The effect of friction stir processing(FSP)at different rotation speeds(400,630,800,and 1000 r/min)and traverse speeds(25 and 50 mm/min)on the tribological properties of a Si particle reinforced Zn−40Al−2Cu-based in-s...The effect of friction stir processing(FSP)at different rotation speeds(400,630,800,and 1000 r/min)and traverse speeds(25 and 50 mm/min)on the tribological properties of a Si particle reinforced Zn−40Al−2Cu-based in-situ composite was investigated.After preliminary optimization,800 r/min and 25 mm/min were selected as optimum FSP parameters.According to the results,multi-pass FSP improved the tribological properties.For instance,at an applied pressure of 0.75 MPa,the wear rate and average coefficient of friction(COF)of four-pass FSPed composite were lower than those of base composite by 53%and 50%,respectively.SEM examinations of worn surfaces,wear debris,and worn subsurfaces revealed that the intensive refinement and uniform distribution of microstructural phases,especially the coarse Si particles,reduced Si particles interspacing,and elimination of casting defects were the most important factors enhancing the substrate resistance against sliding-induced deformation.This led to the formation of stable tribolayers that improved the tribological properties.展开更多
In-situ 2 vol.%TiB2 particle reinforced Al−xSi−0.3Mg(x=7,9,12,15 wt.%)composites were prepared by the salt−metal reaction,and the microstructures and mechanical properties were investigated.The results show that the T...In-situ 2 vol.%TiB2 particle reinforced Al−xSi−0.3Mg(x=7,9,12,15 wt.%)composites were prepared by the salt−metal reaction,and the microstructures and mechanical properties were investigated.The results show that the TiB2 particles with a diameter of 20−80 nm and the eutectic Si with a length of 1−10μm are the main strengthening phases in the TiB2/Al−xSi−0.3Mg composites.The TiB2 particles promote grain refinement and modify the eutectic Si from needle-like to short-rod shape.However,the strengthening effect of TiB2 particles is weakened as the Si content exceeds the eutectic composition,which can be attributed to the formation of large and irregular primary Si.The axial tensile test results and fractography observations indicate that these composites show more brittle fracture characteristics than the corresponding alloy matrixes.展开更多
The corrosion, corrosive wear and dry sliding wear of nanocomposites, are extremely complicated and involve various chemical, physical anbd mechanical factors. The aim of this work is to investigate the effects of nan...The corrosion, corrosive wear and dry sliding wear of nanocomposites, are extremely complicated and involve various chemical, physical anbd mechanical factors. The aim of this work is to investigate the effects of nanosized SiC content on the hardness, dry sliding wear, corrosion and corrosive wear of Al/SiC nanocomposites synthesized by mechanical milling cold pressing and hot extrusion. The corrosion resistance of these composites in 3%NaCl solution was investigated by electrochemical polarization testing and their dry sliding as well as corrosive wear resistance in the same solution was evaluated using a pin-on-disc tester. The microstructures of the samples and their worn surfaces were examined using scanning electron microscopy. It was shown that the dry sliding wear and corrosion resistance of these nanocomposites were improved with the increase of SiC content. It was concluded that due to the lubrication effect of the solution, both the friction coefficient and frictional heat that might soften the material were reduced. In addition, the improved strength of the nanocomposites combined with their better corrosion resistance contributed to their increased corrosive wear resistance, compared with the base alloy. The prominent wear mechanism in the unreinforced alloy was adhesive wear, in the Al/SiC nanocomposites, the wear mechanism changed to abrasive.展开更多
文摘The effect of friction stir processing(FSP)at different rotation speeds(400,630,800,and 1000 r/min)and traverse speeds(25 and 50 mm/min)on the tribological properties of a Si particle reinforced Zn−40Al−2Cu-based in-situ composite was investigated.After preliminary optimization,800 r/min and 25 mm/min were selected as optimum FSP parameters.According to the results,multi-pass FSP improved the tribological properties.For instance,at an applied pressure of 0.75 MPa,the wear rate and average coefficient of friction(COF)of four-pass FSPed composite were lower than those of base composite by 53%and 50%,respectively.SEM examinations of worn surfaces,wear debris,and worn subsurfaces revealed that the intensive refinement and uniform distribution of microstructural phases,especially the coarse Si particles,reduced Si particles interspacing,and elimination of casting defects were the most important factors enhancing the substrate resistance against sliding-induced deformation.This led to the formation of stable tribolayers that improved the tribological properties.
基金The authors are grateful for the financial supports from the National Natural Science Foundation of China(51804349)the China Postdoctoral Science Foundation(2018M632986)the Natural Science Foundation of Hunan Province,China(2019JJ50766).
文摘In-situ 2 vol.%TiB2 particle reinforced Al−xSi−0.3Mg(x=7,9,12,15 wt.%)composites were prepared by the salt−metal reaction,and the microstructures and mechanical properties were investigated.The results show that the TiB2 particles with a diameter of 20−80 nm and the eutectic Si with a length of 1−10μm are the main strengthening phases in the TiB2/Al−xSi−0.3Mg composites.The TiB2 particles promote grain refinement and modify the eutectic Si from needle-like to short-rod shape.However,the strengthening effect of TiB2 particles is weakened as the Si content exceeds the eutectic composition,which can be attributed to the formation of large and irregular primary Si.The axial tensile test results and fractography observations indicate that these composites show more brittle fracture characteristics than the corresponding alloy matrixes.
基金Iranian Nanotechnology Initiative (INI) for finical support of the research work
文摘The corrosion, corrosive wear and dry sliding wear of nanocomposites, are extremely complicated and involve various chemical, physical anbd mechanical factors. The aim of this work is to investigate the effects of nanosized SiC content on the hardness, dry sliding wear, corrosion and corrosive wear of Al/SiC nanocomposites synthesized by mechanical milling cold pressing and hot extrusion. The corrosion resistance of these composites in 3%NaCl solution was investigated by electrochemical polarization testing and their dry sliding as well as corrosive wear resistance in the same solution was evaluated using a pin-on-disc tester. The microstructures of the samples and their worn surfaces were examined using scanning electron microscopy. It was shown that the dry sliding wear and corrosion resistance of these nanocomposites were improved with the increase of SiC content. It was concluded that due to the lubrication effect of the solution, both the friction coefficient and frictional heat that might soften the material were reduced. In addition, the improved strength of the nanocomposites combined with their better corrosion resistance contributed to their increased corrosive wear resistance, compared with the base alloy. The prominent wear mechanism in the unreinforced alloy was adhesive wear, in the Al/SiC nanocomposites, the wear mechanism changed to abrasive.