The dissolution of molybdenite concentrate in NaC1 electrolyte was investigated. The results show that the dissolution rate increases with the increase in liquid-to-solid ratio, stirring speed, NaCl concentration and ...The dissolution of molybdenite concentrate in NaC1 electrolyte was investigated. The results show that the dissolution rate increases with the increase in liquid-to-solid ratio, stirring speed, NaCl concentration and temperature. When the liquid-to-solid ratio is 30：1, stirring speed is 400 r/min, concentration of NaCI is 4 mol/L at pH=9 and room temperature, the leaching efficiency of molybdenite concentrate will reach 99.5% in 240 min. Molybdenite concentrate cannot be electro-oxidized directly on the anode. The kinetic studies show that the dissolution of molybdenite concentrate is represented by shrinking core model with diffusion through a porous product layer of element sulfur, and the apparent activation energy for the dissolution reaction is 8.56 kJ/mol.展开更多
基金Project(2007BAB22B01) supported by the 11th Five-Year Plan of National Science and Technology of China Project(50704036) supported by the National Natural Science Foundation of China
文摘The dissolution of molybdenite concentrate in NaC1 electrolyte was investigated. The results show that the dissolution rate increases with the increase in liquid-to-solid ratio, stirring speed, NaCl concentration and temperature. When the liquid-to-solid ratio is 30：1, stirring speed is 400 r/min, concentration of NaCI is 4 mol/L at pH=9 and room temperature, the leaching efficiency of molybdenite concentrate will reach 99.5% in 240 min. Molybdenite concentrate cannot be electro-oxidized directly on the anode. The kinetic studies show that the dissolution of molybdenite concentrate is represented by shrinking core model with diffusion through a porous product layer of element sulfur, and the apparent activation energy for the dissolution reaction is 8.56 kJ/mol.