We demonstrate the synthesis of C-Cl-codoped titania/attapulgite（TiO2/ATT） composites containing a mixture of TiO2 phases by a facile sol-gel method at 70 ℃ using titanium tetraisopropoxide as the TiO2 precursor an...We demonstrate the synthesis of C-Cl-codoped titania/attapulgite（TiO2/ATT） composites containing a mixture of TiO2 phases by a facile sol-gel method at 70 ℃ using titanium tetraisopropoxide as the TiO2 precursor and ATT as a support for the TiO2 nanoparticles.The photocatalytic activity of the C-Cl-codoped TiO2/ATT composites with mixed anatase/brookite/rutile phases obtained at pH= 3.0 was much higher than that of commercially available Degussa P25 for the photocatalytic degradation of acid red G under visible-light irradiation.The excellent photocatalytic activity of the developed composite originates from the nonmetal codoping,which extends the absorption edge of TiO2 into visible region,and the presence of multiple phases,which slow the recombination of photoexcited electron/hole pairs.The formation of hydroxyl radicals during the photocatalytic degradation process was detected by photoluminescence probing using terephthalic acid.A mechanism for photocatalysis over the C-Cl-codoped TiO2/ATT composites was proposed.展开更多
The natural attapulgite(NAPT)was disaggregated by high-pressure homogenization technology combined with extrusion process to prepare the attapulgite with disaggregated rod crystal bundles(DAPT)and large specific surfa...The natural attapulgite(NAPT)was disaggregated by high-pressure homogenization technology combined with extrusion process to prepare the attapulgite with disaggregated rod crystal bundles(DAPT)and large specific surface area of 133.7 m^(2)/g.NAPT and DAPT were incorporated into the silicone rubber to obtain the composite NAPTSR and DAPT-SR by mechanical blending method,respectively.After thermal oxidative ageing at 300℃ for 0.5 h,temperature for the 5%weight loss increased greatly from 385℃ of the neat silicone rubber to 396-399℃ with addition of NAPT and DAPT.NAPT and DAPT enhanced the interaction between the filler nanoparticles and rubber matrix thus inhibited the nanoparticle agglomeration.The conservation rate of the side methyl group in NAPT-SR and DAPT-SR was greatly improved after ageing.Therefore,the thermal oxidative degradation and ageing performance of the silicone rubber composites was significantly reinforced.Moreover,DAPT could greatly restrain the growth of nanoparticles after ageing.Therefore,DAPT-SR showed the better retention of tensile strength(40.6%),elongation at break(34.9%)and tear strength(30.1%)compared with the corresponding mechanical properties of the neat silicone rubber(10.6%,7.4%,and 5.0%)after ageing.展开更多
Attapulgite clay is a kind of special silicate mineral with high adsorption capacity thanks to its loose structure and porous surface. In this paper, the attapulgite clay was treated effectively with acid under microw...Attapulgite clay is a kind of special silicate mineral with high adsorption capacity thanks to its loose structure and porous surface. In this paper, the attapulgite clay was treated effectively with acid under microwave thermal activation and ultrasonic vibration, respectively, and characterized by XRD, N2 adsorption, FT-IR and SEM. The desulfurization performance of the modified attapulgite clay was then evaluated by using simulated gasoline as the feed. The test results showed that the thiophene removal rate increased with an increasing dosage of hydrochloric acid during microwave modification of attapulgite clay. When the concentration of hydrochloric acid reached 15%, the increase of desulfurization rate became slower, and the desulfurization rate was about 69%.展开更多
[Objective] The paper was to study the dynamic adsorption of microwave modified attapulgite on micro-polluted phenol wastewater. [Method] Cetyl trimethyl ammonium bromide （CATB） modified attapulgite was used to modi...[Objective] The paper was to study the dynamic adsorption of microwave modified attapulgite on micro-polluted phenol wastewater. [Method] Cetyl trimethyl ammonium bromide （CATB） modified attapulgite was used to modify attapulgite, and conducted dynamic test on micro-polluted phenol wastewater. The dynamic charac- teristics of phenol removal were also studied. [Result] Attapulgite modified by CATB has strong adsorption ability on phenol in micro-polluted water, the phenol removal rate increased with the decrease of flow rate of wastewater. When pH value was 6- 8, phenol concentration in wastewater was 17.74 mg/L, flow rate was 2 m/s and ad- sorption time was 25 rain, the removal rate reached 93.07%. The modified atta- pulgite could be regenerated with alkali, and its adsorption ability after regeneration had no obvious decline. The dynamic adsorption process of phenol accorded with the first-order kinetic equation. [Conclusion] The study provided basis for further study on ＂organic matter removal in wastewater.展开更多
基金supported by the National Basic Research Program of China (973 Program, 2007CB613302)the Natural Science Foundation of Hubei Province (2016CFA078)~~
文摘We demonstrate the synthesis of C-Cl-codoped titania/attapulgite（TiO2/ATT） composites containing a mixture of TiO2 phases by a facile sol-gel method at 70 ℃ using titanium tetraisopropoxide as the TiO2 precursor and ATT as a support for the TiO2 nanoparticles.The photocatalytic activity of the C-Cl-codoped TiO2/ATT composites with mixed anatase/brookite/rutile phases obtained at pH= 3.0 was much higher than that of commercially available Degussa P25 for the photocatalytic degradation of acid red G under visible-light irradiation.The excellent photocatalytic activity of the developed composite originates from the nonmetal codoping,which extends the absorption edge of TiO2 into visible region,and the presence of multiple phases,which slow the recombination of photoexcited electron/hole pairs.The formation of hydroxyl radicals during the photocatalytic degradation process was detected by photoluminescence probing using terephthalic acid.A mechanism for photocatalysis over the C-Cl-codoped TiO2/ATT composites was proposed.
