Using a closed field unbalanced magnetron sputtering system,the cemented carbide end mills were coated with a CrTiAlN hard coating,which consisted of a Cr adhesive layer,a CrN interlayer and a CrTiAlN top layer.The mi...Using a closed field unbalanced magnetron sputtering system,the cemented carbide end mills were coated with a CrTiAlN hard coating,which consisted of a Cr adhesive layer,a CrN interlayer and a CrTiAlN top layer.The microstructure and mechanical properties of the coating were investigated by X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM),micro indentation and scratch test.The cutting performance of the coated end mills were conducted by high-speed dry milling hardened steel(P20,HRC 45).The results indicates that the coating is composed of(Cr,Ti,Al)N columnar grains with nanolayers.The coating exhibits good adhesion to cemented carbide substrate and high microhardness of around 30 GPa.The coated end mills show significant improvement on tool life and much lower cutting force as compared to the uncoated ones.And the related mechanisms were discussed.展开更多
基金Projects (500120069,U1201245) supported by the National Natural Science Foundation of ChinaProject (2011J2200036) supported by Guangzhou Scientific and Technological Planning Project,ChinaProject supported by Guangdong Province Universities and Colleges Pearl River Scholar Funded Scheme(2012),China
文摘Using a closed field unbalanced magnetron sputtering system,the cemented carbide end mills were coated with a CrTiAlN hard coating,which consisted of a Cr adhesive layer,a CrN interlayer and a CrTiAlN top layer.The microstructure and mechanical properties of the coating were investigated by X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM),micro indentation and scratch test.The cutting performance of the coated end mills were conducted by high-speed dry milling hardened steel(P20,HRC 45).The results indicates that the coating is composed of(Cr,Ti,Al)N columnar grains with nanolayers.The coating exhibits good adhesion to cemented carbide substrate and high microhardness of around 30 GPa.The coated end mills show significant improvement on tool life and much lower cutting force as compared to the uncoated ones.And the related mechanisms were discussed.