Composite wires of 100 μm insulated CuBewire plated with a layer of NiFeB were produced by elec-troless-deposition, and their magnetic properties were stud-led. The results showed that a good magneto-impedance (MI)ef...Composite wires of 100 μm insulated CuBewire plated with a layer of NiFeB were produced by elec-troless-deposition, and their magnetic properties were stud-led. The results showed that a good magneto-impedance (MI)effect can be obtained at relatively low frequency. The largestMI ratio (△Z/Z)max obtained is 250% at 500 kHz. Mag-neto-resistance effect was also observed at low frequency,with the (△R/R)max observed to be -8.5% at 540 Hz and 38.7% at 10 kHz. Results are discussed, and the equivalent resistance and inductance as the result of the NiFeB layer are taken into account.展开更多
文摘Composite wires of 100 μm insulated CuBewire plated with a layer of NiFeB were produced by elec-troless-deposition, and their magnetic properties were stud-led. The results showed that a good magneto-impedance (MI)effect can be obtained at relatively low frequency. The largestMI ratio (△Z/Z)max obtained is 250% at 500 kHz. Mag-neto-resistance effect was also observed at low frequency,with the (△R/R)max observed to be -8.5% at 540 Hz and 38.7% at 10 kHz. Results are discussed, and the equivalent resistance and inductance as the result of the NiFeB layer are taken into account.