Ni-CNT (carbon nanotube) composite coatings were processed by electrodeposition and their hardness and corrosion characteristics were investigated with variations of CNT concentration in an electrolyte solution and el...Ni-CNT (carbon nanotube) composite coatings were processed by electrodeposition and their hardness and corrosion characteristics were investigated with variations of CNT concentration in an electrolyte solution and electrodeposition current density. With increasing the CNT concentration in the electrodeposition bath and the current density, more CNTs are incorporated into Ni matrix. Hardness values of the Ni-CNT coatings are irrelevant to the CNT concentration in the solution, the current density, and current mode, implying poor adhesion of CNTs to Ni matrix. With increasing the CNT content in the coating, the corrosion resistance of the Ni-CNT composite coating becomes inferior due to the porous microstructure.展开更多
Titania coating of multi wall carbon nano tube(MWCNT) was carried out by sol-gel method in order to improve its photo catalytic properties.The effect of MWCNT/TiO_2 mass to volume ratio on adsorption ability,reaction ...Titania coating of multi wall carbon nano tube(MWCNT) was carried out by sol-gel method in order to improve its photo catalytic properties.The effect of MWCNT/TiO_2 mass to volume ratio on adsorption ability,reaction rate and photo-catalytic removal efficiency of dibenzothiophene(DBT) from n-hexane solution was investigated using a 9 W UV lamp.The results show that the addition of nanotubes improves the photo-catalytic properties of TiO_2 by two factors;however,the DBT removal rate versus MWCNT content is found to follow a bimodal pattern.Two factors are observed to affect the removal rate of DBT and produce two optimum values for MWCNT content.First,large quantities of MWCNTs prevent light absorption by the solution and decrease removal efficiency.By contrast,a low dosage of MWCNT causes recombination of the electron holes,which also decreases the DBT removal rate.The optimum MWCNT contents in the composite are found to be 0.25 g and 0.75 g MWCNT per 80 m L of sol.展开更多
基金supported by the Center for Electronic Packaging Materials of Korea Science Engineering Foundation
文摘Ni-CNT (carbon nanotube) composite coatings were processed by electrodeposition and their hardness and corrosion characteristics were investigated with variations of CNT concentration in an electrolyte solution and electrodeposition current density. With increasing the CNT concentration in the electrodeposition bath and the current density, more CNTs are incorporated into Ni matrix. Hardness values of the Ni-CNT coatings are irrelevant to the CNT concentration in the solution, the current density, and current mode, implying poor adhesion of CNTs to Ni matrix. With increasing the CNT content in the coating, the corrosion resistance of the Ni-CNT composite coating becomes inferior due to the porous microstructure.
文摘Titania coating of multi wall carbon nano tube(MWCNT) was carried out by sol-gel method in order to improve its photo catalytic properties.The effect of MWCNT/TiO_2 mass to volume ratio on adsorption ability,reaction rate and photo-catalytic removal efficiency of dibenzothiophene(DBT) from n-hexane solution was investigated using a 9 W UV lamp.The results show that the addition of nanotubes improves the photo-catalytic properties of TiO_2 by two factors;however,the DBT removal rate versus MWCNT content is found to follow a bimodal pattern.Two factors are observed to affect the removal rate of DBT and produce two optimum values for MWCNT content.First,large quantities of MWCNTs prevent light absorption by the solution and decrease removal efficiency.By contrast,a low dosage of MWCNT causes recombination of the electron holes,which also decreases the DBT removal rate.The optimum MWCNT contents in the composite are found to be 0.25 g and 0.75 g MWCNT per 80 m L of sol.