The 0.4 nm molecular sieve supported Cu-Ni bimetal catalysts for direct synthesis of dimethyl carbonate (DMC) from CO 2 and CH 3 OH were prepared and investigated. The synthesized catalysts were fully characterized by...The 0.4 nm molecular sieve supported Cu-Ni bimetal catalysts for direct synthesis of dimethyl carbonate (DMC) from CO 2 and CH 3 OH were prepared and investigated. The synthesized catalysts were fully characterized by BET, XRD (X-ray diffraction), TPR (temperature programmed reduction), IR (infra-red adsorption), NH 3-TPD (temperature programmed desorption) and CO 2-TPD (temperature programmed desorption) techniques. The results showed that the surface area of catalysts decreased with increasing metal content, and the metals as well as Cu-Ni alloy co-existed on the reduced catalyst surface. There existed interaction between metal and carrier, and moreover, metal particles affected obviously the acidity and basicity of carrier. The large amount of basic sites facilitated the activation of methanol to methoxyl species and their subsequent reaction with activated carbon dioxide. The catalysts were evaluated in a continuous tubular fixed-bed micro-gaseous reactor and the catalyst with bimetal loading of 20% (by mass) had best catalytic activities. Under the conditions of 393 K, 1.1 MPa, 5 h and gas space velocity of 510 h 1 , the selectivity and yield of DMC were higher than 86.0 % and 5.0 %, respectively.展开更多
The efficient synthesis of dimethylhexane-1,6-dicarbamate(HDC)from 1,6-hexanediamine(HDA)and methyl carbonate over a series of heterogeneous catalysts(e.g.,Mg O,Fe2O3,Mo2O3,and Ce O2)was investigated.The reaction path...The efficient synthesis of dimethylhexane-1,6-dicarbamate(HDC)from 1,6-hexanediamine(HDA)and methyl carbonate over a series of heterogeneous catalysts(e.g.,Mg O,Fe2O3,Mo2O3,and Ce O2)was investigated.The reaction pathway was confirmed as an alcoholysis reaction through a series of designed experiments.Under optimized conditions,100%HDA conversion with 83.1%HDCtotaland 16.9%polyurea was obtained using a onestep with high temperature procedure with Ce O2as the catalyst.A new two-step with variable temperature technology was developed based on the reaction pathway to reduce the polyurea yield.Using the proposed method,the HDCtotalyield reached 95.2%,whereas the polyurea yield decreased to 4.8%.The Ce O2catalyst showed high stability and did not exhibit any observable decrease in the HDC yield or any structural changes after four recycling periods.展开更多
基金Supported by the National High Technology Research and Development Program of China (2008AA03Z3472294,2009AA302410)the Guangdong Province Universities and Colleges Pearl River Scholar Funded Scheme (2010)+1 种基金the Guangdong Province Sci & Tech Bureau (2006B12401006, 2008A080800024)the Chinese Universities Basic Research Founding
文摘The 0.4 nm molecular sieve supported Cu-Ni bimetal catalysts for direct synthesis of dimethyl carbonate (DMC) from CO 2 and CH 3 OH were prepared and investigated. The synthesized catalysts were fully characterized by BET, XRD (X-ray diffraction), TPR (temperature programmed reduction), IR (infra-red adsorption), NH 3-TPD (temperature programmed desorption) and CO 2-TPD (temperature programmed desorption) techniques. The results showed that the surface area of catalysts decreased with increasing metal content, and the metals as well as Cu-Ni alloy co-existed on the reduced catalyst surface. There existed interaction between metal and carrier, and moreover, metal particles affected obviously the acidity and basicity of carrier. The large amount of basic sites facilitated the activation of methanol to methoxyl species and their subsequent reaction with activated carbon dioxide. The catalysts were evaluated in a continuous tubular fixed-bed micro-gaseous reactor and the catalyst with bimetal loading of 20% (by mass) had best catalytic activities. Under the conditions of 393 K, 1.1 MPa, 5 h and gas space velocity of 510 h 1 , the selectivity and yield of DMC were higher than 86.0 % and 5.0 %, respectively.
基金Supported by the Science and Technology Ministry of China(2013BAC11B03)National Nature Science Foundation of China(21476244,21206180,21406245)
文摘The efficient synthesis of dimethylhexane-1,6-dicarbamate(HDC)from 1,6-hexanediamine(HDA)and methyl carbonate over a series of heterogeneous catalysts(e.g.,Mg O,Fe2O3,Mo2O3,and Ce O2)was investigated.The reaction pathway was confirmed as an alcoholysis reaction through a series of designed experiments.Under optimized conditions,100%HDA conversion with 83.1%HDCtotaland 16.9%polyurea was obtained using a onestep with high temperature procedure with Ce O2as the catalyst.A new two-step with variable temperature technology was developed based on the reaction pathway to reduce the polyurea yield.Using the proposed method,the HDCtotalyield reached 95.2%,whereas the polyurea yield decreased to 4.8%.The Ce O2catalyst showed high stability and did not exhibit any observable decrease in the HDC yield or any structural changes after four recycling periods.