Equal channel angular expansion extrusion with spherical cavity(ECAEE-SC)was introduced as a novel severe plastic deformation(SPD)technique,which is capable of imposing large plastic strain and intrinsic back-pressure...Equal channel angular expansion extrusion with spherical cavity(ECAEE-SC)was introduced as a novel severe plastic deformation(SPD)technique,which is capable of imposing large plastic strain and intrinsic back-pressure on the processed billet.The plastic deformation behaviors of commercially pure aluminum during ECAEE-SC process were investigated using finite element analysis DEFORM-3D simulation software.The material flow,the load history,the distribution of effective strain and mean stress in the billet were analyzed in comparison with conventional equal channel angular extrusion(ECAE)process.In addition,single-pass ECAEE-SC was experimentally conducted on commercially pure aluminum at room temperature for validation,and the evolution of microstructure and microhardness of as-processed material was discussed.It was shown that during the process,the material is in the ideal hydrostatic stress state and the load requirement for ECAEE-SC is much more than that for ECAE.After a single-pass ECAEE-SC,an average strain of 3.51 was accumulated in the billet with homogeneous distribution.Moreover,the microstructure was significantly refined and composed of equiaxed ultrafine grains with sub-micron size.Considerable improvement in the average microhardness of aluminum was also found,which was homogenized and increased from HV 36.61 to HV 70.20,denoting 91.75%improvement compared with that of the as-cast billet.展开更多
基金Project(51905462)supported by the National Natural Science Foundation of ChinaProject(BK20200297)supported by the Natural Science Foundation of Jiangsu Province,China+1 种基金Project(GDZB-127)supported by Jiangsu Provincial“Six Talent Peaks”Program,ChinaProject(2018202)supported by the“Youth Science and Technology Talents'Sponsored Program of Jiangsu Science and Technology Association,China。
文摘Equal channel angular expansion extrusion with spherical cavity(ECAEE-SC)was introduced as a novel severe plastic deformation(SPD)technique,which is capable of imposing large plastic strain and intrinsic back-pressure on the processed billet.The plastic deformation behaviors of commercially pure aluminum during ECAEE-SC process were investigated using finite element analysis DEFORM-3D simulation software.The material flow,the load history,the distribution of effective strain and mean stress in the billet were analyzed in comparison with conventional equal channel angular extrusion(ECAE)process.In addition,single-pass ECAEE-SC was experimentally conducted on commercially pure aluminum at room temperature for validation,and the evolution of microstructure and microhardness of as-processed material was discussed.It was shown that during the process,the material is in the ideal hydrostatic stress state and the load requirement for ECAEE-SC is much more than that for ECAE.After a single-pass ECAEE-SC,an average strain of 3.51 was accumulated in the billet with homogeneous distribution.Moreover,the microstructure was significantly refined and composed of equiaxed ultrafine grains with sub-micron size.Considerable improvement in the average microhardness of aluminum was also found,which was homogenized and increased from HV 36.61 to HV 70.20,denoting 91.75%improvement compared with that of the as-cast billet.
