The coincidence of relevant factors, e.g. oxygen absorption quantity, weight increment, water soluble iron ions and sulfate ion of sulfide ore samples in the oxidation process, was tested through experiment. Based on ...The coincidence of relevant factors, e.g. oxygen absorption quantity, weight increment, water soluble iron ions and sulfate ion of sulfide ore samples in the oxidation process, was tested through experiment. Based on a large number of tests for a group sample of sulfide ores from a mine, some important conclusions were obtained. The results obtained by the investigation indicate that there is no general interpretation relative to the oxygen absorption and the formation products of sulfate ion and water soluble iron ions during the oxidation process of sulfide ores at ambient temperature. However, the weight increment of the sulfide ore samples in the oxidation process at ambient temperature has a linear relationship with the auantitv of oxvaen absorption.展开更多
Three representative sulfide ore samples were collected from typical metal mines,and their corresponding pre-oxidized products were obtained under nature environment.The thermal behaviors of each sample at heating rat...Three representative sulfide ore samples were collected from typical metal mines,and their corresponding pre-oxidized products were obtained under nature environment.The thermal behaviors of each sample at heating rates of 5,10,15 and 20 °C/min in air flow from ambient temperature to 800 °C were studied by simultaneous thermal analysis and the TG/DSC curves before and after the pre-oxidation were compared.By the peak temperature of DTG curves,the whole reaction process for each sample was divided into different stages,and the apparent activation energies were calculated by the Ozawa-Flynn-Wall method.The results show that the reaction process of each sample after pre-oxidation is more complex,with quicker reaction rates,fewer heat production quantities,and higher or lower ignition-points.The apparent activation energies decrease from 364.017-474.228 kJ/mol to 244.523- 333.161 kJ/mol.Therefore,sulfide ores are more susceptible to spontaneous combustion after the pre-oxidation.展开更多
文摘The coincidence of relevant factors, e.g. oxygen absorption quantity, weight increment, water soluble iron ions and sulfate ion of sulfide ore samples in the oxidation process, was tested through experiment. Based on a large number of tests for a group sample of sulfide ores from a mine, some important conclusions were obtained. The results obtained by the investigation indicate that there is no general interpretation relative to the oxygen absorption and the formation products of sulfate ion and water soluble iron ions during the oxidation process of sulfide ores at ambient temperature. However, the weight increment of the sulfide ore samples in the oxidation process at ambient temperature has a linear relationship with the auantitv of oxvaen absorption.
基金Project(51304051)supported by the National Natural Science Foundation of ChinaProject(2012J05088)supported by the Natural Science Foundation of Fujian Province,China+1 种基金Project(022409)supported by School Talent Award of Fuzhou University,ChinaProject(2013-XQ-18)supported by Science&Technology Development Foundation of Fuzhou University,China
文摘Three representative sulfide ore samples were collected from typical metal mines,and their corresponding pre-oxidized products were obtained under nature environment.The thermal behaviors of each sample at heating rates of 5,10,15 and 20 °C/min in air flow from ambient temperature to 800 °C were studied by simultaneous thermal analysis and the TG/DSC curves before and after the pre-oxidation were compared.By the peak temperature of DTG curves,the whole reaction process for each sample was divided into different stages,and the apparent activation energies were calculated by the Ozawa-Flynn-Wall method.The results show that the reaction process of each sample after pre-oxidation is more complex,with quicker reaction rates,fewer heat production quantities,and higher or lower ignition-points.The apparent activation energies decrease from 364.017-474.228 kJ/mol to 244.523- 333.161 kJ/mol.Therefore,sulfide ores are more susceptible to spontaneous combustion after the pre-oxidation.