Ultrafine-grained(UFG) high purity aluminum exhibits a variety of attractive mechanical properties and special deformation behavior. Equal channel angular pressing(ECAP) process can be used to easily and effectively r...Ultrafine-grained(UFG) high purity aluminum exhibits a variety of attractive mechanical properties and special deformation behavior. Equal channel angular pressing(ECAP) process can be used to easily and effectively refine metals. The microstructure and microtexture evolutions and grain boundary characteristics of the high purity aluminum(99.998%) processed by ECAP at room temperature are investigated by means of TEM and EBSD. The results indicate that the shear deformation resistance increases with repeated EACP passes, and equiaxed grains with an average size of 0.9 μm in diameter are formed after five passes. Although the orientations distribution of grains tends to evolve toward random orientations, and microtextures(80°, 35°, 0°),(40°, 75°, 45°) and(0°, 85°, 45°) peak in the sample after five passes. The grain boundaries in UFG aluminum are high-angle geometrically necessary boundaries. It is suggested that the continuous dynamic recrystallization is responsible for the formation of ultrafine grains in high purity aluminum. Microstructure evolution in the high purity aluminum during ECAP is proposed.展开更多
The two-pass equal channel angular extrusion (ECAE) process was introduced into strain-induced melt activation (SIMA) to predeform a ZK60 alloy with rare earth (RE) addition. Microstructure evolution of ECAE-formed ZK...The two-pass equal channel angular extrusion (ECAE) process was introduced into strain-induced melt activation (SIMA) to predeform a ZK60 alloy with rare earth (RE) addition. Microstructure evolution of ECAE-formed ZK60+RE alloy during reheating was investigated. Furthermore, tensile properties of thixoforged components were determined. The results show that the SIMA process can produce ideal microstructures, and spheroidized solid particles with little entrapped liquid can be obtained. With prolonging holding time, the size of solid particles increases and the degree of spheroidization is improved. The tensile properties of the thixoforged ZK60+RE samples are close to those of two-pass ECAE-formed samples.展开更多
基金Project(12JJ2028)supported by the Hunan Provincial Natural Science Foundation of ChinaProject(201308430093)supported by the China Scholarship CouncilProjects(201012200006,2013zzts185,2012zzts066)supported by the Freedom Explore Program of Central South University,China
文摘Ultrafine-grained(UFG) high purity aluminum exhibits a variety of attractive mechanical properties and special deformation behavior. Equal channel angular pressing(ECAP) process can be used to easily and effectively refine metals. The microstructure and microtexture evolutions and grain boundary characteristics of the high purity aluminum(99.998%) processed by ECAP at room temperature are investigated by means of TEM and EBSD. The results indicate that the shear deformation resistance increases with repeated EACP passes, and equiaxed grains with an average size of 0.9 μm in diameter are formed after five passes. Although the orientations distribution of grains tends to evolve toward random orientations, and microtextures(80°, 35°, 0°),(40°, 75°, 45°) and(0°, 85°, 45°) peak in the sample after five passes. The grain boundaries in UFG aluminum are high-angle geometrically necessary boundaries. It is suggested that the continuous dynamic recrystallization is responsible for the formation of ultrafine grains in high purity aluminum. Microstructure evolution in the high purity aluminum during ECAP is proposed.
文摘The two-pass equal channel angular extrusion (ECAE) process was introduced into strain-induced melt activation (SIMA) to predeform a ZK60 alloy with rare earth (RE) addition. Microstructure evolution of ECAE-formed ZK60+RE alloy during reheating was investigated. Furthermore, tensile properties of thixoforged components were determined. The results show that the SIMA process can produce ideal microstructures, and spheroidized solid particles with little entrapped liquid can be obtained. With prolonging holding time, the size of solid particles increases and the degree of spheroidization is improved. The tensile properties of the thixoforged ZK60+RE samples are close to those of two-pass ECAE-formed samples.