEBA) epoxy resin were investigated by impact test, tensile test and thermogravimetric analysis(TGA). The mechanism underlying the enhancement of mechanical properties of epoxy resin was studied using 1D wide-angle X-ray diffraction(WAXD) and scanning electron microscope(SEM). It was found that the mechanical properties of 1 wt%–5 wt% PDPVT/DGEBA composites were significantly improved compared to neat epoxy resin. Especially, the epoxy resin with 3 wt% PDPVT had the greatest increase in mechanical properties, with the impact strength, tensile strength and elongation while breaking increased by 87%, 59% and 174%, respectively. The increased mechanical strength was due to the fact that PDPVT maintained liquid crystalline phase in cured PDPVT/DGEBA composites, which would blunt the crack tip and prevent crack propagation. Moreover, PDPVT had slight effect on the thermal stability properties of epoxy resin.