混凝土渗透性“PERMIT”测试方法探索

为了探寻"PERMIT"离子迁移方法与现行标准推荐方法的关系,对不同胶凝材料体系混凝土分别进行了"PERMIT"离子迁移试验及RCM快速氯离子迁移试验。通过对"PERMIT"阳极室溶液进行定量分析,发现胶凝材料体系变化对阳极室溶液浓度变化率与电导变化率关系影响不显著,进而建立了两者的普适关系。试验结果表明,"PERMIT"离子迁移测试结果与RCM快速氯离子迁移试验结果存在良好的线性相关关系,在此基础上建立了"PER-MIT"离子迁移方法与RCM快速氯离子迁移方法的关系。研究成果可简化结构混凝土抗氯离子渗透性现场测试步骤,并使测试结果与现行标准推荐方法建立定量联系。

Apparent Mobilities of Na^+, K^+and Ca^(2+) Ions in Variable Charge Soil Colloid Systems

In this paper a simple method for determination of the apparent mobility of cation in a soil colloid system was described. With this method apparent mobilities of Na+, K+, and Ca2+ ions in the systems of the ferric luvisol, acrisol, and ferralsol were determined, and the reduction percentages of the mobilities were calculated. The results showed that the apparent mobilities of different cations at the same normality in a given soil system were in the order UNa> UK> UCa; those of the same cations among different soil systems were in the order ferralsol > acrisol > ferric luvisol, but the reduction percentages were in a reverse order, which among different cations at the same normality was Ca2+> K+> Na+ for ferric luvisol and acrisol systems, but was K+> Ca2+> Na+ for farralsol system. These results were interpreted in terms of different amounts of negative charge the clay fraction of different soils carries, and different mechanisms by which the soils adsorb the cations.

锆合金氧化膜微观缺陷的量化表征

基于离子在氧化膜中的迁移,建立一种可量化表征合金氧化膜微观缺陷的离子迁移方法(IMM)。利用IMM方法,对不同成分的锆合金在不同条件下腐蚀得到的氧化膜样品进行了测试。结果表明:建立的方法能清楚地反映氧化膜中的微观缺陷情况以及微观缺陷随腐蚀条件的变化。该方法进一步完善后,可以为合金氧化微观结构量化分析提供一个有效手段。

Zr-1Nb合金的耐腐蚀性能与氧化膜中应力和缺陷的关系（英文）

采用2种时间间隔加热和冷却高压釜的腐蚀试验研究了Zr-1Nb合金在360℃,18.6 MPa, 0.01 mol/L LiOH水溶液中的耐腐蚀性能;用卷曲法测量了氧化膜中的应力;利用离子迁移方法(IMM)测量了氧化膜中的缺陷数量。结果表明:在腐蚀初期,短时间间隔方式下样品氧化膜中的应力水平和缺陷密度都比长时间间隔方式下的低,前者在腐蚀后期表现出更佳的耐腐蚀性能。这说明在2种时间间隔方式下,腐蚀初期样品的增重在没有明显差别的情况下,氧化膜中的应力水平和缺陷密度均已存在显著的差别,从而造成氧化膜显微组织演化速率的不同,进而引起合金耐腐蚀性能的差别。