Modification of poly(tetrafluoroethylene)(PTFE) films with 2-methacryloyloxyethyl phosphorylcholine(MPC) was performed by low-temperature plasma treatment and grafting polymerization.Surface properties of PTFE were ch...Modification of poly(tetrafluoroethylene)(PTFE) films with 2-methacryloyloxyethyl phosphorylcholine(MPC) was performed by low-temperature plasma treatment and grafting polymerization.Surface properties of PTFE were characterized by attenuated total reflectance Fourier transform infrared(ATR-FTIR) spectra,X-ray photoelectron spectroscopy(XPS) ,and static contact angle.The results show that MPC has been grafted onto PTFE film surface successfully.Contact angle for the modified PTFE films in the water decreased from 108°to 58.25°,while surface energy increased from 17.52 mN/m to 45.47 mN/m.The effects of plasma treatment time,monomer concentration and grafting time on degree of grafting were determined.In the meanwhile,blood compatibility of the PTFE films was studied by checking thrombogenic time of blood plasma.展开更多
Despite the advances of aqueous zinc(Zn)batteries as sustainable energy storage systems,their practical application remains challenging due to the issues of spontaneous corrosion and dendritic deposits at the Zn metal...Despite the advances of aqueous zinc(Zn)batteries as sustainable energy storage systems,their practical application remains challenging due to the issues of spontaneous corrosion and dendritic deposits at the Zn metal anode.In this work,conformal growth of zinc hydroxide sulfate(ZHS)with dominating(001)facet was realized on(002)plane-dominated Zn metal foil fabricated through a facile thermal annealing process.The ZHS possessed high Zn^(2+)conductivity(16.9 mS cm^(-1))and low electronic conductivity(1.28×10^(4)Ωcm),and acted as a heterogeneous and robust solid electrolyte interface(SEI)layer on metallic Zn electrode,which regulated the electrochemical Zn plating behavior and suppressed side reactions simultaneously.Moreover,low self-diffusion barrier along the(002)plane promoted the 2D diffusion and horizontal electrochemical plating of metallic Zn for(002)-textured Zn electrode.Consequently,the as-achieved Zn electrode exhibited remarkable cycling stability over 7000 cycles at 2 mA cm^(-2)and 0.5 mAh cm^(-2)with a low overpotential of 25 mV in symmetric cells.Pairing with a MnO_(2)cathode,the as-achieved Zn electrode achieved stable cell cycling with 92.7%capacity retention after 1000 cycles at 10 C with a remarkable average Coulombic efficiency of 99.9%.展开更多
文摘Modification of poly(tetrafluoroethylene)(PTFE) films with 2-methacryloyloxyethyl phosphorylcholine(MPC) was performed by low-temperature plasma treatment and grafting polymerization.Surface properties of PTFE were characterized by attenuated total reflectance Fourier transform infrared(ATR-FTIR) spectra,X-ray photoelectron spectroscopy(XPS) ,and static contact angle.The results show that MPC has been grafted onto PTFE film surface successfully.Contact angle for the modified PTFE films in the water decreased from 108°to 58.25°,while surface energy increased from 17.52 mN/m to 45.47 mN/m.The effects of plasma treatment time,monomer concentration and grafting time on degree of grafting were determined.In the meanwhile,blood compatibility of the PTFE films was studied by checking thrombogenic time of blood plasma.
基金financial support by the Innovation Fund of Wuhan National Laboratory for Optoelectronics of Huazhong University of Science and Technologythe China Postdoctoral Science Foundation (2018M640694 and 2020T130223)+1 种基金support of the Singapore National Research Foundation (NRF-NRFF2017-04)Agency for Science, Technology and Research (Central Research Fund Award)
文摘Despite the advances of aqueous zinc(Zn)batteries as sustainable energy storage systems,their practical application remains challenging due to the issues of spontaneous corrosion and dendritic deposits at the Zn metal anode.In this work,conformal growth of zinc hydroxide sulfate(ZHS)with dominating(001)facet was realized on(002)plane-dominated Zn metal foil fabricated through a facile thermal annealing process.The ZHS possessed high Zn^(2+)conductivity(16.9 mS cm^(-1))and low electronic conductivity(1.28×10^(4)Ωcm),and acted as a heterogeneous and robust solid electrolyte interface(SEI)layer on metallic Zn electrode,which regulated the electrochemical Zn plating behavior and suppressed side reactions simultaneously.Moreover,low self-diffusion barrier along the(002)plane promoted the 2D diffusion and horizontal electrochemical plating of metallic Zn for(002)-textured Zn electrode.Consequently,the as-achieved Zn electrode exhibited remarkable cycling stability over 7000 cycles at 2 mA cm^(-2)and 0.5 mAh cm^(-2)with a low overpotential of 25 mV in symmetric cells.Pairing with a MnO_(2)cathode,the as-achieved Zn electrode achieved stable cell cycling with 92.7%capacity retention after 1000 cycles at 10 C with a remarkable average Coulombic efficiency of 99.9%.