The special experimental device and sulfuric acid electrolyte were adopted to study the influence of anodic oxidation heat on hard anodic film for 2024 aluminum alloy. Compared with the oxidation heat transferred to t...The special experimental device and sulfuric acid electrolyte were adopted to study the influence of anodic oxidation heat on hard anodic film for 2024 aluminum alloy. Compared with the oxidation heat transferred to the electrolyte through anodic film, the heat transferred to the coolant through aluminum substrate is more beneficial to the growth of anodic film. The film forming speed, film thickness, density and hardness are significantly increased as the degree of undercooling of the coolant increases. The degree of undercooling of the coolant, which is necessary for the growth of anodic film, is related to the degree of undercooling of the electrolyte, thickness of aluminum substrate, thickness of anodic film, natural parameters of bubble covering and current density. The microstructure and performance of the oxidation film could be controlled by the temperature of the coolant.展开更多
Sodium-ion batteries are considered as a promising candidate for lithium-ion batteries due to abundant sodium resources and similar intercalation chemistry.Hard carbon derived from biomass with the virtue of abundance...Sodium-ion batteries are considered as a promising candidate for lithium-ion batteries due to abundant sodium resources and similar intercalation chemistry.Hard carbon derived from biomass with the virtue of abundance and renewability is a cost-effective anode material.Herein,hard carbon is derived from renewable bagasse through a simple two-step method combining mechanical ball milling with carbonization.The hard carbon electrodes exhibit superior electrochemical performance with a high reversible capacity of 315 mA∙h/g.Furthermore,the initial capacity of the full cell,HC//NaMn0.4Ni0.4Ti0.1Mg0.1O2,is 253 mA∙h/g and its capacity retention rate is 77%after 80 cycles,which further verifies its practical application.The simple and low-cost preparation process,as well as excellent electrochemical properties,demonstrates that hard carbon derived from bagasse is a promising anode for sodium-ion batteries.展开更多
基金Project (SBZDPY-11-17) supported by the Fund on Key Laboratory Project for Hydrodynamic Force, Ministry of Education, China Project (SZD0502-09-0) supported by Key Disciplines of Materials Processing Engineering of Sichuan Province, China
文摘The special experimental device and sulfuric acid electrolyte were adopted to study the influence of anodic oxidation heat on hard anodic film for 2024 aluminum alloy. Compared with the oxidation heat transferred to the electrolyte through anodic film, the heat transferred to the coolant through aluminum substrate is more beneficial to the growth of anodic film. The film forming speed, film thickness, density and hardness are significantly increased as the degree of undercooling of the coolant increases. The degree of undercooling of the coolant, which is necessary for the growth of anodic film, is related to the degree of undercooling of the electrolyte, thickness of aluminum substrate, thickness of anodic film, natural parameters of bubble covering and current density. The microstructure and performance of the oxidation film could be controlled by the temperature of the coolant.
基金Projects(51661009,51761007)supported by the National Natural Science Foundation of China,Projects(2019GXNSFDA245014,2016GXNSFGA380001)supported by the Natural Science Foundation of Guangxi Province,China,Projects(2019AC20164,2019AC20053)supported by the Science and Technology Base and Talent Special Project of Guangxi Province,China。
文摘Sodium-ion batteries are considered as a promising candidate for lithium-ion batteries due to abundant sodium resources and similar intercalation chemistry.Hard carbon derived from biomass with the virtue of abundance and renewability is a cost-effective anode material.Herein,hard carbon is derived from renewable bagasse through a simple two-step method combining mechanical ball milling with carbonization.The hard carbon electrodes exhibit superior electrochemical performance with a high reversible capacity of 315 mA∙h/g.Furthermore,the initial capacity of the full cell,HC//NaMn0.4Ni0.4Ti0.1Mg0.1O2,is 253 mA∙h/g and its capacity retention rate is 77%after 80 cycles,which further verifies its practical application.The simple and low-cost preparation process,as well as excellent electrochemical properties,demonstrates that hard carbon derived from bagasse is a promising anode for sodium-ion batteries.