The mineralogical phase transformation of a low-grade nickel laterite ore during pre-roasting process and the extraction of silicon during alkaline leaching process were investigated.The results indicate that the reac...The mineralogical phase transformation of a low-grade nickel laterite ore during pre-roasting process and the extraction of silicon during alkaline leaching process were investigated.The results indicate that the reaction activity of nickel ores is effectively improved by pre-roasting at650°C for2h,because of the transformation of lizardite into magnesium olivine and protoenstatite.When finely ground ore samples(44-61μm)pre-roasted firstly react with sodium hydroxide solution(60g/L)with a solid/liquid ratio of1:5at140°C for120min,the extraction of silicon can reach89.89%,and the other valuable elements of magnesium,iron and nickel are accumulated in the solid residues.The leaching kinetics of nickel laterite ore can be described successfully by the diffusion through the product layer control model.The activation energy is calculated to be11.63kJ/mol and the kinetics equation can be expressed as1-3(1-x)2/3+2(1-x)=13.53×10-2exp[-11.63/(RT)]t.展开更多
Siderite,as an abundant iron ore,has not been effectively utilized,with a low utilization rate.In this study,the in-situ kinetics and mechanism of siderite during suspension magnetization roasting(SMR)were investigate...Siderite,as an abundant iron ore,has not been effectively utilized,with a low utilization rate.In this study,the in-situ kinetics and mechanism of siderite during suspension magnetization roasting(SMR)were investigated to improve the selective conversion of siderite to magnetite and CO,enriching the theoretical system of green SMR using siderite as a reductant.According to the gas products analyses,the peak value of the reaction rate increased with increasing temperature,and its curves presented the feature of an early peak and long tail.The mechanism function of the siderite pyrolysis was the contraction sphere model(R_(3)):f(α)=3(1−α)2/3;E_(α)was 46.4653 kJ/mol;A was 0.5938 s^(−1);the kinetics equation was k=0.5938exp[−46.4653/(RT)].The in-situ HT-XRD results indicated that siderite was converted into magnetite and wüstite that exhibited a good crystallinity in SMR under a N_(2) atmosphere.At 620℃,the saturation magnetization(M_(s)),remanence magnetization(Mr),and coercivity(Hc)of the product peaked at 53.63×10^(-3)A·m^(2)/g,10.23×10^(-3)A·m^(2)/g,and 12.40×10^(3)A/m,respectively.Meanwhile,the initial particles with a smooth surface were transformed into particles with a porous and loose structure in the roasting process,which would contribute to reducing the grinding cost.展开更多
基金Project(2014CB643405) supported by the National Basic Research Program of ChinaProjects(51204036,51234009) supported by the National Natural Science Foundation of ChinaProject(BJ201604) supported by the Program for Top Young Talents of Higher Education Institutions of Hebei Province,China
文摘The mineralogical phase transformation of a low-grade nickel laterite ore during pre-roasting process and the extraction of silicon during alkaline leaching process were investigated.The results indicate that the reaction activity of nickel ores is effectively improved by pre-roasting at650°C for2h,because of the transformation of lizardite into magnesium olivine and protoenstatite.When finely ground ore samples(44-61μm)pre-roasted firstly react with sodium hydroxide solution(60g/L)with a solid/liquid ratio of1:5at140°C for120min,the extraction of silicon can reach89.89%,and the other valuable elements of magnesium,iron and nickel are accumulated in the solid residues.The leaching kinetics of nickel laterite ore can be described successfully by the diffusion through the product layer control model.The activation energy is calculated to be11.63kJ/mol and the kinetics equation can be expressed as1-3(1-x)2/3+2(1-x)=13.53×10-2exp[-11.63/(RT)]t.
基金Projects(51874071,52022019,51734005)supported by the National Natural Science Foundation of ChinaProject(161045)supported by the Fok Ying Tung Education Foundation for Yong Teachers in the Higher Education Institutions of China。
文摘Siderite,as an abundant iron ore,has not been effectively utilized,with a low utilization rate.In this study,the in-situ kinetics and mechanism of siderite during suspension magnetization roasting(SMR)were investigated to improve the selective conversion of siderite to magnetite and CO,enriching the theoretical system of green SMR using siderite as a reductant.According to the gas products analyses,the peak value of the reaction rate increased with increasing temperature,and its curves presented the feature of an early peak and long tail.The mechanism function of the siderite pyrolysis was the contraction sphere model(R_(3)):f(α)=3(1−α)2/3;E_(α)was 46.4653 kJ/mol;A was 0.5938 s^(−1);the kinetics equation was k=0.5938exp[−46.4653/(RT)].The in-situ HT-XRD results indicated that siderite was converted into magnetite and wüstite that exhibited a good crystallinity in SMR under a N_(2) atmosphere.At 620℃,the saturation magnetization(M_(s)),remanence magnetization(Mr),and coercivity(Hc)of the product peaked at 53.63×10^(-3)A·m^(2)/g,10.23×10^(-3)A·m^(2)/g,and 12.40×10^(3)A/m,respectively.Meanwhile,the initial particles with a smooth surface were transformed into particles with a porous and loose structure in the roasting process,which would contribute to reducing the grinding cost.