Abstract： PAN （Polyacrylonitrile）-based carbonaceous fibers were prepared at the heat treatment temperature （HTT） range of 650 to 900 ℃. The relationships among HTT, carbon content and volume resistivity of the ...Abstract： PAN （Polyacrylonitrile）-based carbonaceous fibers were prepared at the heat treatment temperature （HTT） range of 650 to 900 ℃. The relationships among HTT, carbon content and volume resistivity of the carbonaceous fibers were investigated. The carbonaceous fibers/PTFE （Polytetrafluoroethylene） antistatic coatings were prepared by the spraying technology and the effects of carbonaceous fibers and pigments on surface resistivity of the coatings were systematically discussed. Micrographs provide insight into the antistatic mechanism of the coating. The results show that carbon content of the carbonaceous fibers increases from 68.8% to 74.8% （mass fraction） and the volume resistivity decreases drastically from 1.94× 10^-3 to 8.27× 10 ^-2.cm. The surface resistivity of the antistatic coating is adjustable between 10^5 and 10^8Ω2 to fit the different antistatic materials. Static is dissipated by a conductive network of short fibers and the tunneling effect between the neighboring fibers and conductive pigments. Conductive pigments make the conductive network more perfect and improve the antistatic ability, but insulating pigments acting as barriers for the formation of conductive channel increases the surface resistivity of the coatings. The influence of pigments on the surface resistivity drops gradually with the decrease of the carbonaceous fibers volume resistivity.展开更多
We have successfully employed metal-organic chemical vapor deposition （MOCVD） technique to simultaneously deposit double-sided YBa2Cu3O7-δ （YBCO） films on both sides of YzO3/yttria-stabilized zirconia （YSZ）/Ce...We have successfully employed metal-organic chemical vapor deposition （MOCVD） technique to simultaneously deposit double-sided YBa2Cu3O7-δ （YBCO） films on both sides of YzO3/yttria-stabilized zirconia （YSZ）/CeO2 （YYC） buffered biaxially textured Ni-5 at.% W substrates, which is of great prospect to cut the production cost of YBCO coated conductors. X-ray diffraction analysis revealed that both sides of YBCO film were purely c-axis oriented and highly textured. The co-scan of （005） YBCO and Ф-scan of （103） YBCO yielded full width at half maximum （FWHM） values of 4.9° and 6.6° for one side of double-sided YBCO film, respectively, as well as 4.4° and 6.4° for the other side. The current transportation measurements performed on such double-sided 500 nm-thickness YBCO films showed the self-field critical current density （Jc） at 77 K of 0.6 MA/cm^2 and 1.2 MA/cm^2, respectively. Further research is in the process of exploring new solution to improve the Jc in practice.展开更多
基金Project(2011CB605601)supported by the National Basic Research Program(973 Program)of ChinaProject(50902088)supported by the National Natural Science Foundation of China+1 种基金Project(ZR2011EMM002)supported by the Natural Science Foundation in Shandong Province,ChinaProject(2009AA035301)supported by the National High Technology Research and Development Program(863 Program)of China
文摘Abstract： PAN （Polyacrylonitrile）-based carbonaceous fibers were prepared at the heat treatment temperature （HTT） range of 650 to 900 ℃. The relationships among HTT, carbon content and volume resistivity of the carbonaceous fibers were investigated. The carbonaceous fibers/PTFE （Polytetrafluoroethylene） antistatic coatings were prepared by the spraying technology and the effects of carbonaceous fibers and pigments on surface resistivity of the coatings were systematically discussed. Micrographs provide insight into the antistatic mechanism of the coating. The results show that carbon content of the carbonaceous fibers increases from 68.8% to 74.8% （mass fraction） and the volume resistivity decreases drastically from 1.94× 10^-3 to 8.27× 10 ^-2.cm. The surface resistivity of the antistatic coating is adjustable between 10^5 and 10^8Ω2 to fit the different antistatic materials. Static is dissipated by a conductive network of short fibers and the tunneling effect between the neighboring fibers and conductive pigments. Conductive pigments make the conductive network more perfect and improve the antistatic ability, but insulating pigments acting as barriers for the formation of conductive channel increases the surface resistivity of the coatings. The influence of pigments on the surface resistivity drops gradually with the decrease of the carbonaceous fibers volume resistivity.
基金supported by the National Natural Science Foundation of China(Grant No.51002024)Sichuan Youth Science and Technology Innovation Research Team Funding(Grant No.2011JTD0006)Fundamental Research Funds for the Central Universities(Grant Nos.ZYGX2012J039 and ZYGX2011Z002)
文摘We have successfully employed metal-organic chemical vapor deposition （MOCVD） technique to simultaneously deposit double-sided YBa2Cu3O7-δ （YBCO） films on both sides of YzO3/yttria-stabilized zirconia （YSZ）/CeO2 （YYC） buffered biaxially textured Ni-5 at.% W substrates, which is of great prospect to cut the production cost of YBCO coated conductors. X-ray diffraction analysis revealed that both sides of YBCO film were purely c-axis oriented and highly textured. The co-scan of （005） YBCO and Ф-scan of （103） YBCO yielded full width at half maximum （FWHM） values of 4.9° and 6.6° for one side of double-sided YBCO film, respectively, as well as 4.4° and 6.4° for the other side. The current transportation measurements performed on such double-sided 500 nm-thickness YBCO films showed the self-field critical current density （Jc） at 77 K of 0.6 MA/cm^2 and 1.2 MA/cm^2, respectively. Further research is in the process of exploring new solution to improve the Jc in practice.