Microstructural evolution and dynamic recrystallization(DRX)mechanisms of a Ti-48Al-2Cr-2Nb(at.%)alloy prepared by selective electron beam melting(SEBM)during hot deformation at 1150℃and 0.1 s^(-1)were investigated b...Microstructural evolution and dynamic recrystallization(DRX)mechanisms of a Ti-48Al-2Cr-2Nb(at.%)alloy prepared by selective electron beam melting(SEBM)during hot deformation at 1150℃and 0.1 s^(-1)were investigated by hot compression tests,optical microscope(OM),scanning electron microscope(SEM),electron back-scattered diffraction(EBSD)and transmission electron microscope(TEM).The results show that the initial microstructure of the as-SEBMed alloy exhibits layers of coarseγgrains and fineγ+α_(2)+(α_(2)/γ)lamellar mixture grains alternately along the building direction.During the early stage of hot deformation,deformation twins tend to form within the coarse grains,facilitating subsequent deformation,and a small number of DRX grains appear in the fine-grained regions.With the increase of strain,extensive DRX grains are formed through different DRX mechanisms in both coarse and fine-grained regions,involving discontinuous dynamic recrystallization mechanism(DDRX)in the fine-grained regions and a coexistence of DDRX and continuous dynamic recrystallization(CDRX)in the coarsegrained regions.展开更多
In order to analyze the effect of voltage during micro-arc oxidation(MAO)on corrosion and wear properties of Ti6Al4V(TC4),the MAO technology was employed to treat TC4 samples fabricated by selective electron beam melt...In order to analyze the effect of voltage during micro-arc oxidation(MAO)on corrosion and wear properties of Ti6Al4V(TC4),the MAO technology was employed to treat TC4 samples fabricated by selective electron beam melting(SEBM)at the voltages of 400,420 and 450 V.The results show that the metastable anatase phase gradually transforms to rutile phase with oxidation time and temperature increasing.The surface morphology of coating contains numerous micropores with uniform size distribution.Cracks and pores over 10μm are found on MAO-TC4 sample with applied voltage of 450 V.The thickness of MAO coating is positively correlated with the voltage.The corrosion resistance and wear resistance are related to phase composition,micropore size distribution on the surface and film thickness.When the voltage is 420 V,the coating shows the smallest corrosion current density(0.960×10^-7 A/cm^2)and the largest resistance(7.17×10^5Ω·cm^2).Under the same load condition,the coating exhibits larger friction coefficient and wear loss than the TC4 substrate.With the increase of voltage,the wear mechanism of the coating changes from abrasive wear to adhesive wear,and the adhesive wear is intensified at applied voltage of 450 V,with a maximum friction coefficient of 0.821.展开更多
The effect of porosity on compressive,bending,and tensile properties of the porous tantalum scaffolds fabricated by electron beam powder bed fusion(EB-PBF)was investigated.The porous tantalum scaffolds with porosity f...The effect of porosity on compressive,bending,and tensile properties of the porous tantalum scaffolds fabricated by electron beam powder bed fusion(EB-PBF)was investigated.The porous tantalum scaffolds with porosity from 69%to 77.8%were obtained by varying the designed porosity and adjusting the processing parameters.It is found that the pores and unfused powder decrease with the increase of deposited energy density.The decrease of porosity leads to an improvement in mechanical properties.The relevancy between compressive/bending/tensile yield strength and relative density can be described appropriately by exponential model,while the relationship between elastic modulus and relative density is in good agreement with the Gibson-Ashby model.All the porous tantalum scaffolds exhibit good ductility in compressive,bending and tensile tests.No fragmentation of struts is observed during the compression process,but cracks are formed on the strut surface after 90°bending,mainly due to the high sensibility to defects caused by the oxide.展开更多
基金the financial supports from the Shaanxi Province Key Research and Development Projects,China(No.2023KXJ-071)the National Natural Science Foundation of China(Nos.52274402,52174381)。
文摘Microstructural evolution and dynamic recrystallization(DRX)mechanisms of a Ti-48Al-2Cr-2Nb(at.%)alloy prepared by selective electron beam melting(SEBM)during hot deformation at 1150℃and 0.1 s^(-1)were investigated by hot compression tests,optical microscope(OM),scanning electron microscope(SEM),electron back-scattered diffraction(EBSD)and transmission electron microscope(TEM).The results show that the initial microstructure of the as-SEBMed alloy exhibits layers of coarseγgrains and fineγ+α_(2)+(α_(2)/γ)lamellar mixture grains alternately along the building direction.During the early stage of hot deformation,deformation twins tend to form within the coarse grains,facilitating subsequent deformation,and a small number of DRX grains appear in the fine-grained regions.With the increase of strain,extensive DRX grains are formed through different DRX mechanisms in both coarse and fine-grained regions,involving discontinuous dynamic recrystallization mechanism(DDRX)in the fine-grained regions and a coexistence of DDRX and continuous dynamic recrystallization(CDRX)in the coarsegrained regions.
基金Projects(51504191,51671152,51874225)supported by the National Natural Science Foundation of ChinaProject supported by the Fund of State Key Laboratory of Porous Metal Materials,China。
文摘In order to analyze the effect of voltage during micro-arc oxidation(MAO)on corrosion and wear properties of Ti6Al4V(TC4),the MAO technology was employed to treat TC4 samples fabricated by selective electron beam melting(SEBM)at the voltages of 400,420 and 450 V.The results show that the metastable anatase phase gradually transforms to rutile phase with oxidation time and temperature increasing.The surface morphology of coating contains numerous micropores with uniform size distribution.Cracks and pores over 10μm are found on MAO-TC4 sample with applied voltage of 450 V.The thickness of MAO coating is positively correlated with the voltage.The corrosion resistance and wear resistance are related to phase composition,micropore size distribution on the surface and film thickness.When the voltage is 420 V,the coating shows the smallest corrosion current density(0.960×10^-7 A/cm^2)and the largest resistance(7.17×10^5Ω·cm^2).Under the same load condition,the coating exhibits larger friction coefficient and wear loss than the TC4 substrate.With the increase of voltage,the wear mechanism of the coating changes from abrasive wear to adhesive wear,and the adhesive wear is intensified at applied voltage of 450 V,with a maximum friction coefficient of 0.821.
基金supported by the Key R&D Program of Guangdong Province,China(Nos.2019B090904001,2018B090906003)。
文摘The effect of porosity on compressive,bending,and tensile properties of the porous tantalum scaffolds fabricated by electron beam powder bed fusion(EB-PBF)was investigated.The porous tantalum scaffolds with porosity from 69%to 77.8%were obtained by varying the designed porosity and adjusting the processing parameters.It is found that the pores and unfused powder decrease with the increase of deposited energy density.The decrease of porosity leads to an improvement in mechanical properties.The relevancy between compressive/bending/tensile yield strength and relative density can be described appropriately by exponential model,while the relationship between elastic modulus and relative density is in good agreement with the Gibson-Ashby model.All the porous tantalum scaffolds exhibit good ductility in compressive,bending and tensile tests.No fragmentation of struts is observed during the compression process,but cracks are formed on the strut surface after 90°bending,mainly due to the high sensibility to defects caused by the oxide.