Three types of SiC fibers with different tensile strength were employed to prepare unidirectional titanium matrix composites. The strengths of the original SiC fibers and extracted fibers from the composites were meas...Three types of SiC fibers with different tensile strength were employed to prepare unidirectional titanium matrix composites. The strengths of the original SiC fibers and extracted fibers from the composites were measured. The results show that the mechanical properties of fibers are greatly damaged by the consolidation processing of the composite. The strength data of the extracted fibers are used to predict the strength of the composites according to two theoretic models. The Globe Load-Sharing(GLS) model overestimates the strength of the composites. If the Local Load-Sharing(LLS) model assumes that failure occurs after the formation of a cluster with three broken fibers, the model can predict the strength of the composites exactly.展开更多
Continuous SiC(OAl) fibers, named KD-A fibers, were prepared by the melt-spinning of ceramic precursor polyaluminocarbosilane, air-curing, and pyrolizing at 1 300 ℃. These fibers contained small amount of aluminum an...Continuous SiC(OAl) fibers, named KD-A fibers, were prepared by the melt-spinning of ceramic precursor polyaluminocarbosilane, air-curing, and pyrolizing at 1 300 ℃. These fibers contained small amount of aluminum and 7%- 9% oxygen. The KD-A fibers were converted into sintered SiC(Al) fibers, named KD-SA, by sintering at 1 800 ℃. The fibers were characterized by chemical analysis, tensile strength test, SEM and XRD. The tensile strength, elastic modulus and diameter of the KD-A fibers are 2.6 GPa, 210 GPa, 12 - 14 μm, respectively. The KD-A fibers have higher thermal stability, more excellent oxidation resistance than the Nicalon fibers. The properties of the KD-A fibers have reached the level of Hi-Nicalon fibers. The tensile strength, elastic modulus and diameter of the KD-A fibers are 2.1 GPa, 405 GPa, 10 - 12 μm, respectively. The KD-SA fibers with nearly stoichiometric component have stable performance at high temperature, and better creep resistance than the Tyranno SA fibers.展开更多
Air-curing is usually applied to the polymer-derived SiC fibers and, as a result, oxygen is embedded to the material. An effective relationship between oxygen content of the SiC fibers and mass gain of their precursor...Air-curing is usually applied to the polymer-derived SiC fibers and, as a result, oxygen is embedded to the material. An effective relationship between oxygen content of the SiC fibers and mass gain of their precursor fibers was established. Results also showed that oxygen content has a great influence on the mechanical properties and excellent tensile strength is usually obtained at the oxygen content of 12%～13%, similar to the density of SiC fibers. Oxygen content has a positive effect on the ceramic yield, and thus, is good to the density and tensile strength; while, oxygen content is also negative to volume content of SiC phase and crystallization of the SiC fibers, and thus, detrimental to the density and tensile strength. Both of the two effects result in the peak behavior of the tensile strength of SiC fibers.展开更多
基金Project(50371069) supported by the National Natural Science Foundation of Chinaproject(2006B20) supported by the Doctoral Innovation Foundation of Northwestern Polytechnical University, China
文摘Three types of SiC fibers with different tensile strength were employed to prepare unidirectional titanium matrix composites. The strengths of the original SiC fibers and extracted fibers from the composites were measured. The results show that the mechanical properties of fibers are greatly damaged by the consolidation processing of the composite. The strength data of the extracted fibers are used to predict the strength of the composites according to two theoretic models. The Globe Load-Sharing(GLS) model overestimates the strength of the composites. If the Local Load-Sharing(LLS) model assumes that failure occurs after the formation of a cluster with three broken fibers, the model can predict the strength of the composites exactly.
文摘Continuous SiC(OAl) fibers, named KD-A fibers, were prepared by the melt-spinning of ceramic precursor polyaluminocarbosilane, air-curing, and pyrolizing at 1 300 ℃. These fibers contained small amount of aluminum and 7%- 9% oxygen. The KD-A fibers were converted into sintered SiC(Al) fibers, named KD-SA, by sintering at 1 800 ℃. The fibers were characterized by chemical analysis, tensile strength test, SEM and XRD. The tensile strength, elastic modulus and diameter of the KD-A fibers are 2.6 GPa, 210 GPa, 12 - 14 μm, respectively. The KD-A fibers have higher thermal stability, more excellent oxidation resistance than the Nicalon fibers. The properties of the KD-A fibers have reached the level of Hi-Nicalon fibers. The tensile strength, elastic modulus and diameter of the KD-A fibers are 2.1 GPa, 405 GPa, 10 - 12 μm, respectively. The KD-SA fibers with nearly stoichiometric component have stable performance at high temperature, and better creep resistance than the Tyranno SA fibers.
文摘Air-curing is usually applied to the polymer-derived SiC fibers and, as a result, oxygen is embedded to the material. An effective relationship between oxygen content of the SiC fibers and mass gain of their precursor fibers was established. Results also showed that oxygen content has a great influence on the mechanical properties and excellent tensile strength is usually obtained at the oxygen content of 12%～13%, similar to the density of SiC fibers. Oxygen content has a positive effect on the ceramic yield, and thus, is good to the density and tensile strength; while, oxygen content is also negative to volume content of SiC phase and crystallization of the SiC fibers, and thus, detrimental to the density and tensile strength. Both of the two effects result in the peak behavior of the tensile strength of SiC fibers.