CoNiFe,CoNiFeB and CoNiFeP soft magnetic thin films were prepared by cyclic voltammetry method.The morphologies,composition and structures were characterized by scanning electron microscope（SEM）,energy-dispersive X-...CoNiFe,CoNiFeB and CoNiFeP soft magnetic thin films were prepared by cyclic voltammetry method.The morphologies,composition and structures were characterized by scanning electron microscope（SEM）,energy-dispersive X-ray spectroscope（EDS） and X-ray diffractometer（XRD）.The soft magnetic properties were investigated through vibrating sample magnetometer（VSM）.The corrosion resistance was investigated through Tafel polarization and electrochemical impedance spectroscopic（EIS）.The results show that all the electrodeposited CoNiFe,CoNiFeB and CoNiFeP films are mixtures of crystalline and amorphous phases,and high amount of boron/phosphorus-containing additives favors the formation of amorphous state.Nanostructure is obtained in CoNiFe and CoNiFeB films.The inclusion of boron causes the film more dense and also increases its corrosion resistance.Meanwhile,the inclusion of boron lowers its coercivity（Hc） from 851.48 A/m to 604.79 A/m,but the saturation magnetic flux density（Bs） is almost unchanged.However,the addition of phosphorus greatly increases the film particle size and decreases its corrosion stability.The coercivity（Hc） of CoNiFeP film is also highly increased to 12485.79 A/m,and its saturation magnetic flux density（Bs） is greatly decreased to 1.25 T.展开更多
Nanocrystalline NdFeB film was fabricated onto the copper substrate through direct current electroplating method,and characterized by scanning electron microscope(SEM) coupled with energy dispersive X-ray spectroscope...Nanocrystalline NdFeB film was fabricated onto the copper substrate through direct current electroplating method,and characterized by scanning electron microscope(SEM) coupled with energy dispersive X-ray spectroscope(EDS),vibrating sample magnetometer and potentiodynamic polarization techniques.The initial electroplating behavior was investigated by cyclic voltammetry(CV) and electrochemical impedance spectroscopy(EIS) techniques.Results revealed that the corrosion resistance of the NdFeB film was better than that of the traditional sintered NdFeB magnet.The depositing process of the NdFeB film followed the three-dimensional nucleation and subsequent grain growth mechanism,and was controlled by charger transfer.With the increase of the negative potential bias,the deposition mechanism of NdFeB film changed from heterogeneous to homogeneous nucleation/growth,which consequently resulted in the decrease of charge-transfer-resistance.展开更多
Thickness effects of thin La0.7Sr0.3MnO3 （LSMO） films on （LaAlOa）0.3（Sr2AlTaO6）0.7 substrates were examined by a slow positron beam technique. Doppler-broadening line shape parameter S was measured as a function...Thickness effects of thin La0.7Sr0.3MnO3 （LSMO） films on （LaAlOa）0.3（Sr2AlTaO6）0.7 substrates were examined by a slow positron beam technique. Doppler-broadening line shape parameter S was measured as a function of thickness and differnt annealing conditions. Results reveal there could be more than one mechanism to induce vacancy-like defects. It was found that strain-induced defects mainly influence the S value of the in situ oxygenambience annealing LSMO thin films and the strain could vanish still faster along with the increase of thickness, and the oxygen-deficient induced defects mainly affect the S value of post-annealing LSMO films.展开更多
CoFe204/Pb（Zr0.53Ti0.47）O3 （CFO/PZT） magnetoelectric composite thin films of 2-2 type structure had been prepared onto Pt/Ti/SiO2/Si substrate by a sol-gel process and spin coat- ing technique. The structure of th...CoFe204/Pb（Zr0.53Ti0.47）O3 （CFO/PZT） magnetoelectric composite thin films of 2-2 type structure had been prepared onto Pt/Ti/SiO2/Si substrate by a sol-gel process and spin coat- ing technique. The structure of the prepared thin film is substrate/PZT/CFO/PZT/CFO. Two CFO ferromagnetic layers are separated from each other by a thin PZT layer. The upper CFO layer is magnetostatically coupled with the lower CFO layer. Subsequent scan- ning electron microscopy （SEM） investigations show that the prepared thin films exhibit good morphologies and compact structure, and cross-sectional micrographs clearly display a multilayered nanostructure of multilayered thin films. The composite thin films exhibit both good magnetic and ferroelectric properties. The spacing between ferromagnetic layers can be varied by adjusting the thickness of intermediate PZT layer. It is found that the strength of magnetostatic coupling has a great impact on magnetoelectric properties of composite thin films, i.e., the magnetoelectric voltage coefficient of composite thin film tends to increase with the decreasing of pacing between two neighboring CFO ferromagnetic layers as a result of magnetostatic coupling effect.展开更多
To achieve a better understanding of the effects of the colossal magnetoresistivity in the mixed valence manganites,the model of a negative magnetoresistivity scaling proposed by Wagner et al is explored in both mat...To achieve a better understanding of the effects of the colossal magnetoresistivity in the mixed valence manganites,the model of a negative magnetoresistivity scaling proposed by Wagner et al is explored in both mathematical and physical analyses.The inconsistency in Wagners model is discussed and corrected. The behaviors of the large spin polarons in Nd 0.52 Sr 0.48 MnO 3 film at T c are studied and analyzed.The results show that only through necessary corrections can Wagners model become self consistent. A further exploration of the nature of the magnetically aligned clusters will make the model more convincing.展开更多
