The effects of the Cr3C2 content and wheel speed on the amorphization behavior of the melt-spun SmCo7-x（Cr3C2）x （x=0.10-0.25） alloys were studied systematically by X-ray diffraction analysis （XRD）, differential ...The effects of the Cr3C2 content and wheel speed on the amorphization behavior of the melt-spun SmCo7-x（Cr3C2）x （x=0.10-0.25） alloys were studied systematically by X-ray diffraction analysis （XRD）, differential scanning calorimetry （DSC） and magnetic measurements. The ribbon melt-spun at lower wheel speed （20 m/s） has composite structure composed of mostly SmCo7 and a small amount of Sm2Co17R. The grain size of SmCo7 phase decreases with the increase of Cr3C2 content. With the increase of wheel speed, the XRD peaks become lower and accompanied with a broad increase in backgrounds, indicating a considerable decrease in the grain size of the SmCo7 phase. When the wheel speed increases to 40 m/s, SmCo7-x（Cr3C2）x alloys can be obtained in the amorphous state for 0.15≤x≤0.25 with intrinsic coercive Hci of 0.004-0.007 T. The DSC analysis reveals that SmCo7 phase firstly precipitates from the amorphous matrix at 650 °C, followed by the crystallization of Sm2Co17 phase at 770 °C.展开更多
The electrocaloric effect(ECE) of multilayer ceramic capacitor(MLCC) of Y5 V type was directly measured via a differential scanning calorimetry(DSC) method and a reference resistor was used to calibrate the heat flow ...The electrocaloric effect(ECE) of multilayer ceramic capacitor(MLCC) of Y5 V type was directly measured via a differential scanning calorimetry(DSC) method and a reference resistor was used to calibrate the heat flow due to the heat dissipation. The results are compared with those calculated from Maxwell relations by using the polarization data obtained from the polarization–electric field hysteresis loops. The direct method shows a larger ECE temperature change, which is accounted for the situation approaches an ideal condition. For the indirect method using Maxwell relations, only the polarization projection along the electric field was taken into account, which will be less than the randomly distributed real polarizations that contribute to the ECE. The MLCCs exhibit a broad peak of ECE around 80 C, which will be favorite for the practical ECE cooling devices.展开更多
基金Project (51104188) supported by the National Natural Science Foundation for Young Scholars of China
文摘The effects of the Cr3C2 content and wheel speed on the amorphization behavior of the melt-spun SmCo7-x（Cr3C2）x （x=0.10-0.25） alloys were studied systematically by X-ray diffraction analysis （XRD）, differential scanning calorimetry （DSC） and magnetic measurements. The ribbon melt-spun at lower wheel speed （20 m/s） has composite structure composed of mostly SmCo7 and a small amount of Sm2Co17R. The grain size of SmCo7 phase decreases with the increase of Cr3C2 content. With the increase of wheel speed, the XRD peaks become lower and accompanied with a broad increase in backgrounds, indicating a considerable decrease in the grain size of the SmCo7 phase. When the wheel speed increases to 40 m/s, SmCo7-x（Cr3C2）x alloys can be obtained in the amorphous state for 0.15≤x≤0.25 with intrinsic coercive Hci of 0.004-0.007 T. The DSC analysis reveals that SmCo7 phase firstly precipitates from the amorphous matrix at 650 °C, followed by the crystallization of Sm2Co17 phase at 770 °C.
基金supported by the National Natural Science Foundation of China(Grant No.51372042)the Department of Education of Guangdong Province of People’s Republic of China(Grant No.2014GKXM039)+1 种基金Guangdong Provincial Natural Science Foundation(Grant No.2015A030308004)the NSFC-Guangdong Joint Fund(Grant NoU1501246)
文摘The electrocaloric effect(ECE) of multilayer ceramic capacitor(MLCC) of Y5 V type was directly measured via a differential scanning calorimetry(DSC) method and a reference resistor was used to calibrate the heat flow due to the heat dissipation. The results are compared with those calculated from Maxwell relations by using the polarization data obtained from the polarization–electric field hysteresis loops. The direct method shows a larger ECE temperature change, which is accounted for the situation approaches an ideal condition. For the indirect method using Maxwell relations, only the polarization projection along the electric field was taken into account, which will be less than the randomly distributed real polarizations that contribute to the ECE. The MLCCs exhibit a broad peak of ECE around 80 C, which will be favorite for the practical ECE cooling devices.