Aluminum capacitor foils with a tunnel etch structure were reacted with boiling water and then anodized at 530 V in boric acid solution or boric acid＋citric acid mixed solution.The microstructure and crystallinity of...Aluminum capacitor foils with a tunnel etch structure were reacted with boiling water and then anodized at 530 V in boric acid solution or boric acid＋citric acid mixed solution.The microstructure and crystallinity of the resulting anodized film were examined by TEM and XRD.The special capacitance,resistance and withstanding voltage of the film were explored with electrochemical impedance spectroscopy（EIS）,LCR meter and small-current charging.The results show that the high voltage anodized oxide film consists of an inner layer with high crystallinity and an outer layer with low crystallinity.However,the crystallinity of the film formed in boric acid＋citric acid mixed solution is higher than that of the film formed in only boric acid solution,leading to an increase in film＇s field strength and special capacitance.Meanwhile,there are more defects from phase transformation in the out layer of the film formed in boric acid＋citric acid mixed solution than in that of film formed in only boric acid solution,leading to a decrease in film＇s resistance and withstanding voltage.展开更多
基金Project supported by University New Materials Disciplines Construction Program of Beijing Region
文摘Aluminum capacitor foils with a tunnel etch structure were reacted with boiling water and then anodized at 530 V in boric acid solution or boric acid＋citric acid mixed solution.The microstructure and crystallinity of the resulting anodized film were examined by TEM and XRD.The special capacitance,resistance and withstanding voltage of the film were explored with electrochemical impedance spectroscopy（EIS）,LCR meter and small-current charging.The results show that the high voltage anodized oxide film consists of an inner layer with high crystallinity and an outer layer with low crystallinity.However,the crystallinity of the film formed in boric acid＋citric acid mixed solution is higher than that of the film formed in only boric acid solution,leading to an increase in film＇s field strength and special capacitance.Meanwhile,there are more defects from phase transformation in the out layer of the film formed in boric acid＋citric acid mixed solution than in that of film formed in only boric acid solution,leading to a decrease in film＇s resistance and withstanding voltage.