A quantum well intermixing（QW1） investigation on double quantum well（DQW） structure with two different emitting wavelength caused by phosphorus ion implantation and following rapid thermal annealing （RTA） was ca...A quantum well intermixing（QW1） investigation on double quantum well（DQW） structure with two different emitting wavelength caused by phosphorus ion implantation and following rapid thermal annealing （RTA） was carried out by means of photoluminescence（PL）. The ion implantation was performed at the energy of 120 keV with the dose ranging from 1 × 10^11cm^-2 to 1× 10^14cm^-2. The RTA was performed at the temperature of 700 ℃ for 30 s under pure nitrogen protection. The PL measurement implied that the band gap blue-shift from the upper well increases with the ion dose faster than that from lower well and the PL peaks from both QWs remained well separated under the lower dose implantation（-1 × 10^11cm^-2） indicating that the implant vacancy distribution affects the QWl. When the ion dose is over - 1 × 10^12cm^-2, the band gap blue-shift from both wells increases with the ion dose and finally the two peaks merge together as one peak indicating the ion implantation caused a total intermixing of both quantum wells.展开更多
For All-Solid-State battery applications, Mg2＋-ion conducting polymer electrolytes and Mg-metal electrode are currently considered as alternate choices in place of Li＋-ion conducting polymer electrolytes/Li-metal el...For All-Solid-State battery applications, Mg2＋-ion conducting polymer electrolytes and Mg-metal electrode are currently considered as alternate choices in place of Li＋-ion conducting polymer electrolytes/Li-metal electrode. Present paper reports fabrication of All-Solid-State battery based on the following Mg2＋-ion conducting nano composite polymer electrolyte （NCPE） films： [85PEO： 15Mg（C104）2] ＋ 5% TiO2 （〈 100 nm）, [85PEO： 15Mg（CIO4）2] ＋ 3% SiO2（-8 nm）. [85PEO： 15Mg（CIO4）2] ＋ 3% MgO （〈 100 nm）, [85PEO：15Mg（C1O4）2] ＋ 3% MgO （-44 μm）. NCPE films were prepared by hot-press technique. Solid Polymer Electrolyte （SPE） composition： [85PEO： 15Mg（CIO4）2], identified as high conducting film at room temperature, has been used as ISt--phase host and nano/micro particles of active （MgO）/passive （SiO2, TiO2） fillers as IInd-phase dispersoid. Filler particle dependent conductivity studies identified above mentioned NCPE films as optimum conducting composition （OCC） at room temperature. Ion transport behavior of SPE/NCPE film materials was investigated previously. Present paper reports materials characterization and cell performance studies on All-Solid-State batteries： Mg （Anode） Ⅱ SPE or NCPE films tt C＋MnO2＋Electrolyte （Cathode）. Open circuit voltage （OCV） obtained was in the range： 1.79-1.92 V. The batteries were discharged at room temperature under different load conditions and some important battery parameters have been evaluated from plateau region of cell-potential discharge profiles. All the batteries performed quite satisfactorily specially under low current drain states.展开更多
文摘A quantum well intermixing（QW1） investigation on double quantum well（DQW） structure with two different emitting wavelength caused by phosphorus ion implantation and following rapid thermal annealing （RTA） was carried out by means of photoluminescence（PL）. The ion implantation was performed at the energy of 120 keV with the dose ranging from 1 × 10^11cm^-2 to 1× 10^14cm^-2. The RTA was performed at the temperature of 700 ℃ for 30 s under pure nitrogen protection. The PL measurement implied that the band gap blue-shift from the upper well increases with the ion dose faster than that from lower well and the PL peaks from both QWs remained well separated under the lower dose implantation（-1 × 10^11cm^-2） indicating that the implant vacancy distribution affects the QWl. When the ion dose is over - 1 × 10^12cm^-2, the band gap blue-shift from both wells increases with the ion dose and finally the two peaks merge together as one peak indicating the ion implantation caused a total intermixing of both quantum wells.
文摘For All-Solid-State battery applications, Mg2＋-ion conducting polymer electrolytes and Mg-metal electrode are currently considered as alternate choices in place of Li＋-ion conducting polymer electrolytes/Li-metal electrode. Present paper reports fabrication of All-Solid-State battery based on the following Mg2＋-ion conducting nano composite polymer electrolyte （NCPE） films： [85PEO： 15Mg（C104）2] ＋ 5% TiO2 （〈 100 nm）, [85PEO： 15Mg（CIO4）2] ＋ 3% SiO2（-8 nm）. [85PEO： 15Mg（CIO4）2] ＋ 3% MgO （〈 100 nm）, [85PEO：15Mg（C1O4）2] ＋ 3% MgO （-44 μm）. NCPE films were prepared by hot-press technique. Solid Polymer Electrolyte （SPE） composition： [85PEO： 15Mg（CIO4）2], identified as high conducting film at room temperature, has been used as ISt--phase host and nano/micro particles of active （MgO）/passive （SiO2, TiO2） fillers as IInd-phase dispersoid. Filler particle dependent conductivity studies identified above mentioned NCPE films as optimum conducting composition （OCC） at room temperature. Ion transport behavior of SPE/NCPE film materials was investigated previously. Present paper reports materials characterization and cell performance studies on All-Solid-State batteries： Mg （Anode） Ⅱ SPE or NCPE films tt C＋MnO2＋Electrolyte （Cathode）. Open circuit voltage （OCV） obtained was in the range： 1.79-1.92 V. The batteries were discharged at room temperature under different load conditions and some important battery parameters have been evaluated from plateau region of cell-potential discharge profiles. All the batteries performed quite satisfactorily specially under low current drain states.
