A novel aluminum bronze over the Cu-Al binary alloy eutectoid Cu-14Al-4.5Fe was prepared by a jointly-charging one-melting technique and conventional sand casting. The bronze coatings were atmospherically plasma spray...A novel aluminum bronze over the Cu-Al binary alloy eutectoid Cu-14Al-4.5Fe was prepared by a jointly-charging one-melting technique and conventional sand casting. The bronze coatings were atmospherically plasma sprayed on the 45# medium carbon steel substrate. The effect of rare earth Ce on the microstructures and Vickers hardness of the cast alloy and coatings were characterized by scanning electron microscopy, X-ray diffraction, electronic probe microanalysis, transmission electron microscopy and microhardness measurements. The results indicate that the hardness of both as-cast alloy and coating are enhanced by the addition of 0.6% Ce due to the refinement of κ phases which are well distributed in the matrix. The rapid solidification in the plasma spray processing retains Fe-supersaturated in the Al-bronze alloy coatings, which avoids the formation of eutectoid （α＋γ2） phase and stacking faults are found in the coatings with Ce added, accordingly improves the mechanical properties.展开更多
3Gd2O3-3Yb2O3-4Y2O3 （mole fraction, %） co-doped ZrO2 （GY-YSZ） thermal barrier coatings （TBCs） were produced by electron beam physical vapor deposition （EB-PVD）. The oxidation behavior of GY-YSZ at 1 050 ℃ was...3Gd2O3-3Yb2O3-4Y2O3 （mole fraction, %） co-doped ZrO2 （GY-YSZ） thermal barrier coatings （TBCs） were produced by electron beam physical vapor deposition （EB-PVD）. The oxidation behavior of GY-YSZ at 1 050 ℃ was investigated using impedance spectroscopy （IS） combined with scanning electron microscopy （SEM）, Raman spectroscopy and X-ray diffractometry （XRD）. Various electrical responses observed in the impedance spectra corresponding to GY-YSZ grains and grain boundaries were explained using circuit modeling. The change in the conduction mechanism of GY-YSZ was found to be related to the O^2- vacancy and lattice distortion due to the stabilizer diffusion during the oxidation. The results also suggested that the specific oxidation information about the GY-YSZ grains and grain boundaries should be acquired at a moderate measurement temperature, which was related to the resistance value in the impedance spectra. The resistance values of the GY-YSZ grains and grain boundaries should be measured at 200 ℃ and 300 ℃, respectively.展开更多
Oxidation behaviors of TP304H steel with electrophoresis deposited CeO2 coating in water vapor were studied at 610℃～770℃ for 65 h. The results showed that CeO2 coating reduced effectively the oxidation rate of TP30...Oxidation behaviors of TP304H steel with electrophoresis deposited CeO2 coating in water vapor were studied at 610℃～770℃ for 65 h. The results showed that CeO2 coating reduced effectively the oxidation rate of TP304H. Analysis with SEM and EDS showed the structure of oxide scale turned from multi-layer to mono-layer and oxide scale with high Cr content formed on the surface of CeO2 coating while inner oxidation disappeared. Based on test results and CeO2characters that Ce ion can vary between Ce4+ and Ce3+ under oxygen-rich and oxygen-poor environment, it is concluded that CeO2 coating acts as a barrier to prevent oxygen inner diffusion and the partial oxygen pressure of CeO2 coating-substrate interface is limited. Cr first diffuses outward across CeO2 coating and forms oxide scale on the surface, which delays formation of Fe oxide.展开更多
基金Projects (50804019, 51165021) supported by the National Natural Science Foundation of ChinaProject (0901ZTB009) supported by the Super Tutor Foundation from the Education Department of Gansu Province, China
文摘A novel aluminum bronze over the Cu-Al binary alloy eutectoid Cu-14Al-4.5Fe was prepared by a jointly-charging one-melting technique and conventional sand casting. The bronze coatings were atmospherically plasma sprayed on the 45# medium carbon steel substrate. The effect of rare earth Ce on the microstructures and Vickers hardness of the cast alloy and coatings were characterized by scanning electron microscopy, X-ray diffraction, electronic probe microanalysis, transmission electron microscopy and microhardness measurements. The results indicate that the hardness of both as-cast alloy and coating are enhanced by the addition of 0.6% Ce due to the refinement of κ phases which are well distributed in the matrix. The rapid solidification in the plasma spray processing retains Fe-supersaturated in the Al-bronze alloy coatings, which avoids the formation of eutectoid （α＋γ2） phase and stacking faults are found in the coatings with Ce added, accordingly improves the mechanical properties.
基金Projects (50771009, 50731001 and 51071013) supported by the National Natural Science Foundations of China Project (2010CB631200) supported by the National Basic Research Program of China
文摘3Gd2O3-3Yb2O3-4Y2O3 （mole fraction, %） co-doped ZrO2 （GY-YSZ） thermal barrier coatings （TBCs） were produced by electron beam physical vapor deposition （EB-PVD）. The oxidation behavior of GY-YSZ at 1 050 ℃ was investigated using impedance spectroscopy （IS） combined with scanning electron microscopy （SEM）, Raman spectroscopy and X-ray diffractometry （XRD）. Various electrical responses observed in the impedance spectra corresponding to GY-YSZ grains and grain boundaries were explained using circuit modeling. The change in the conduction mechanism of GY-YSZ was found to be related to the O^2- vacancy and lattice distortion due to the stabilizer diffusion during the oxidation. The results also suggested that the specific oxidation information about the GY-YSZ grains and grain boundaries should be acquired at a moderate measurement temperature, which was related to the resistance value in the impedance spectra. The resistance values of the GY-YSZ grains and grain boundaries should be measured at 200 ℃ and 300 ℃, respectively.
文摘Oxidation behaviors of TP304H steel with electrophoresis deposited CeO2 coating in water vapor were studied at 610℃～770℃ for 65 h. The results showed that CeO2 coating reduced effectively the oxidation rate of TP304H. Analysis with SEM and EDS showed the structure of oxide scale turned from multi-layer to mono-layer and oxide scale with high Cr content formed on the surface of CeO2 coating while inner oxidation disappeared. Based on test results and CeO2characters that Ce ion can vary between Ce4+ and Ce3+ under oxygen-rich and oxygen-poor environment, it is concluded that CeO2 coating acts as a barrier to prevent oxygen inner diffusion and the partial oxygen pressure of CeO2 coating-substrate interface is limited. Cr first diffuses outward across CeO2 coating and forms oxide scale on the surface, which delays formation of Fe oxide.