基金Projects(50771092,21073162) supported by the National Natural Science Foundation of ChinaProject(2005DKA10400-Z15) supported by the Ministry of Science and Technology of China
文摘CoNiFe,CoNiFeB and CoNiFeP soft magnetic thin films were prepared by cyclic voltammetry method.The morphologies,composition and structures were characterized by scanning electron microscope（SEM）,energy-dispersive X-ray spectroscope（EDS） and X-ray diffractometer（XRD）.The soft magnetic properties were investigated through vibrating sample magnetometer（VSM）.The corrosion resistance was investigated through Tafel polarization and electrochemical impedance spectroscopic（EIS）.The results show that all the electrodeposited CoNiFe,CoNiFeB and CoNiFeP films are mixtures of crystalline and amorphous phases,and high amount of boron/phosphorus-containing additives favors the formation of amorphous state.Nanostructure is obtained in CoNiFe and CoNiFeB films.The inclusion of boron causes the film more dense and also increases its corrosion resistance.Meanwhile,the inclusion of boron lowers its coercivity（Hc） from 851.48 A/m to 604.79 A/m,but the saturation magnetic flux density（Bs） is almost unchanged.However,the addition of phosphorus greatly increases the film particle size and decreases its corrosion stability.The coercivity（Hc） of CoNiFeP film is also highly increased to 12485.79 A/m,and its saturation magnetic flux density（Bs） is greatly decreased to 1.25 T.
基金Project(2008BS04030)supported by Research Award Fund for Outstanding Young Scientists in Shandong Province,China
文摘Nanocrystalline NdFeB film was fabricated onto the copper substrate through direct current electroplating method,and characterized by scanning electron microscope(SEM) coupled with energy dispersive X-ray spectroscope(EDS),vibrating sample magnetometer and potentiodynamic polarization techniques.The initial electroplating behavior was investigated by cyclic voltammetry(CV) and electrochemical impedance spectroscopy(EIS) techniques.Results revealed that the corrosion resistance of the NdFeB film was better than that of the traditional sintered NdFeB magnet.The depositing process of the NdFeB film followed the three-dimensional nucleation and subsequent grain growth mechanism,and was controlled by charger transfer.With the increase of the negative potential bias,the deposition mechanism of NdFeB film changed from heterogeneous to homogeneous nucleation/growth,which consequently resulted in the decrease of charge-transfer-resistance.
文摘Thickness effects of thin La0.7Sr0.3MnO3 （LSMO） films on （LaAlOa）0.3（Sr2AlTaO6）0.7 substrates were examined by a slow positron beam technique. Doppler-broadening line shape parameter S was measured as a function of thickness and differnt annealing conditions. Results reveal there could be more than one mechanism to induce vacancy-like defects. It was found that strain-induced defects mainly influence the S value of the in situ oxygenambience annealing LSMO thin films and the strain could vanish still faster along with the increase of thickness, and the oxygen-deficient induced defects mainly affect the S value of post-annealing LSMO films.
文摘CoFe204/Pb（Zr0.53Ti0.47）O3 （CFO/PZT） magnetoelectric composite thin films of 2-2 type structure had been prepared onto Pt/Ti/SiO2/Si substrate by a sol-gel process and spin coat- ing technique. The structure of the prepared thin film is substrate/PZT/CFO/PZT/CFO. Two CFO ferromagnetic layers are separated from each other by a thin PZT layer. The upper CFO layer is magnetostatically coupled with the lower CFO layer. Subsequent scan- ning electron microscopy （SEM） investigations show that the prepared thin films exhibit good morphologies and compact structure, and cross-sectional micrographs clearly display a multilayered nanostructure of multilayered thin films. The composite thin films exhibit both good magnetic and ferroelectric properties. The spacing between ferromagnetic layers can be varied by adjusting the thickness of intermediate PZT layer. It is found that the strength of magnetostatic coupling has a great impact on magnetoelectric properties of composite thin films, i.e., the magnetoelectric voltage coefficient of composite thin film tends to increase with the decreasing of pacing between two neighboring CFO ferromagnetic layers as a result of magnetostatic coupling effect.
基金National Natural Science Foundation of China(No.50 0 72 0 1 5) Key Teacher Supporting Project (G0 0 0 32 ) +1 种基金StartingFoundation for Returned ResearchersKey Projectof Science andTechnology Research of National Education Committee
文摘To achieve a better understanding of the effects of the colossal magnetoresistivity in the mixed valence manganites,the model of a negative magnetoresistivity scaling proposed by Wagner et al is explored in both mathematical and physical analyses.The inconsistency in Wagners model is discussed and corrected. The behaviors of the large spin polarons in Nd 0.52 Sr 0.48 MnO 3 film at T c are studied and analyzed.The results show that only through necessary corrections can Wagners model become self consistent. A further exploration of the nature of the magnetically aligned clusters will make the model more convincing.