基金This research was supported by a grant of the National Natural Science Foundation of China (30600037)by a grant for the con-struction of scientific and technological platforms fromthe Chinese Ministry of Science and Technology (2005DKA21006)+1 种基金by a grant of Shanghai Forest and Garden Bureau (G069901) by the Knowledge Innovation Programof the Chinese Academy of Sciences (KSCX2-YW-Z-061)
基金supported by the Key Special Program on the S&T for the Pollution Control and Treatment of Water Bodies (No.2017ZX07603-003)。
文摘The natural attapulgite(NAPT)was disaggregated by high-pressure homogenization technology combined with extrusion process to prepare the attapulgite with disaggregated rod crystal bundles(DAPT)and large specific surface area of 133.7 m^(2)/g.NAPT and DAPT were incorporated into the silicone rubber to obtain the composite NAPTSR and DAPT-SR by mechanical blending method,respectively.After thermal oxidative ageing at 300℃ for 0.5 h,temperature for the 5%weight loss increased greatly from 385℃ of the neat silicone rubber to 396-399℃ with addition of NAPT and DAPT.NAPT and DAPT enhanced the interaction between the filler nanoparticles and rubber matrix thus inhibited the nanoparticle agglomeration.The conservation rate of the side methyl group in NAPT-SR and DAPT-SR was greatly improved after ageing.Therefore,the thermal oxidative degradation and ageing performance of the silicone rubber composites was significantly reinforced.Moreover,DAPT could greatly restrain the growth of nanoparticles after ageing.Therefore,DAPT-SR showed the better retention of tensile strength(40.6%),elongation at break(34.9%)and tear strength(30.1%)compared with the corresponding mechanical properties of the neat silicone rubber(10.6%,7.4%,and 5.0%)after ageing.
基金supported financially by the National Natural Science Foundation of China (21306162)the National 973 Project of China (2010CB226903)+1 种基金the Natural Science Foundation of the Jiangsu Higher Education Institutions of China (14KJB430023)the Union Innovation Funds-Prospective Joint Research Project of Jiangsu Province (BY2012152)
文摘Attapulgite clay is a kind of special silicate mineral with high adsorption capacity thanks to its loose structure and porous surface. In this paper, the attapulgite clay was treated effectively with acid under microwave thermal activation and ultrasonic vibration, respectively, and characterized by XRD, N2 adsorption, FT-IR and SEM. The desulfurization performance of the modified attapulgite clay was then evaluated by using simulated gasoline as the feed. The test results showed that the thiophene removal rate increased with an increasing dosage of hydrochloric acid during microwave modification of attapulgite clay. When the concentration of hydrochloric acid reached 15%, the increase of desulfurization rate became slower, and the desulfurization rate was about 69%.
基金Supported by Innovation Fund Project of Ministry of Science and Technology(10C26213201183)~~
文摘[Objective] The paper was to study the dynamic adsorption of microwave modified attapulgite on micro-polluted phenol wastewater. [Method] Cetyl trimethyl ammonium bromide （CATB） modified attapulgite was used to modify attapulgite, and conducted dynamic test on micro-polluted phenol wastewater. The dynamic charac- teristics of phenol removal were also studied. [Result] Attapulgite modified by CATB has strong adsorption ability on phenol in micro-polluted water, the phenol removal rate increased with the decrease of flow rate of wastewater. When pH value was 6- 8, phenol concentration in wastewater was 17.74 mg/L, flow rate was 2 m/s and ad- sorption time was 25 rain, the removal rate reached 93.07%. The modified atta- pulgite could be regenerated with alkali, and its adsorption ability after regeneration had no obvious decline. The dynamic adsorption process of phenol accorded with the first-order kinetic equation. [Conclusion] The study provided basis for further study on ＂organic matter removal in wastewater.