It is taken as a novel prospective process to treat iron concentrate from hydrometallurgical zinc kiln slag forcomprehensive utilization of valuable metals by a hydrochloric acid leaching-spray pyrolysis method.The le...It is taken as a novel prospective process to treat iron concentrate from hydrometallurgical zinc kiln slag forcomprehensive utilization of valuable metals by a hydrochloric acid leaching-spray pyrolysis method.The leaching mechanism ofdifferent valuable metals was studied.The results revealed that the leaching rates of Ag,Pb,Cu,Fe,As and Zn were99.91%,99.25%,95.12%,90.15%,87.58%and58.15%,respectively with6mol/L HCl and L/S ratio of10:1at60°C for120min.The actionof SiO2in leaching solution was also studied.The results showed that the precipitation and settlement of SiO2(amorphous)adsorbedpart of metal ions in solution,which greatly inhibited the leaching of Cu,Fe,As and Zn,so it is crucial to control the precipitation ofamorphous SiO2.展开更多
Rotary kiln process for iron ore oxide pellet production is hard to detect and control.Construction of one-dimensional model of temperature field in rotary kiln was described.And the results lay a solid foundation for...Rotary kiln process for iron ore oxide pellet production is hard to detect and control.Construction of one-dimensional model of temperature field in rotary kiln was described.And the results lay a solid foundation for online control.Establishment of kiln process control expert system was presented,with maximum temperature of pellet and gas temperature at the feed end as control cores,and interval estimate as control strategy.Software was developed and put into application in a pellet plant.The results show that control guidance of this system is accurate and effective.After production application for nearly one year,the compressive strength and first grade rate of pellet are increased by 86 N and 2.54%,respectively,while FeO content is 0.05% lowered.This system can reveal detailed information of real time kiln process,and provide a powerful tool for online control of pellet production.展开更多
The effect of coal levels on phosphorus removal from a high phosphorus oolitic hematite ore after direct reduction roasting have been investigated. Raw ore, coal, and a dephosphorizatiou agent were mixed and the mixtu...The effect of coal levels on phosphorus removal from a high phosphorus oolitic hematite ore after direct reduction roasting have been investigated. Raw ore, coal, and a dephosphorizatiou agent were mixed and the mixture was then roasted in a tunnel kiln. The roasted products were treated by two stages of grind- ing followed by magnetic separation. XRD and SEM-EDS examination of the products was used to analyze differences in the roasted products. The results show that coal is one of the most important factors affect- ing the direct reduction roasting process. When the inner coal levels increased from 0% to 15% the iron grade decreased linearly from 94.94%to 88.81% and the iron recovery increased from 55.94% to 92.94%. At the same time the phosphorus content increased from 0.045% to 0.231%. Increasing the inner coal levels also caused more hematite to be reduced to metallic iron but the oolitic structure of the roasted product was preserved in the presence of high coal loading. The phase of the phosphorus in raw ore was not changed after direct reduction roasting. The effect of coal on the phosphorus content in the H-concentrate arises from changes in the difficulty of mechanically liberating the metallic iron from the phosphorus bearing minerals.展开更多
基金Project(51404307)supported by the National Natural Science Foundation of ChinaProject(2014CB643400)supported by the National Basic Research Program of China
文摘It is taken as a novel prospective process to treat iron concentrate from hydrometallurgical zinc kiln slag forcomprehensive utilization of valuable metals by a hydrochloric acid leaching-spray pyrolysis method.The leaching mechanism ofdifferent valuable metals was studied.The results revealed that the leaching rates of Ag,Pb,Cu,Fe,As and Zn were99.91%,99.25%,95.12%,90.15%,87.58%and58.15%,respectively with6mol/L HCl and L/S ratio of10:1at60°C for120min.The actionof SiO2in leaching solution was also studied.The results showed that the precipitation and settlement of SiO2(amorphous)adsorbedpart of metal ions in solution,which greatly inhibited the leaching of Cu,Fe,As and Zn,so it is crucial to control the precipitation ofamorphous SiO2.
基金Project(NCET-05-0630) supported by Program for New Century Excellent Talents in University of China
文摘Rotary kiln process for iron ore oxide pellet production is hard to detect and control.Construction of one-dimensional model of temperature field in rotary kiln was described.And the results lay a solid foundation for online control.Establishment of kiln process control expert system was presented,with maximum temperature of pellet and gas temperature at the feed end as control cores,and interval estimate as control strategy.Software was developed and put into application in a pellet plant.The results show that control guidance of this system is accurate and effective.After production application for nearly one year,the compressive strength and first grade rate of pellet are increased by 86 N and 2.54%,respectively,while FeO content is 0.05% lowered.This system can reveal detailed information of real time kiln process,and provide a powerful tool for online control of pellet production.
基金the National Natural Science Foundation of China (No. 51074016) for the financial support for this research
文摘The effect of coal levels on phosphorus removal from a high phosphorus oolitic hematite ore after direct reduction roasting have been investigated. Raw ore, coal, and a dephosphorizatiou agent were mixed and the mixture was then roasted in a tunnel kiln. The roasted products were treated by two stages of grind- ing followed by magnetic separation. XRD and SEM-EDS examination of the products was used to analyze differences in the roasted products. The results show that coal is one of the most important factors affect- ing the direct reduction roasting process. When the inner coal levels increased from 0% to 15% the iron grade decreased linearly from 94.94%to 88.81% and the iron recovery increased from 55.94% to 92.94%. At the same time the phosphorus content increased from 0.045% to 0.231%. Increasing the inner coal levels also caused more hematite to be reduced to metallic iron but the oolitic structure of the roasted product was preserved in the presence of high coal loading. The phase of the phosphorus in raw ore was not changed after direct reduction roasting. The effect of coal on the phosphorus content in the H-concentrate arises from changes in the difficulty of mechanically liberating the metallic iron from the phosphorus bearing minerals.