Mg-4 Li-3(Al-Si),Mg-8 Li-3(Al-Si)and Mg-12 Li-3(Al-Si)alloys based on theα-Mg,α-Mg+β-Li,β-Li phases,respectively,were produced to investigate the effect of alloying with Al-Si eutectic on the microstructure and me...Mg-4 Li-3(Al-Si),Mg-8 Li-3(Al-Si)and Mg-12 Li-3(Al-Si)alloys based on theα-Mg,α-Mg+β-Li,β-Li phases,respectively,were produced to investigate the effect of alloying with Al-Si eutectic on the microstructure and mechanical properties of the three alloys.Alloying with the Al-Si eutectic of Mg-xLi(x=4,8 and 12 wt.%)alloys caused the formation of different types of Al-Li precipitates:Al3Li,AlLi and Li3Al2,respectively.Also,considerable quantities of Mg2Si phase particles were found in the three alloys.The results of tensile tests showed that the Mg-4Li-3(Al-Si)alloy exhibited the highest ultimate tensile strength(UTS)of 249 MPa but the lowest elongation of 6.3%.The Mg-12Li-3(Al-Si)alloy had the highest elongation of 26%but the lowest UTS of 173 MPa.The different mechanical properties were attributed to the different crystal structures of the three alloys and the precipitate with different type,morphology and distribution.展开更多
基金Projects(51971040,51701029,51671041,51531002) supported by the National Natural Science Foundation of ChinaProject(2016YFB0301100) supported by the National Key Research and Development Program of China+2 种基金Projects(2018T110943,2017M620410) supported by the China Postdoctoral Science FoundationProject(Xm2017010) supported by the the Chongqing Postdoctoral Scientific Research Foundation,ChinaProject(2018CDGFCL005) supported by the Fundamental Research Funds for the Central Universities,China
文摘Mg-4 Li-3(Al-Si),Mg-8 Li-3(Al-Si)and Mg-12 Li-3(Al-Si)alloys based on theα-Mg,α-Mg+β-Li,β-Li phases,respectively,were produced to investigate the effect of alloying with Al-Si eutectic on the microstructure and mechanical properties of the three alloys.Alloying with the Al-Si eutectic of Mg-xLi(x=4,8 and 12 wt.%)alloys caused the formation of different types of Al-Li precipitates:Al3Li,AlLi and Li3Al2,respectively.Also,considerable quantities of Mg2Si phase particles were found in the three alloys.The results of tensile tests showed that the Mg-4Li-3(Al-Si)alloy exhibited the highest ultimate tensile strength(UTS)of 249 MPa but the lowest elongation of 6.3%.The Mg-12Li-3(Al-Si)alloy had the highest elongation of 26%but the lowest UTS of 173 MPa.The different mechanical properties were attributed to the different crystal structures of the three alloys and the precipitate with different type,morphology and distribution.